Gold alloy

A gold alloy and alloy technology, applied in the field of gold alloys, can solve the problems of affecting quality, easy to be oxidized, poor color, etc., and achieve the effects of long service life, low preparation cost and excellent high temperature characteristics

Inactive Publication Date: 2015-02-04
北海嘉华珠宝有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because 14K gold is mixed with many other elements, some elements are easily oxidized in the case of long-term exposure in the air, and the color is not maintained well, which affects its quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The present invention provides a kind of gold alloy, which is characterized in that, by weight percentage, it comprises the following components:

[0051] Silver 5%, zinc 7%, copper 5%, niobium 2%, calcium 0.5%, zirconium 0.5%, erbium 4.5%, holmium 1%, epoxy resin 1%, curing agent 0.2%, and the rest are gold and non- Avoid impurities.

Embodiment 2

[0053] The present invention provides a kind of gold alloy, which is characterized in that, by weight percentage, it comprises the following components:

[0054] Silver 6.5%, zinc 5%, copper 4%, niobium 3%, calcium 1.0%, zirconium 0.8%, erbium 3.5%, holmium 0.8%, epoxy resin 2%, curing agent 0.5%, and the rest are gold and non- Avoid impurities.

Embodiment 3

[0056] The present invention provides a kind of gold alloy, which is characterized in that, by weight percentage, it comprises the following components:

[0057] Silver 7%, zinc 4.5%, copper 3.5%, niobium 3%, calcium 1.5%, zirconium 0.5%, erbium 4.5%, holmium 0.5%, epoxy resin 3%, curing agent 1%, and the rest are gold and non- Avoid impurities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of alloys, and particularly relates to a gold alloy. The gold alloy comprises 5-10% of Ag, 3-7% of Zn, 2-5% of Cu, 2-4% of Nb, 0.5-1.5% of Ca, 0.5-1.5% of Zr, 2-4.5% of Er, 0.5-1% of Ho, 1-3% of epoxy resin and the balance of gold and inevitable impurities. The invention also provides a synthetic method of the gold alloy. The gold alloy provided by the invention has the advantages of excellent high-temperature property, very long service life, high-temperature resistance, oxidization resistance and creep resistance; gold jewelry made from the gold alloy has the advantages of low price, high hardness and long-lasting color and luster and can be worn for a long time.

Description

technical field [0001] The invention belongs to the technical field of alloys, and particularly relates to a gold alloy. Background technique [0002] Gold alloy has a long history as a material for the traditional production of gold jewelry. Usually, the gold alloy used in pure gold jewelry is 99.99% gold with 0.09% Cu or Ag metal added. The hardness is generally soft, so pure gold The product is easy to deform and is not suitable for inlaid jewelry. In addition, the color of pure gold is yellow, which is not fashionable enough today when white jewelry is popular. Therefore, common jewelry is made of 18K or 14K gold with a gold content of 75%. 25% of a piece of 18K gold jewelry is Ni, Cu, Zn, Ag and other metals, 14K gold jewelry contains more than 58.33% gold elements, and the rest are Cu, Zn, Ag and other metals. Compared with 18K gold, 14K gold can be mixed with more other elements, which can adjust different colors, high hardness, various processing of inlaid gemstones...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C5/02
Inventor 张宁
Owner 北海嘉华珠宝有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com