Technology for rapidly and efficiently treating large-area poor paint sprayed parts

A treatment process and large-area technology, which can be used in devices for coating liquids on surfaces, coatings, chemical paint/ink removers, etc. The method is simple and convenient, the production cost is reduced, and the environmental pollution is small.

Inactive Publication Date: 2015-02-11
ZHEJIANG GEELY HOLDING (GROUP) CO LTD +2
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] 1. Large-scale grinding, manual grinding is labor-intensive, inconvenient to handle, and takes a long time
[0009] 2. After grinding, it will damage the steel plate of the body and make it thinner, which may cause the body or the polished parts to be scrapped
[0010] 3. When grinding a large-area plate, some parts are not easy to clean, which will affect the follow-up work. Moreover, the parts where the iron leakage is polished are easy to rust and there is a risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A fast and efficient large-area paint spraying defect treatment process, including the following steps in sequence:

[0034] 1) Prepare the parts with bad spraying;

[0035] 2) Use a protective plate to cover the area around the poorly sprayed parts, and pass out the parts to be treated; rub paraffin wax under the protective plate, and the amount of paraffin wax to be wiped is 0.05g / cm 2 , the protective plate is a soft PVC plate with a closed structure with a hole in the middle, and the inner side of the protective plate is arc-shaped,

[0036] 3) Spray liquid nitrogen along the inner edge of the protective plate, and spray paint remover within 10s after spraying liquid nitrogen;

[0037] 4) Then spray liquid nitrogen on the main part of the poorly sprayed part, and spray paint remover at the same time, the amount of paint remover is 0.5g / cm 2 ;

[0038] 5) After standing for 3-5 minutes, heat the main part of the poorly sprayed part, the heating temperature is 50 ℃...

Embodiment 2

[0042] A fast and efficient large-area paint spraying defect treatment process, including the following steps in sequence:

[0043] 1) Prepare the parts with bad spraying;

[0044] 2) Use a protective plate to cover the poorly sprayed parts, and pass out the parts to be treated; rub paraffin wax under the protective plate, and the amount of paraffin wax to be wiped is 0.1g / cm 2 , the protective plate is a soft PVC plate with a closed structure with a hole in the middle, and the inner side of the protective plate is arc-shaped,

[0045] 3) Spray liquid nitrogen along the inner edge of the protective plate, and spray paint remover within 3 seconds after spraying liquid nitrogen;

[0046] 4) Then spray liquid nitrogen on the main part of the poorly sprayed part, and spray paint remover at the same time, the amount of paint remover is 0.3 / cm 2 ;

[0047] 5) After standing for 3-5 minutes, heat the main part of the poorly sprayed part, the heating temperature is 65 ℃, keep for 1...

Embodiment 3

[0051] A fast and efficient large-area paint spraying defect treatment process, including the following steps in sequence:

[0052] 1) Prepare the parts with bad spraying;

[0053] 2) Use a protective plate to cover the poorly sprayed parts, and pass out the parts to be treated; wipe paraffin wax under the protective plate, and the amount of paraffin wax to be wiped is 0.08g / cm 2 , the protective plate is a soft PVC plate with a closed structure with a hole in the middle, and the inner side of the protective plate is arc-shaped,

[0054] 3) Spray liquid nitrogen along the inner edge of the protective plate, and spray paint remover within 7s after spraying liquid nitrogen;

[0055] 4) Then spray liquid nitrogen on the main part of the poorly sprayed part, and spray paint remover at the same time, the amount of paint remover is 0.4g / cm 2 ;

[0056] 5) After standing for 3-5 minutes, heat the main part of the poorly sprayed part, the heating temperature is 50-65 ℃, keep for 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of automobile manufacture, in particular to a technology for rapidly and efficiently treating large-area poor paint sprayed parts. The technology adopts liquid nitrogen and paint remover combined treatment, accelerates the poor sprayed part treatment speed, and improves the treatment efficiency; after small-area parts are treated, edges are perfectly protected, and the degree of combination between the edges subjected to secondary spraying and an original paint film is convenient to enhance; the operation technology is simple, and the labor intensity is reduced; the poor sprayed parts are thoroughly cleaned.

Description

technical field [0001] The invention relates to the field of automobile manufacturing, in particular to a fast and efficient large-area paint spraying defect treatment process. Background technique [0002] The automobile manufacturing process is divided into four major processes, stamping, welding, painting, and general assembly. The painting process is to electrophoresis, intermediate coating, and topcoat on the welded body-in-white, so that the "body-in-white" can be sprayed with added value. color. [0003] Automotive coatings can be simply divided into the following coatings: electrophoretic coatings, intermediate coatings, paint coatings, and varnish coatings. The functions and problems of each coating are as follows: [0004] Electrophoretic coating film: This coating film has anti-corrosion ability. If the coating effect is not good, it needs to be polished, but for large-area grinding and leaking iron, the car body will have the risk of rusting. On the other hand,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/24B05D1/32C09D9/04
Inventor 张凯王闯安聪慧冯擎峰
Owner ZHEJIANG GEELY HOLDING (GROUP) CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com