a breathable fabric
A technology for breathable fabrics and fabrics, which is applied to through-hole fabrics, fabrics, fabric surface trimming and other directions, can solve problems such as loss of elasticity, decreased air permeability, hard hand feeling, etc., and achieves soft hand feel, low production cost, and good air permeability.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0042] Use 78dtex-68f-NY.FDY for surface warp and inner warp, and 40 for surface and inner weft S NY spun yarn, the ratio of surface warp, inner warp and surface weft to inner weft is 1:1, the weave is a double-layer weave with continuous floating length of 3 weave points, and the through holes of the upper and lower layers are arranged vertically. The combination of top-down and bottom-up joints, threading healds in front and rear areas, weaving with 8 or 12 heald frames, the total density of the gray fabric in the warp direction is 260 threads / inch, and the total density in the weft direction is 124 threads / inch. After finishing and processing after dyeing, the finished product is finally obtained. The specific parameters are shown in Table 1.
[0043] Its main processing projects and conditions are: refining (temperature 95 °C, speed 70 m / min); pre-setting (temperature 180 °C, speed 50 m / min); acid dyeing (temperature 90 °C, time 30 min); drying (temperature 140°C, speed ...
Embodiment 2
[0045] 167dtex-48f-PET.DTY is used for surface warp and inner warp, and 40 for surface and inner weft S PET spun yarn, the surface warp, inner warp and the ratio of surface weft and inner weft are 1:1, the weave is a double-layer weave with continuous floating length of 4 weave points, and the positions of the through holes on the upper and lower layers are arranged vertically. The joint method of top connection and bottom connection and top connection is divided into front and rear areas, weaving with 8 or 12 heald frames, and the total density of gray cloth in warp direction is 192 wires / inch, and the total density of weft direction is 146 wires / inch. After finishing and processing after dyeing, the finished product is finally obtained. The specific parameters are shown in Table 1.
[0046] Its main processing projects and conditions are: refining (temperature 95°C, speed 45 m / min); drying (temperature 140°C, speed 45 m / min); presetting (temperature 190°C, speed 45 m / min); ...
Embodiment 3
[0048] Surface warp and inside warp use 56dtex-72f-PET.DTY yarn, surface weft and inside weft use 83dtex-36f-high viscosity PET / low viscosity PET.FDY yarn (twist 1500T / M), surface warp and inside warp And the ratio of surface weft and inner weft is 1:1, the organization is a double-layer structure with continuous floating length of 5 weave points, the positions of the through holes of the upper and lower layers are arranged vertically, and the upper and lower are connected with the upper joint. The method is divided into front and rear areas, weaving with 8 or 12 heald frames, and the gray cloth has a total density of 284 wires / inch in the warp direction and 184 wires / inch in the weft direction. , see Table 1 for the specific parameters.
[0049] Its main processing projects and conditions are: refining (temperature 95°C, speed 45 m / min); drying (temperature 140°C, speed 45 m / min); presetting (temperature 180°C, speed 45 m / min); alkali reduction Quantity (continuous reduction...
PUM
| Property | Measurement | Unit |
|---|---|---|
| length | aaaaa | aaaaa |
| Basis weight | aaaaa | aaaaa |
| Basis weight | aaaaa | aaaaa |