Paint with good gloss retention

A coating and acrylic paint technology, applied in polyester coatings, epoxy resin coatings, coatings, etc., can solve the problems of coating film loss of gloss and poor gloss retention of coatings, and achieve improved oil resistance and alcohol solvent resistance Good performance, not easy to aging effect

Inactive Publication Date: 2015-03-11
青岛市市南区隆德中医药研究所
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The coating film will lose its original luster when it is exposed to light, and many current coatings do not have strong gloss retention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A paint with good gloss retention is characterized in that: its component weight ratio is: 18% alkyd resin, 20% tung oil, 10% epoxy resin, 5% terephthalic acid, 3% Acrylic modified alkyd resin, 16% palm wax ester, 5% methacrylic resin, 1% isophthalic acid, 3% acrylic paint, 6% phthalic anhydride, 5% poly Vinyl butyral, 3-5% defoamer, and the rest are thinners.

[0015] The acrylic paint is matte acrylic paint, and the palm wax ester is palm oil ester. The defoamer is polysiloxane defoamer.

[0016] Preferably, the alkyd resin is made through the following steps: a) taking by weighing 5.3 moles of trimethylolpropane, 1.6 moles of phthalic anhydride, and 1.6 moles of hydroxyl substances is 0.7 moles of adipic anhydride and isononanoic acid in an amount of 0.92 moles of hydroxyl species;

[0017] b) Put isononanoic acid, trimethylolpropane, phthalic anhydride and adipic anhydride into the reactor, heat up to 90 degrees, start stirring, then heat up to 1605 degrees at a ...

Embodiment 2

[0019] A paint with good gloss retention is characterized in that: its component weight ratio is: 18% alkyd resin, 25% tung oil, 16% epoxy resin, 2% terephthalic acid, 6% Acrylic modified alkyd resin, 12% palm wax ester, 8% methacrylic resin, 1% isophthalic acid, 2% acrylic paint, 6% phthalic anhydride, 5% poly Vinyl butyral, 5% defoamer, and the rest are thinners.

[0020] The acrylic paint is glossy acrylic paint, and the palm wax ester is palm kernel ester. The defoamer is polysiloxane defoamer.

[0021] Preferably, the alkyd resin is made through the following steps: a) taking by weighing the amount of hydroxy substance is 5.3 moles of trimethylolpropane, the amount of hydroxy substance is 1.7 moles of phthalic anhydride, the amount of hydroxy substance is 0.9 moles of adipic anhydride and isononanoic acid in an amount of 0.85 moles of hydroxyl species;

[0022] b) Put isononanoic acid, trimethylolpropane, phthalic anhydride and adipic anhydride into the reaction kettle...

Embodiment 3

[0024] A paint with good gloss retention is characterized in that: its component weight ratio is: 18% alkyd resin, 30% tung oil, 16% epoxy resin, 2% terephthalic acid, 5% Acrylic modified alkyd resin, 13% palm wax ester, 5% methacrylic resin, 1% isophthalic acid, 3% acrylic paint, 6% phthalic anhydride, 10% poly Vinyl butyral, 5% defoamer, and the rest are thinners.

[0025] The acrylic paint is semi-matte acrylic paint, and the palm wax ester is palm olein. The defoamer is polysiloxane defoamer.

[0026] Preferably, the alkyd resin is made through the following steps: a) taking by weighing 5.2 moles of trimethylolpropane, 1.6 moles of phthalic anhydride, and 1.6 moles of hydroxyl substances is 0.86 moles of adipic anhydride and isononanoic acid in an amount of 0.92 moles of hydroxyl species;

[0027] b) Put isononanoic acid, trimethylolpropane, phthalic anhydride and adipic anhydride into the reactor, heat up to 92 degrees, start stirring, then heat up to 160 degrees at a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to paint, in particular to paint with good gloss retention. The paint comprises the following components in percentage by weight: 12-18% of alkyd resin, 20-30% of tung oil, 10-16% of epoxy resin, 2-5% of terephthalic acid, 3-6% of acrylate modified alkyd resin, 12-16% of palm wax ester, 5-8% of methacrylic resin, 0.5-1% of isophthalic acid, 1-3% of propylene pigment, 3-6% of phthalic anhydride, 5-10% of polyvinyl butyral, 3-5% of an antifoaming agent, and the balance of a thinner. The paint has the advantages that the use is extensive, the properties are excellent, a high-density reticular structure is formed after a paint film is dried, the paint is not easy to age, the gloss retention is good, the property of resisting mineral oil and alcohols solvents is good, and the water resistance, the insulativity and the oil resistance of the paint are greatly improved after being torrefied.

Description

technical field [0001] The invention relates to a paint, especially a paint with good gloss retention. . Background technique [0002] Coating is a material that can be coated on the surface of an object by different construction techniques to form a solid film with strong adhesion, certain strength and continuity. The film formed in this way is commonly called a coating film, also known as a paint film or a coating. It belongs to organic chemical polymer materials, and the formed coating film belongs to the type of polymer compounds. According to the classification of modern chemical products, coatings belong to fine chemical products. Modern coatings are gradually becoming a class of multifunctional engineering materials and an important industry in the chemical industry. [0003] The coating film will lose its original luster when it is exposed to light, and many coatings currently have poor gloss retention. Contents of the invention [0004] The present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D191/00C09D167/00C09D163/00C09D167/06C09D129/14C09D7/12C08G63/46C08G63/78
CPCC09D191/00C08G63/46C08G63/78C08K2201/014C08L2205/02C08L2205/035C09D7/41C09D7/63C09D7/65
Inventor 栾心展栾德东
Owner 青岛市市南区隆德中医药研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com