A technology of polyurea resin and floor coatings, applied in the field of coatings, can solve the problems of slow drying, poor impact resistance, poor flexibility, etc., and achieve the effects of high solid content, film thickness, and good wear resistance

Inactive Publication Date: 2015-04-08
SHENZHEN JIADA HIGH TECH IND DEV
View PDF1 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to overcome the above-mentioned deficiencies of the prior art, provide a kind of polyurea floor paint and preparation thereof, use method and polyurea resin, described polyurea resin is polyaspartate polyurea resin, described The polyaspartic ester polyurea resin can exist stably at normal temperature, and th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurea floor coating and preparation and application methods thereof as well as carbamide resin
  • Polyurea floor coating and preparation and application methods thereof as well as carbamide resin
  • Polyurea floor coating and preparation and application methods thereof as well as carbamide resin

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] Correspondingly, the present invention also provides the preparation method of above-mentioned polyurea floor paint, and described preparation method comprises the steps:

[0035] Step S01: Obtain each component according to the components and contents in the polyurea floor coating;

[0036] Step S02: Stir and disperse polyaspartate polyurea resin, titanium dioxide, dispersant, and barium sulfate or glass powder at high speed for 20-30 minutes;

[0037] Step S03: After reducing the rotation speed, add talc powder or fine sand and stir for 5-15 minutes, then add defoamer and leveling agent, stir for 10-20 minutes, unload and pack to obtain polyaspartic acid ester polyurea floor coating.

[0038] Wherein, in step S03, when the raw material composition of the polyurea floor coating also includes a color paste, the color paste is added together with the defoamer and the leveling agent.

[0039] In the above step S02, the polyaspartate polyurea resin can directly add titan...

Embodiment 1

[0048] A method for distributing components of a polyurea floor coating and a preparation method thereof, the polyurea floor coating contains the following components by weight:

[0049]

[0050] Its preparation method technological process comprises the following steps:

[0051] S11. Add 1.80 kg of diethyl maleate and 2.83 kg of DMDC to the reaction kettle, heat up to 65° C., react for 72 hours under stirring, and cool down to room temperature to obtain polyaspartate polyurea resin;

[0052] S12. Add titanium dioxide, barium sulfate, and a dispersant to the polyaspartate polyurea resin in step S11, and stir and disperse at high speed for 25 minutes to obtain a mixed material;

[0053] S13. After reducing the rotating speed, go to step S12 to obtain the talcum powder in the mixed material and stir for 10 minutes, then mix the blue slurry, defoamer, and leveling agent for 15 minutes, then unload, pack, and obtain a polyurea floor coating.

Embodiment 2

[0055] A component formula of polyurea floor paint and a preparation method thereof. This polyurea floor paint contains the components of following parts by weight:

[0056]

[0057] Its preparation method technological process comprises the following steps:

[0058] S21. Add 1.80 kg of diethyl maleate and 2.8 kg of DMDC to the reactor, heat up to 65° C., react under stirring for 72 hours, cool down to room temperature, and obtain polyaspartic acid ester polyurea resin;

[0059] S22. Add titanium dioxide, barium sulfate, and a dispersant to the polyaspartate polyurea resin in step S11, and stir and disperse at high speed for 25 minutes to obtain a mixed material;

[0060] S23. After reducing the rotating speed, go to step S12 to obtain the talcum powder in the mixed material and stir for 10 minutes, then add the blue paste, defoamer and leveling agent, stir for 15 minutes, unload, pack, and obtain polyurea floor coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tear strengthaaaaaaaaaa
Elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyurea floor coating and preparation and application methods thereof as well as carbamide resin. The carbamide resin is polyaspartic acid ester carbamide resin; the polyaspartic acid ester carbamide resin is prepared by reacting diethyl maleate and 3,3-dimethyl-4,4-methylenebis(cyclohexylamine) as raw materials at 60-80 DEG C for 70-74 DEG C, with the weight ratio of the diethyl maleate to the 3,3-dimethyl-4,4-methylenebis(cyclohexylamine) is 1.0 to (1.55-1.60). The polyaspartic acid ester carbamide resin can stably exist at a room temperature; the polyaspartic acid ester carbamide resin is taken as a base component; and packing, an assistant and the like are added, so as to prepare the polyurea floor coating disclosed by the invention. The polyurea floor coating and an HDI curing agent are mixed to use at a certain ratio, so that the polyurea floor coating has the advantages of good abrasive resistance, ageing resistance, waterproofness, controllable elasticity and high-strength shock resistance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a polyurea floor coating, its preparation and use method and polyurea resin. Background technique [0002] With the rapid development of my country's national economy and the continuous improvement of people's living standards, as well as the improvement of architects' design concepts, buildings are becoming more and more high-end and multi-functional. Therefore, building exterior wall products are bound to develop in the direction of high-tech and multi-functional. Among industrial floors, traditional epoxy resin floors occupy a large market, but due to their poor flexibility, poor impact resistance, slow drying, and thin one-time film formation, there are many restrictions in the use process. [0003] Therefore, the prior art has yet to be developed. Contents of the invention [0004] The object of the present invention is to overcome the above-mentioned deficiencies of the prior ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/02C09D7/12
CPCC09D175/02C08K3/34C08K3/36C08K2003/2241C08K2003/3045C09D7/40C09D7/61
Inventor 关有俊王永刚熊宸熊永强
Owner SHENZHEN JIADA HIGH TECH IND DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap