A kind of desulfurization catalyst and its preparation method and the method for hydrocarbon oil desulfurization

A desulfurization catalyst, alumina technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve problems such as reduced adsorbent activity

Active Publication Date: 2017-01-04
CHINA PETROLEUM & CHEM CORP +1
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The purpose of the present invention is to provide a desulfurization catalyst and its preparation method and a method for desulfurization of hydrocarbon oil in order to overcome the problem of reduced adsorbent activity in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of desulfurization catalyst and its preparation method and the method for hydrocarbon oil desulfurization
  • A kind of desulfurization catalyst and its preparation method and the method for hydrocarbon oil desulfurization
  • A kind of desulfurization catalyst and its preparation method and the method for hydrocarbon oil desulfurization

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The present invention also provides a method for preparing a desulfurization catalyst. The method includes: (1) subjecting a mixed solution obtained by mixing a lead-containing compound, a zinc-containing compound, and water to a precipitation reaction, and filtering, drying and filtering the mixture obtained by the precipitation reaction. Roasting to obtain a precipitated product; (2) contacting a silicon oxide source, an alumina source, a phosphorus-containing compound, water and an acid solution to form a slurry, and mixing the precipitated product obtained in step (1) with the slurry to form a carrier mixture; Then the carrier mixture is shaped, dried and calcined to form a carrier; (3) a compound containing an active metal is introduced into the carrier obtained in step (2) and dried and calcined to obtain a desulfurization catalyst precursor; the active metal is cobalt , At least one of nickel, iron and manganese; (4) reducing the desulfurization catalyst precursor ...

Embodiment 1

[0084] This example is used to illustrate the preparation method of the desulfurization catalyst of the present invention.

[0085] (1) Prepare precipitation product. Mix 10.9 kilograms of zinc acetate dihydrate powder (produced by Beijing Chemical Plant, analytically pure), 0.86 kilograms of lead acetate trihydrate (Sinopharm Chemical Reagent Company, analytically pure), and 18 kilograms of deionized water. Stir for 30 minutes and then completely dissolve. The precipitated product obtained by adding 1.8 kg of ammonia water was filtered and dried at 150°C for 2 hours, and then calcined at 500°C for 1 hour to obtain the precipitated product C1.

[0086] The precipitated product C1 was subjected to fluorescence analysis and XRD measurement. XRD spectrum (see figure 1 ) There is no diffraction peak of PbO, and the standard diffraction peak of ZnO shifts to the right, where A 100 -B 100 =0.2°, A 002 -B 002 =0.21°, A 101 -B 101 =0.2°, indicating that PbO and ZnO in the precipitation pr...

Embodiment 2

[0094] This example is used to illustrate the preparation method of the desulfurization catalyst of the present invention.

[0095] (1) Prepare precipitation product. Mix 14.0 kg of zinc nitrate hexahydrate (produced by Beijing Chemical Plant, analytically pure), 1.80 kg of lead nitrate powder (Sinopharm Chemical Reagent Company, analytically pure) and 18 kg of deionized water, stir for 30 minutes, add 2.0 kg of urea and heat to A white precipitate was obtained after treatment at 80°C for 2 hours. After filtration, it was dried at 150°C for 2 hours, and then calcined at 500°C for 1 hour to obtain precipitated product C2.

[0096] The precipitation product C2 was subjected to fluorescence analysis and XRD measurement. XRD spectrum (see figure 1 ) There is no diffraction peak of PbO, and the standard diffraction peak of ZnO shifts to the right, where A 100 -B 100 =0.25°, A 002 -B 002 =0.24°, A 101 -B 101 =0.24°, indicating that PbO and ZnO in the precipitation product C2 all form a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a desulfurization catalyst which includes following components, on the basis of the total weight of the desulfurization catalyst, by weight: 5-35% of a silicon oxide source, 5-35% of aluminum oxide, 30-70% of zinc oxide, 2-15% of lead oxide, 0.5-10% of a phosphorus oxide based on the weight of P2O5 and 5-30% of an active metal. At least partial lead oxide and the zinc oxide are formed into a zinc-lead solid solution with a general formula being Pb<x>Zn<1-x>O, wherein 0<x<=0.12 and the x refers to atom molar ratio. The active metal is at least one of cobalt, nickel, iron and manganese. The invention also provides a preparation method of the desulfurization catalyst and a hydrocarbon oil desulfurizing method. The desulfurization catalyst is better in desulfurization activity and activity stability.

Description

Technical field [0001] The invention relates to a desulfurization catalyst and a preparation method thereof and a method for desulfurizing hydrocarbon oil, in particular to a desulfurization catalyst, a preparation method of a desulfurization catalyst and a desulfurization catalyst obtained by the method, and a desulfurization catalyst for desulfurization of hydrocarbon oil Method applied in. Background technique [0002] As people pay more and more attention to environmental protection, environmental protection laws and regulations are becoming stricter. Reducing the sulfur content of gasoline and diesel is considered to be one of the most important measures to improve air quality, because the sulfur in the fuel will affect the performance of the automobile catalytic converter. Have an adverse effect. The sulfur in the exhaust gas of automobile engines can inhibit the precious metals in the converter and cause it to be irreversibly poisoned, reducing the converter's effect on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/185C10G45/06
Inventor 林伟田辉平王磊杨民舒春溪王金慧
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap