Carbon fiber bicycle disc brake base and its forming process

A carbon fiber base and bicycle technology, applied in bicycle accessories, bicycle brakes, etc., can solve the problems of damaged carbon fiber, poor product disc brake size, and affecting the strength of the base, so as to avoid damage, reduce secondary processing procedures, and ensure strength effect on longevity

Active Publication Date: 2017-01-04
上海迪诺克新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such a processing method is to carry out post-processing on the formed carbon fiber bicycle base. The drilling process will not only produce processing tolerances, resulting in poor dimensions of the product disc brake, but also damage the carbon fibers and affect the strength of the base.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber bicycle disc brake base and its forming process
  • Carbon fiber bicycle disc brake base and its forming process
  • Carbon fiber bicycle disc brake base and its forming process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0020] Such as Figure 3 to Figure 5 As shown, the present invention discloses a carbon fiber bicycle disc brake base, which includes a carbon fiber base 1 and a cylindrical nut 2. The carbon fiber base 1 is provided with two protruding feet 11, and the two protruding feet 11 are respectively provided with cylindrical nuts 2, and integrated with the carbon fiber base 1 to form a carbon fiber bicycle disc brake base.

[0021] The specific molding process of the carbon fiber bicycle disc brake base is:

[0022] Step 1. Design and process the cylindrical nut 2 with thread;

[0023] Step 2. Prefabricate the base 1 of the carbon fiber bicycle disc brake, and at the same time embed the column nuts 2 into the two protruding feet 11 of the prefabricated carbon fiber base 1;

[0024] Step 3. Place the base 1 of the carbon fiber bicycle disc brake with the pre-embedded cylindrical nut 2 in the mold A, lock the cylindrical nut 2 with the screw 3 and fix it in the positioning cavity of the mold ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a carbon fiber bicycle disc brake substrate and a molding process thereof. Processed cylindrical nuts with threads are embedded in two protruding legs of a prefabricated carbon fiber substrate; the substrate is placed in a mold, the cylindrical nuts are locked by screws and are fixed in a positioning mold cavity of the mold; the mold is closed and the substrate is molded; the mold is opened, the carbon fiber bicycle disc brake substrate is taken out, and the screws are unfastened, and thus the production of the integrated disc brake substrate is completed. The cylindrical nuts are embedded in the carbon fiber bicycle disc brake substrate, and are fixed by the screws, so that the carbon fiber bicycle disc brake substrate and the cylindrical nuts are integrally molded, and are excellently combined by utilizing the carbon fiber material characteristics; through the setprecision of the cylindrical nuts, the mounting size of a disc brake is ensured and the secondary processing steps are omitted; in addition, by the integrated molding mode, the damage to carbon fibers can be avoided, and the strength and the life of the disc brake substrate are effectively ensured.

Description

Technical field [0001] The invention relates to a method for manufacturing a bicycle disc brake base, in particular to a carbon fiber bicycle disc brake base and its forming process. Background technique [0002] With the continuous advancement of science and technology, carbon fiber composite materials (carbon fiber) are no longer limited to the use of aerospace. Various carbon fiber composite materials have also entered the lives of ordinary people, ranging from badminton rackets to cars. Carbon fiber composites are everywhere. The figure of the material. The strength of carbon fiber composite is higher than that of copper, but its own weight is less than that of aluminum. Compared with glass fiber, carbon fiber also has the characteristics of high strength and high modulus. It is a very excellent reinforced material and can be used as a new type of non-metallic material. To apply. [0003] Cooperate figure 1 , 2 As shown, the current common carbon fiber bicycle disc brake base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C65/44B62L1/02
Inventor 熊道武蔡洁
Owner 上海迪诺克新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products