Special putty for ceramic tile surface with capability of adsorbing formaldehyde and high adhesion and preparation method of special putty

A high-adhesion, formaldehyde-absorbing technology, used in filling slurry and other directions, can solve the problem of inability to completely solve the problem and high cost, and achieve the effects of low cost, reduced formaldehyde content, and excellent water resistance.

Inactive Publication Date: 2015-04-29
安徽朗凯奇科技股份有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods are not only expensive, but also cannot completely solve the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special putty for ceramic tile surface with capability of adsorbing formaldehyde and high adhesion and preparation method of special putty
  • Special putty for ceramic tile surface with capability of adsorbing formaldehyde and high adhesion and preparation method of special putty
  • Special putty for ceramic tile surface with capability of adsorbing formaldehyde and high adhesion and preparation method of special putty

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The special putty for the tile surface that absorbs formaldehyde and has high cohesive force provided in this embodiment, the specific weight parts of the raw materials are as follows:

[0046]

[0047] in,

[0048] The white Portland cement is No. 32.5 white Portland cement provided by Mingyue Chemical Co., Ltd.;

[0049] Diatomite is 800-1000 mesh ultrafine diatomite provided by Shanghai Liangjiang Titanium White Chemical Products Co., Ltd.;

[0050] Ground calcium carbonate is 400 mesh heavy calcium carbonate provided by Anzhibang;

[0051] Ash calcium powder is 400 mesh ash calcium powder provided by Anzhibang;

[0052] Quartz powder is 40-160 mesh graded quartz powder provided by Yongxing Zhushi Co., Ltd.;

[0053] The anti-formaldehyde agent is 1,3-dimethyl-2-imidazolidinone produced by Nanjing Fusheng Chemical Co., Ltd.;

[0054] Activated carbon is activated carbon produced by Pingdingshan Lvlin Activated Carbon Co., Ltd.;

[0055] The dispersible latex ...

Embodiment 2

[0064] The special putty for the tile surface that absorbs formaldehyde and has high cohesive force provided in this embodiment, the specific weight parts of the raw materials are as follows:

[0065]

[0066] A kind of preparation method of special putty for ceramic tile surface which absorbs formaldehyde and has high cohesive force is as follows:

[0067](1), take various raw materials respectively by above-mentioned weight;

[0068] (2), open the mixer, dust collector;

[0069] (3) Add 35% water to the above-mentioned raw materials and mix them until they are in the shape of putty.

Embodiment 3

[0071] The special putty for the tile surface that absorbs formaldehyde and has high cohesive force provided in this embodiment, the specific weight parts of the raw materials are as follows:

[0072]

[0073]

[0074] A kind of preparation method of special putty for ceramic tile surface which absorbs formaldehyde and has high cohesive force is as follows:

[0075] (1), take various raw materials respectively by above-mentioned weight;

[0076] (2), open the mixer, dust collector;

[0077] (3), when the mixer is at a rotating speed of 1000r / min, add 25% water to the above-mentioned raw materials and mix and stir for 35 minutes. After releasing at least 50 parts by weight of the bottom material, continue to stir for 10 minutes until the mixture is evenly putty-like.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses special putty for the ceramic tile surface with the capability of adsorbing formaldehyde and high adhesion and a preparation method of the special putty. The special putty is prepared from the following raw materials in parts by weight: 35-40 parts of white portland cement, 5-30 parts of heavy calcium carbonate, 5-10 parts of ash-calcium-powder, 5-30 parts of quartz powder, 10-15 parts of diatomite, 2-6 parts of a formaldehyde-resistant agent, 5-10 parts of activated carbon, 4-8 parts of disperable emulsion powder, 0.3-1 part of water soluble cellulose, 1-3 parts of lignocellulose and 2-4 parts of a slipping agent. The putty powder is capable of adsorbing the formaldehyde in air and removing the formaldehyde in a coating together by adsorbing, so that the indoor formaldehyde content is greatly lowered, and the human health is facilitated.

Description

technical field [0001] The invention relates to the technical field of chemical coatings, in particular to a formaldehyde-absorbing high-adhesion special putty for ceramic tile surfaces and a preparation method thereof. Background technique [0002] In our daily life, we have many opportunities to come into contact with formaldehyde, especially during the decoration of new houses, a large number of decoration materials (such as: latex paint, wood-based panels and paints, etc.) will contain formaldehyde to a greater or lesser extent. People living in an environment containing formaldehyde for a long time will harm human health through breathing and contact. [0003] As a wall decoration material, tiles have been widely used in my country due to their excellent waterproof, pollution resistance, anti-aging and other advantages. Especially in the family indoor bathroom and kitchen tiles for decoration, due to the poor quality of the tiles or bonding materials, the tiles crack, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 朱厚信杨洪涛
Owner 安徽朗凯奇科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com