Wear and ultraviolet resistant coating

An anti-ultraviolet and coating technology, applied in the field of coatings, can solve problems such as aging, achieve fast curing speed, excellent environmental protection performance, and reduce production costs

Inactive Publication Date: 2015-04-29
QINGDAO DESHENGTAI CONSTR INSTALLATION ENG
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These UV absorbers are usually org

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example 1

[0013] The present invention is a wear-resistant and anti-ultraviolet paint, which is made of the following raw materials in parts by weight:

[0014] 1.2 parts of silicon carbide powder, 0.5 parts of hardener, 6.5 parts of bisphenol A epoxy resin, 2.3 parts of perlite powder, 2.5 parts of dioctyl phthalate, 2.2 parts of OP emulsifier, 0.5 parts of sodium acetate, chlorosulfonation 0.3 parts of polyethylene and 0.2 parts of film-forming aids.

[0015] The film-forming assistant is an ether alcohol organic solvent. The hardener is a water-based epoxy resin.

Example Embodiment

[0016] Example 2

[0017] The present invention is a wear-resistant and anti-ultraviolet paint, which is made of the following raw materials in parts by weight:

[0018] 3.5 parts of silicon carbide powder, 0.8 parts of hardener, 7.8 parts of bisphenol A epoxy resin, 3.6 parts of perlite powder, 4.8 parts of dioctyl phthalate, 5.1 parts of OP emulsifier, 0.8 parts of sodium acetate, chlorosulfonation 0.5 part of polyethylene and 0.4 part of film-forming aid.

[0019] The film-forming assistant is an ether alcohol organic solvent. The hardener is a water-based epoxy resin.

[0020] The wear-resistant and anti-ultraviolet paint provided by the present invention is a good ultraviolet light-curable and scratch-resistant paint. It not only has convenient sources of raw materials, but also has excellent stability regardless of the raw material itself and the finished paint, which is convenient for industrial promotion and application, and the paint has The characteristics of fast curing s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear and ultraviolet resistant coating. The coating is prepared from the following raw materials, by weight, 1.2-3.5 parts of silicon carbide powder, 0.5-0.8 parts of a hardener, 6.5-7.8 parts of bisphenol A epoxy resin, 2.3-3.6 parts of perlite powder, 2.5-4.8 parts of dicapryl phthalate, 2.2-5.1 parts of an OP emulsifier, 0.5-0.8 parts of sodium acetate, 0.3-0.5 parts of chlorosulfonated polyethylene and 0.2-0.4 parts of a film forming assistant. The wear and ultraviolet resistant coating is a good ultraviolet-curable scratch-resistant coating, raw materials are convenient to obtain, and the raw materials and the coating respectively have excellent stability, so the industrial popularization and application of the coating are convenient; the coating also has the characteristics of fast curing speed, simple preparation technology, and substantially reduced production cost; and a coat made by using the coating has the characteristics of moderate hardness, good transmittance and the like.

Description

technical field [0001] The invention relates to a coating, in particular to a wear-resistant and anti-ultraviolet coating, which belongs to the field of coatings. Background technique [0002] Ultraviolet rays account for 5% of the solar spectrum energy, and the wavelength is below 380nm. Ultraviolet rays can cause discoloration of objects and are harmful to the human body, such as cataracts and skin cancer. Therefore, in addition to heat insulation requirements and blocking infrared penetration, heat insulation coatings also require ultraviolet blocking. Generally, in order to block ultraviolet rays, UV absorbers are added to the pressure-sensitive adhesive. These UV absorbers are usually organic and therefore have aging problems. The best way is to add anti-ultraviolet inorganic additives, such as nano-zinc oxide and other substances, to the heat-insulating coating. Blocking ultraviolet rays, in addition to protecting the human body, also has the function of protecting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/02C09D7/12
CPCC09D163/00C08L2205/025C08L2205/03C09D7/61C09D7/63
Inventor 王朝
Owner QINGDAO DESHENGTAI CONSTR INSTALLATION ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap