A preparation method of mortar with high-efficiency waterproof, moisture-proof, expansion, anti-crack and anti-seepage functions

A mortar and functional technology, applied in the field of mortar preparation, can solve problems such as damage, accelerated corrosion of steel bars, cracking and water seepage of building materials

Active Publication Date: 2016-08-24
广州市盈坚建材科技发展有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction, while accelerating the corrosion of steel bars, resulting in cracking and water seepage of building materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing mortar with high-efficiency waterproof, moisture-proof, expansion-proof, anti-crack and anti-seepage functions, characterized in that:

[0029] Weigh 282g of raw cement, 18g of cement composite additives, 750g of sand, 4g of polypropylene fiber, and 3g of naphthalene-based water reducer; put the above raw materials into a conical double-helix mixer according to the proportion and mix them evenly. The mixing time is 50 minutes. After getting the mortar;

[0030] The preparation method steps of the cement composite additive are:

[0031] Step (1): According to 32 parts of alumina clinker, 8 parts of calcined alunite, 2 parts of zinc sulfate, 12 parts of dickite, 12 parts of attapulgite clay, 12 parts of fly ash, 2 parts of zeolite powder, diatomaceous earth 3 parts, 4 parts of bentonite, 2 parts of methyl cellulose, 0.7 part of sodium sulfite, 0.7 part of quicklime, 0.4 part of calcium fluoride to prepare raw materials,

[0032] Step (2): 32 parts...

Embodiment 2

[0036] A method for preparing mortar with high-efficiency waterproof, moisture-proof, expansion-proof, anti-crack and anti-seepage functions, characterized in that:

[0037] Weigh 282g of raw cement, 18g of cement composite additives, 750g of sand, 4g of polypropylene fiber, and 3g of naphthalene-based water reducer; put the above raw materials into a conical double-helix mixer according to the proportion and mix them evenly. The mixing time is 50 minutes. After getting the mortar;

[0038] The preparation method steps of the cement composite additive are:

[0039] Step (1): According to 30 parts of alumina clinker, 10 parts of calcined alunite, 5 parts of zinc sulfate, 20 parts of dickite, 20 parts of attapulgite clay, 10 parts of fly ash, 5 parts of zeolite powder, diatomaceous earth 2 parts, 5 parts of bentonite, 1 part of methyl cellulose, 1 part of sodium sulfite, 1 part of quicklime, 0.2 part of calcium fluoride to prepare raw materials,

[0040] Step (2): 30 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of mortar with efficient water-resisting, moisture-resisting expanding, crack-resisting and seepage preventing functions. The preparation method is characterized by comprising the following steps: weighing raw materials cement, a cement compound additive, sands, polypropylene fibers and a naphthalene water reducer; putting the raw materials in a cone-shaped double helix stirrer in proportion, uniformly stirring for 50 minutes and stirring to obtain the mortar. The mortar disclosed by the invention has the efficient water-resisting, moisture-resisting, expanding, crack-resisting and seepage preventing functions and is free of corrosive action to reinforcing steel bars.

Description

technical field [0001] The invention relates to a preparation method of mortar, that is, a preparation method of mortar with high-efficiency waterproof, moisture-proof, expansion-proof, crack-proof and seepage-proof functions, and belongs to the field of building material manufacturing. Background technique [0002] During the project, the basements, roofs, roads and bridges of many buildings did not reach the designed service life, and some projects were seriously damaged after only a few years of use and had to be repaired. The main reason is that the current waterproof materials and cement plus The agent generally contains Cl-,,,,, and K+ ions are too heavy, and when added to the cement, it reacts with the active silica in the concrete to form an alkali silicate gel and cause the concrete to expand and crack. This is a common problem in engineering. Alkali-aggregate reaction also accelerates the corrosion of steel bars, resulting in cracking and water seepage of building ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B14/06C04B16/06
Inventor 肖艾平
Owner 广州市盈坚建材科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com