High-toughness wear-resisting medium manganese steel hot rolled plate and manufacturing method thereof

A manufacturing method and technology for hot-rolled sheets, which are applied in the field of wear-resistant metal material rolling, can solve the problems of poor welding performance, toughness, insufficient fatigue performance, and harsh service environment, and achieve the effects of good toughness, high hardness, and strengthening solid solution.

Inactive Publication Date: 2015-06-10
TIANJIN WILL LONG SCI &TECH CO LTD
View PDF4 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The microstructure of this type of steel is martensite or martensite-bainite, and the hardness can reach 300-600HB. However, due to the complex geological conditions of coal mining and the harsh service environment, the commonly used wear-resistant steel (wear-resistant The grade is generally 400 or 450), and its wear resi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] 1. Molten steel is smelted according to the composition ratio, poured and rolled into billets, hot-rolled to prepare steel plates, smelting process: electric arc furnace is used to smelt molten steel according to the composition ratio, and its composition is: C: 1.0, Si: 0.3, Mn: 8.5, P≤0.030, S≤0.005, Cr: 2.0, Mo: 0.35, V: 0.2, Nb: 0.003, Ti: 0.01, Al: 0.01, B: 0.003, and the rest are Fe and inevitable residual impurity elements. And refining outside the furnace.

[0026] 2. Rolling process: After the slab is heated at 1250°C, it is rolled for multiple passes. The total reduction rate is not less than 65%, the deformation rate of each pass is 10~20%, and the final rolling temperature is not lower than 1050°C.

[0027] 3. Solution heat treatment: the solution temperature should not be lower than 1050°C, and the temperature after the surface of the steel plate is controlled to be lower than 300°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-toughness wear-resisting medium manganese steel hot rolled plate and a manufacturing method thereof. The high-toughness wear-resisting medium manganese steel hot rolled plate is prepared from the following chemical components in percentage by mass: 0.8-1.2% of C, less than or equal to 0.8% of Si, 7.0-9.0% of Mn, less than or equal to 0.030% of P, less than or equal to 0.005% of S, 1.5-2.0% of Cr, 0.2-1.0% of Mo, 0.2-1.0% of Mo, 0.2-1.0% of V, less than or equal to 0.2% of Nb, less than or equal to 0.05% of Ti, less than or equal to 0.04% of Al, less than or equal to 0.003 of B and the balance of Fe and inevitable residual impurity elements. The manufacturing method of the hot rolled steel plate comprises the following steps: smelting liquid steel according to set element components, after performing vacuum degassing treatment (external refining) on the liquid steel, performing continuous casting to form a continuous casting blank or die casting and initial rolling to form a steel billet, heating the steel billet at 1250 DEG C and then performing multi-pass rolling with the total reduction rate of not lower than 65% and the pass deformation rate of 10-20% at a final rolling temperature not lower than 1050 DEG C; next, performing solution treatment on the rolled steel plate at a solution temperature not lower than 1050 DEG C, controlling the surface temperature of the steel plate after coming out of water not to be lower than 300 DEG C, and finally obtaining the steel plate, wherein the tensile strength of the obtained steel plate is 700-900MPa, the normal-temperature impact toughness Akv of the steel plate is greater than or equal to 90J, and the hardness of the steel plate after water toughening treatment is less than or equal to 250HBW. The obtained steel plate is suitable for scraper conveyor middle grooves, self-discharging truck compartment plates, ball mill lining plates, feed bin lining plates and the like applicable under the conditions of medium and low loads.

Description

technical field [0001] The invention belongs to the technical field of rolling of wear-resistant metal materials, and in particular relates to a hot-rolled plate of strong toughness wear-resistant medium manganese steel and a manufacturing method thereof. Background technique [0002] Abrasion is one of the main failure modes of materials. According to incomplete statistics, only in the metallurgy, mining, electric power, coal and agricultural machinery sectors in China, the annual economic loss caused by workpiece wear is about 40 billion yuan. Therefore, the development of wear-resistant materials directly Affected the service life of the worn workpiece. Wear-resistant steel is a kind of wear-resistant material widely used in various wear conditions. There are many types, which can be roughly divided into high-manganese steel and medium- and low-alloy wear-resistant steel. [0003] High manganese steel has excellent work hardening performance. When the material is work ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38C21D8/02
Inventor 王军祥岳宏霖高继萍
Owner TIANJIN WILL LONG SCI &TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products