Anti-corrosion material for automobile radiator intake chambers

A technology of automobile radiator and water inlet chamber, applied in the field of materials, can solve the problems of high cost, poor corrosion resistance, short service life, etc., and achieve the effects of light weight, strong corrosion resistance and long service life

Inactive Publication Date: 2015-08-26
GUIZHOU AEROSPACE KAIHONG SCI & TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention aims to provide a corrosion-resistant automobile radiator water inlet material to solve the problems of poor corrosion resistance, high cost and short service life in many radiator water inlet materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Recipe: Nylon 66 95 parts, glass fiber 20 parts, toughening agent 1.5 parts, antioxidant 1.2 parts, anti-hydrolysis agent 1.1 parts.

[0023] Preparation:

[0024] (1) raw material preparation: get nylon by weight 66 , glass fiber, toughening agent, antioxidant, anti-hydrolysis agent;

[0025] (2) Mixing preparation: nylon 66 , toughening agent, antioxidant, and antihydrolysis agent were put into the mixer and mixed for 15 minutes, and the mixture was put into the twin-screw extruder, and then the glass fiber was added into the twin-screw extruder, and the processing temperature was controlled at 250°C , melted and extruded to make a shape.

Embodiment 2

[0027] Recipe: Nylon 66 105 parts, 30 parts of glass fiber, 1.9 parts of toughening agent, 1.6 parts of antioxidant, 1.5 parts of anti-hydrolysis agent.

[0028] Preparation:

[0029] (1) raw material preparation: get nylon by weight 66 , glass fiber, toughening agent, antioxidant, anti-hydrolysis agent;

[0030] (2) Mixing preparation: nylon 66 , toughening agent, antioxidant, and antihydrolysis agent were put into the mixer and mixed for 15 minutes, and the mixture was put into the twin-screw extruder, and then the glass fiber was added into the twin-screw extruder, and the processing temperature was controlled at 250°C , after melting, extrusion can be done.

Embodiment 3

[0032] Recipe: Nylon 66 98 parts, 23 parts of glass fiber, 1.6 parts of toughening agent, 1.3 parts of antioxidant, 1.2 parts of anti-hydrolysis agent.

[0033] Preparation:

[0034] (1) raw material preparation: get nylon by weight 66 , glass fiber, toughening agent, antioxidant, anti-hydrolysis agent;

[0035] (2) Mixing preparation: nylon 66 , toughening agent, antioxidant, and antihydrolysis agent were put into the mixer and mixed for 15 minutes, and the mixture was put into the twin-screw extruder, and then the glass fiber was added into the twin-screw extruder, and the processing temperature was controlled at 250°C , after melting, extrusion can be done.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-corrosion material for automobile radiator intake chambers. The material comprises, by weight, 95 parts to 105 parts of nylon 66, 20 parts to 30 parts of glass fiber, 1.5 parts to 1.9 parts of flexibilizer, 1.2 parts to 1.6 parts of antioxidant, and 1.1 parts to 1.5 parts of hydrolysis resistance agent. A preparation method comprises raw material preparation and mixing preparation. The glass fiber can have the effect on improving the strength of the material, the plasticity of the material can be improved due to the flexibilizer, the oxidization process of polymer can be slowed down due to the antioxidant and the hydrolysis resistance agent, and therefore, the polymer can be smoothly machined, and the service life of the polymer can be prolonged. According to the method, because the ingredients and the content of the ingredients of the material are strictly controlled, the prepared material for the automobile radiator intake chambers has the advantages of being high in corrosion resistance, light in weight, high in strength, long in service life and the like, and is an excellent material for manufacturing the radiator intake chambers.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a corrosion-resistant automobile radiator water inlet chamber material. Background technique [0002] The radiator is an important part of the automobile engine cooling system, and its function is to dissipate the heat absorbed by the coolant in the engine water jacket from the high-temperature parts into the air. Therefore, the performance of the radiator directly affects the heat dissipation effect of the automobile engine, and then has a great impact on the power, economy and reliability of the automobile. With the continuous improvement of the speed and power of automobile engines, the heat load is getting higher and higher, and the requirements for cooling systems are also getting higher and higher. People pay more and more attention to the research of cooling systems including radiators. New technologies and new materials Emerging continuously, car radiators are developi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/06C08L9/02C08L23/16C08L9/00C08L33/04C08K13/04C08K7/14C08K5/18C08K5/29C08K5/3437C08J5/04
CPCC08L77/06C08J5/043C08J2377/06C08L9/02C08L23/16C08L9/00C08L33/04C08K13/04C08K7/14C08K5/18C08K5/29C08K5/3437
Inventor 付伟李强郭寅斌杨清勇
Owner GUIZHOU AEROSPACE KAIHONG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com