Adhesive for combining aluminum-foil papers and preparation method thereof

A technology of aluminum foil paper and glue, applied in the direction of adhesive type, amylose / pullulan derivative adhesive, etc., can solve the problems of non-environmental protection and high price, and achieve low raw material cost, good fluidity, The effect of simple process

Inactive Publication Date: 2015-09-16
SHANDONG JINJIAN LOGISTICS CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Like 201210555478.1, there are also problems of high price and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive for combining aluminum-foil papers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] At room temperature, add 100 parts by weight of oxidized starch to a container containing 110 parts by weight of water, stir evenly so that the oxidized starch is completely dissolved in water to obtain a mixed material liquid; add 4 parts by weight of hydrogen peroxide to the mixed material liquid After that, mix evenly, then add 4 parts by weight of borax and mix evenly, add 20 parts by weight of caustic soda and mix evenly, finally add 0.8 parts by weight of tributyl phosphate and mix evenly, you can get the aluminum foil composite adhesive agent.

Embodiment 2

[0052] The difference between this example and Example 1 is that the amounts of each raw material are different, specifically: 105 parts by weight of water, 120 parts by weight of oxidized starch, 5 parts by weight of hydrogen peroxide, 5 parts by weight of borax, 24 parts by weight of caustic soda and phosphoric acid 0.9 parts by weight of tributyl ester.

Embodiment 3

[0054] The difference between this example and Example 1 is mainly that the amount of each raw material is different, specifically: 100 parts by weight of water, 125 parts by weight of oxidized starch, 6 parts by weight of hydrogen peroxide, 6 parts by weight of borax, 25 parts by weight of caustic soda and phosphoric acid 1 part by weight of tributyl ester.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an adhesive for combining aluminum-foil papers and a preparation method thereof, and belongs to the technical field of adhesives. The adhesive consists of the following components: 100-140 parts by weight of oxidized starch, 4-6 parts by weight of borax, 20-30 parts by weight of sodium hydroxide, 4-8 parts by weight of hydrogen peroxide, 0.8-1.2 parts by weight of tributyl phosphate, and 90-110 parts by weight of water. Due to the fact that the adhesive employs the oxidized starch as the main raw material, the cost on raw materials of the adhesive is reduced, and the adhesive is environment-friendly and non-toxic; due to the fact that the hydrogen peroxide, the borax, the sodium hydroxide and the tributyl phosphate are mixed with certain amount of water under the normal temperature according to specific procedures, not only the technology is simple, but also the prepared adhesive can be stored for 12 months without influencing the character of service; therefore, the adhesive is good in stability; moreover, the adhesive contains 13-20% of solid, therefore, the adhesive is good in fluidity and is able to meet the requirements of different combining speeds.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to an adhesive for aluminum foil paper compounding and a preparation method thereof. Background technique [0002] With the development of society and economy, the packaging of commodities is also constantly updated. Packaging materials based on paper and plastic films have been gradually replaced by exquisite and beautiful aluminum foil paper. The use of aluminum foil paper is increasing. Production brings new business opportunities. [0003] Aluminum foil paper is made of 10-20 micron thick aluminum foil and 20-70 micron thick paper bonded by glue. The aluminum foil and paper used are very thin, and the amount of glue used is relatively small, which affects the stability and fluidity of the glue. put forward higher requirements. In order to achieve the bonding and compounding of aluminum foil and paper, Chinese invention patent application 201210555478.1 discloses ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/20
Inventor 周英
Owner SHANDONG JINJIAN LOGISTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap