Steel plate for cryogenic spherical tank container and production method thereof

A production method and steel plate technology, applied to 0.5NiDR steel plate for low-temperature spherical tanks and its production field, can solve problems such as high cost and poor Z-direction performance, achieve high low-temperature impact energy, enhance market competitiveness, and reduce costs Effect

Active Publication Date: 2017-11-10
WUYANG IRON & STEEL
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mechanical properties of domestic large-thickness, large-weight steel, such as negative temperature impact energy at 1 / 2 of the plate thickness, especially the Z-direction performance is not good, and the production cost is high, resulting in domestic large-thickness, large single-weight steel plates for low-temperature pressure vessels Can not meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel plate for cryogenic spherical tank container and production method thereof
  • Steel plate for cryogenic spherical tank container and production method thereof
  • Steel plate for cryogenic spherical tank container and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: The 0.5NiDR steel plate used for the low-temperature spherical tank container adopts the following composition and production process.

[0033] The thickness of this 0.5NiDR steel plate is 26mm, which is smelted from the following components by weight percentage: C 0.05%, Si 0.16%, Mn 1.57%, Ni 0.31%, P 0.008%, S 0.001%, Al 0.042%, Nb 0.039%, the balance is iron and unavoidable impurities.

[0034] The processing step of this 0.5NiDR steel plate production method is as follows:

[0035] (1) Casting process: the billet is produced by continuous casting process.

[0036] (2) Heating process: all steel billets are subjected to Group II steel heating system; the maximum heating temperature of steel billets is 1220°C, the soaking temperature is 1200°C, and the total heating time is 12min / cm.

[0037] (3) Rolling process: After the steel billet is heated, the final rolling temperature of the first stage is 1070°C; the starting rolling temperature of the second...

Embodiment 2

[0041] Embodiment 2: The 0.5NiDR steel plate used for the low-temperature spherical tank container adopts the following composition and production process.

[0042] The thickness of this 0.5NiDR steel plate is 40mm, which is smelted from the following components by weight: C 0.12%, Si 0.35%, Mn 1.24%, Ni 0.80%, P 0.006%, S 0.003%, Al 0.034%, Nb 0.028%, the balance is iron and unavoidable impurities.

[0043] The processing step of this 0.5NiDR steel plate production method is as follows:

[0044] (1) Casting process: the billet is produced by continuous casting process.

[0045] (2) Heating process: all steel billets are subjected to Group II steel heating system; the maximum heating temperature of steel billets is 1220°C, the soaking temperature is 1180°C, and the total heating time is 14min / cm.

[0046] (3) Rolling process: After the billet is heated, the final rolling temperature of the first stage is 1050°C; the starting temperature of the second stage rolling is 900°C, ...

Embodiment 3

[0050] Embodiment 3: The 0.5NiDR steel plate used for the low-temperature spherical tank container adopts the following composition and production process.

[0051] The thickness of the 0.5NiDR steel plate is 8mm, which is smelted from the following components by weight: C 0.10%, Si 0.15%, Mn 1.38%, Ni 0.65%, P 0.010%, S 0.004%, Al 0.026%, Nb 0.031%, the balance is iron and unavoidable impurities.

[0052] The processing step of this 0.5NiDR steel plate production method is as follows:

[0053] (1) Casting process: the billet is produced by continuous casting process.

[0054] (2) Heating process: all steel billets are subjected to Group II steel heating system; the maximum heating temperature of steel billets is 1220°C, the soaking temperature is 1190°C, and the total heating time is 10min / cm.

[0055] (3) Rolling process: After the billet is heated, the final rolling temperature of the first stage is 1100°C; the starting temperature of the second stage rolling is 930°C, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel plate for a low-temperature spherical tank container and a heat treatment production method thereof, which is smelted from the following components by weight percentage: C≤0.12%, Si 0.15%-0.50%, Mn 1.2%-1.6%, Ni 0.3 %~0.8%, P≤0.010%, S≤0.005%, Al 0.020%~0.045%, Nb≤0.040%, the balance is Fe and unavoidable impurities. The chemical composition design of the steel plate of the present invention adopts low-cost carbon and manganese solid solution strengthening, and by adjusting and optimizing the ratio of other elements in the steel plate, it can ensure good mechanical properties of the steel plate under the condition of low carbon equivalent, so that the steel plate has good structure, comprehensive Performance and welding performance, but also reduce costs and enhance market competitiveness. The method obtains a uniform ferrite+tempered sorbite structure through a reasonable heat treatment process, and improves the impact toughness of a large thickness steel plate; 25%, simulating post-weld performance, good welding performance, and good mechanical properties.

Description

technical field [0001] The invention relates to a steel plate for a low-temperature pressure vessel and a production method thereof, in particular to a 0.5NiDR steel plate for a low-temperature spherical tank vessel and a production method thereof. Background technique [0002] Since the 1990s, Wugang has successfully mass-produced 16MnDR, 15MnNiDR, 09MnNiDR, SA203E (08Ni3DR, 3.5Ni) and other low-temperature pressure vessel steel plates (minimum service temperature -70°C), which are widely used in the manufacture of low-temperature welded pressure vessels; change It broke the long-term dependence on imports of steel plates for low-temperature equipment in China, and made positive contributions to the localization of low-temperature equipment for large-scale projects. [0003] The steel plates for low-temperature pressure vessels produced by Wuyang Iron and Steel Co., Ltd. have pure steel, low inclusion content, excellent performance, good strength-toughness and low-temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D8/02C22C38/08C22C38/12
Inventor 刘丹贾国生谢良法韦明彭世宝李杰刘利香宋庆吉张海军张志军高雅徐腾飞王晓书
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com