Preparation process of greyness temmoku oil-spot glaze porcelain

A preparation process and technology of Tianmu glaze, applied in the field of ceramic manufacturing, can solve the problems of unstable quality and low yield

Inactive Publication Date: 2015-10-21
史江伟
View PDF5 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The change of the glaze layer in the high-temperature melting state cannot be visually observed and controlled. Subtle changes in external conditions or difficult to control the heat during the firing process often lead to low yield and unstable quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] A kind of preparation technology of gray spot tianmu oil drop glaze, comprises the following steps:

[0030] Step 1. After mixing the carcass raw materials evenly according to a certain ratio, stir them with water at a mass ratio of 1:1 to obtain a mixture; grind the mixture into a slurry with a ball mill, and finely grind it for 20-60 minutes to reach a fineness of 250-300 After mixing and beating the mud for 6-20 hours, the resulting whipped mud is molded into a plain tire, and the plain tire is put into a kiln for 4-5 hours at 860-950°C for 4-5 hours, and then cooled to room temperature with the furnace ,spare;

[0031] Step 2: Mix the Tianmu glaze raw materials according to a certain ratio and put them into the ball mill, add water with the same total weight as the Tianmu glaze raw materials, start the wet grinding for 40-80 minutes, and the fineness of the wet-milled Tianmu glaze slurry is 300-400 mesh, statically Place it for 24 hours, use a moisture meter to det...

Embodiment 1

[0048] Firing a kind of gray spot Tianmu oil drop glaze porcelain includes the following steps:

[0049] Step 1. Mix the carcass raw materials according to the weight ratio of 30 parts of quartz sand, 10 parts of ilmenite ore, 20 parts of white clay, 6 parts of soda stone, 7 parts of wood knot clay, 3 parts of feldspar and 1.5 parts of talc. , mixed with water in a mass ratio of 1:1 to obtain a mixture; the mixture was ground into a slurry with a ball mill, finely ground for 20 minutes, and the fineness reached 250 mesh; after mixing and whipping the slurry for 6 hours, the resulting whipped slurry was hand-pulled Shaped into a plain tire, put the plain tire into the kiln for 4 hours at 860°C after standing to dry, then cool to room temperature with the furnace, and set aside;

[0050] Step 2. Mix the raw materials of Tianmu glaze according to the ratio of 65 parts by weight of black medicine soil and 25 parts of ilmenite ore, and put them into the ball mill, add water with th...

Embodiment 2

[0054] Firing a kind of gray spot Tianmu oil drop glaze porcelain includes the following steps:

[0055] Step 1. Mix the carcass raw materials according to the proportion of 32 parts of quartz sand, 12 parts of ilmenite ore, 22 parts of clay, 7 parts of soda stone, 8 parts of wood knot clay, 3 parts of feldspar and 2 parts of talc in parts by weight. , mixed with water in a mass ratio of 1:1 to obtain a mixture; the mixture was ground into a slurry with a ball mill, finely ground for 30 minutes, and the fineness reached 270 mesh; after mixing and whipping the slurry for 8 hours, the resulting whipped slurry was hand-pulled Shaped into a plain tire, put it into the kiln for 4 hours at 880°C and cool it down to room temperature with the furnace, and set aside for later use;

[0056] Step 2. Mix the Tianmu glaze raw materials according to the ratio of 68 parts by weight of black medicine soil and 28 parts of ilmenite ore and put them into the ball mill, add water with the same to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a preparation process of greyness temmoku oil-spot glaze porcelain. The preparation process comprises the following steps of 1, body firing, 2, glaze preparation, 3, glazing and 4, firing. The glaze is composed of black powder soil and ferrotitanium ore, the black powder soil accounts for 65-75 parts of the total weight of temmoku glaze raw materials, and the ferrotitanium ore accounts for 25-35 parts of the total weight of the temmoku glaze raw materials. The preparation process of the greyness temmoku oil-spot glaze porcelain comprises the steps that the ferrotitanium ore is included in the glaze materials, and comprises the main components of pseudobrookite, Ti is adopted as color development reagent of temmoku glaze greyness, bubbles in a glaze layer float upwards to break through a glaze face, grey corrosion is left on the glaze face, and due to the fact that iron elements are black in the firing process, the glazing color is shown as black-background grain with the grey corrosion. Due to the fact that a large amount of the black powder soil is added to the glaze materials, the glaze material formula of greyness temmoku oil-spot glaze fired in ancient times is restored to the maximum extent, and the fired glaze is plain and dignified in color, and is of great momentum.

Description

technical field [0001] The invention relates to the field of ceramic manufacturing, in particular to a preparation process for gray-spotted Tianmu oil-drop glazed porcelain. Background technique [0002] Tianmu glaze is the name of the black cup fired in Jian kiln in Japan. Jian kiln is represented by Jianyang, Fujian Province today. The kiln site is located in Shuiji Town, Jianyang, and is famous for producing black porcelain. It was created in the Tang Dynasty, became the most popular in the Song Dynasty, especially the Southern Song Dynasty, and ended in the Qing Dynasty. [0003] Among the varieties of ceramic art glazes in our country, "Tianmu glaze" originated from the Song Dynasty, and it first referred to the tea cups of Jian Kiln in Fujian and Jizhou Kiln in Jiangxi. Oil drop, iron embroidery, Yaobian, etc. The firing technique of Tianmu glaze is called "divine skill". The magical skill "divine" is applying a glaze color. Once fired, it will present colorful, unp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/34C04B33/13C04B41/86
Inventor 史江伟
Owner 史江伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap