Method for making low basis weight manila board from wood fiber

A low-quantity, white-on-gray technology, applied in pulp beating/refining methods, natural cellulose pulp/paper, papermaking, etc., can solve the problems of fiber performance degradation and increased production costs, and achieve low production costs and cost savings , Improve the effect of bulk

Active Publication Date: 2015-10-21
DONGGUAN NINE DRAGONS PAPER IND
View PDF10 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the current waste paper and papermaking industry, gray-bottom whiteboard paper is mainly produced from waste paper, but the performance of fibers in waste paper is greatly reduced after repeated use. I

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0063] Example 1

[0064] A method for manufacturing low-weight gray-bottomed whiteboard paper using wood fiber includes the following steps:

[0065] A. Dissolve: Disperse and dissolve wood fibers to obtain wood fiber slurry;

[0066] B. Beating: beating the wood fiber slurry after dissolution treatment;

[0067] C. Coarse screening: Coarse screening the wood fiber slurry after beating treatment;

[0068] D. Purification: The wood fiber slurry treated by coarse screen is mixed with MW slurry, and then subjected to fine sieving, slag removal, concentration and thermal dispersion treatment to prepare the core layer slurry for manufacturing coated white paper;

[0069] E. Papermaking: process the surface layer slurry, lining layer slurry, bottom layer slurry and the core layer slurry prepared in step D to produce low-weight gray-bottom white paper.

[0070] In the step A, the mass percentage concentration of the wood fiber in the wood fiber slurry is 2%; the length of the wood fiber in the ...

Example Embodiment

[0084] Example 2

[0085] The difference between the present invention and the above-mentioned embodiment 1 is:

[0086] In the step A, the mass percentage concentration of the wood fiber in the wood fiber slurry is 3%; the length of the wood fiber in the wood fiber slurry is 0.3 cm and the width is 0.08 mm.

[0087] In the step B, the pulp freeness is 600 CSF; in the step C, the sieve diameter used for the coarse screen is 2 mm.

[0088] In the step D, the weight ratio of the wood fiber pulp to the MW pulp is 4:96, and the MW pulp is a mixed waste paper pulp with a brightness of 38% ISO.

[0089] In the step D, the sieve aperture used for the fine sieve is 0.1 mm, and the fine sieve pressure is 200 KPa.

[0090] The front pre-coating paint includes the following raw materials by weight: 54 parts of calcium carbonate, 24 parts of kaolin, 10.4 parts of latex, 0.18 parts of water repellent, 0.02 parts of antifoaming agent, 0.05 parts of dispersant, 0.03 parts of bactericide, rheological 0...

Example Embodiment

[0097] Example 3

[0098] The difference between the present invention and the above-mentioned embodiment 1 is:

[0099] In the step A, the mass percentage concentration of the wood fiber in the wood fiber slurry is 3%; the wood fiber in the wood fiber slurry has a length of 0.4 cm and a width of 0.1 mm.

[0100] In the step B, the pulp freeness is 625 CSF; in the step C, the sieve diameter used for the coarse screen is 3 mm.

[0101] In the step D, the weight ratio of the wood fiber pulp to the MW pulp is 4:96, and the MW pulp is a mixed waste paper pulp with a brightness of 40% ISO.

[0102] In the step D, the sieve aperture used for the fine sieve is 0.15 mm, and the fine sieve pressure is 220 KPa.

[0103] The front pre-coating paint includes the following raw materials by weight: 58 parts of calcium carbonate, 28 parts of kaolin, 10.8 parts of latex, 0.25 parts of water repellent, 0.02 parts of antifoaming agent, 0.06 parts of dispersant, 0.03 parts of bactericide, rheology 0.55 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of papermaking, in particular to a method for making a low basis weight manila board from wood fiber. The method comprises the steps of: A. dissolution, i.e. dispersing wood fiber and conducting dissolution treatment to obtain a wood fiber slurry; B. beating, i.e. conducting beating treatment on the wood fiber slurry subjected to dissolution treatment; C. coarse screening, i.e. conducting coarse screening treatment on the wood fiber slurry subjected to beating treatment; D. purification, i.e. mixing the wood fiber slurry subjected to coarse screening treatment with an MW slurry, then carrying out fine screening, slag removal, concentration and heat dispersion treatment, thus obtaining a core layer slurry for making coated white board paper; E. papermaking, i.e. processing a surface layer slurry, a lining slurry, a bottom slurry and the core layer slurry prepared by step D to obtain the low basis weight manila board. The method provided by the invention can effectively improve the bulkness of finished paper, reduces the paper basis weight exceeding problem, at the same time avoids the penetration point problem of thick and large wood fiber in finished paper, and greatly reduces the production cost.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a method for manufacturing low-weight gray-bottomed white board paper using wood fibers. Background technique [0002] In the current waste paper and papermaking industry, gray-bottom whiteboard paper is mainly produced from waste paper, but the performance of fibers in waste paper is greatly reduced after repeated use. In order to ensure the various indicators of paper, most paper mills will Use high-priced waste paper raw materials or even add raw wood pulp to improve production, but this method will increase production costs. Therefore, it is necessary to develop a method for producing gray-bottomed whiteboards that can increase the bulk of gray-bottomed whiteboards without increasing production costs. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies existing in the prior art, the object of the present invention is to provide a m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H11/00D21H11/14D21B1/34D21D1/30D21D5/02D21H19/80D21H19/44
Inventor 张成飞刘金山林新阳
Owner DONGGUAN NINE DRAGONS PAPER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap