A UV-cured transfer high-gloss decorative plate and its manufacturing method

A manufacturing method and technology for decorative panels, which are used in building construction, covering/lining, construction, etc. to achieve the effects of smooth and wear-resistant surface, fast curing speed and wide application range

Active Publication Date: 2018-01-30
中关村人居环境工程与材料研究院
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problems described above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A UV-cured transfer high-gloss decorative plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0058] 1) Dedusting the back of the plasterboard;

[0059] 2) Apply a 0.05mm thick sealing paint on the back of the plasterboard by single roller coating, and use a double mercury lamp curing machine for 3s UV curing;

[0060] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0061] 4) Coat the front of the plasterboard with a 0.05mm thick adhesion primer by means of forward and reverse roller coating, and use a double gallium lamp curing machine for 3s UV curing;

[0062] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0063] 6) Apply a 0.05mm thick white primer with a single roller, and use a double gallium lamp curing machine for 3s UV curing;

[0064] 7) Apply a 0.05mm thick sealing primer with positive ...

Embodiment 2

[0074] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0075] 1) Dedusting the back of the plasterboard;

[0076] 2) Apply a 0.08mm thick sealer paint on the back of the plasterboard with a single roller coating method, and use a double mercury lamp curing machine for 6s UV curing;

[0077] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0078] 4) Coat the front of the plasterboard with a 0.08mm thick adhesion primer by means of forward and reverse roller coating, and use a double gallium lamp curing machine for 6s UV curing;

[0079] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0080] 6) Apply a 0.08mm thick white primer with a single roller, and use a double gallium lamp curing machine for 6s UV curing;

[0081] 7) Apply a 0.08mm thick sealing primer with...

Embodiment 3

[0091] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0092] 1) Dedusting the back of the plasterboard;

[0093] 2) Apply a 0.12mm thick sealer paint on the back of the plasterboard with a single roller coating method, and use a double mercury lamp curing machine for 10s of UV curing;

[0094] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0095] 4) Apply a 0.12mm-thick adhesion primer to the front of the plasterboard by means of forward and reverse roller coating, and use a double-gallium lamp curing machine for 10s of UV curing;

[0096] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0097] 6) Apply a 0.12mm thick white primer with a single roller, and use a double gallium lamp curing machine for 10s of UV curing;

[0098] 7) Apply a 0.12mm thick sealing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an ultraviolet light curing transfer high-gloss decorative plate and a manufacturing method thereof. The manufacturing method includes: (1) forming a primer surface on the front surface of the decorative substrate; (2) sizing the primer surface, covering the transfer film, and performing ultraviolet curing, and then removing the transfer film; (3) The front surface of the substrate is coated with color paint and cured by ultraviolet light; (4) a high-gloss finish paint is rolled on the cured color paint and cured by ultraviolet light. The decorative board has the characteristics of high-definition simulation, bright and saturated color, smooth and wear-resistant surface, light weight and low price.

Description

technical field [0001] The invention relates to a decorative board and a manufacturing method thereof, in particular to an ultraviolet light-cured transfer high-gloss decorative board and a manufacturing method thereof. Background technique [0002] Ultraviolet light (UV) curing is to use the photosensitivity of the photoinitiator (photosensitizer) to form excited ecological molecules under the irradiation of ultraviolet light, and decompose them into free radicals or ions, so that unsaturated organic compounds can be polymerized, grafted, and exchanged. Combined chemical reactions to achieve the purpose of curing. UV curing technology has been applied in the manufacture of decorative panels. Substrates using UV curing technology include cement pressure boards, solid wood multilayer boards, density boards, and glass magnesium fireproof boards. However, the UV-cured decorative boards manufactured with the above-mentioned types of boards as substrates cannot meet the current...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/07E04F13/14
Inventor 赵金平王弘书冯小江唐门辉刘雪婧高秀慧
Owner 中关村人居环境工程与材料研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com