Anti-sedimentation release agent and preparation method thereof
A release agent and anti-sedimentation technology, which is applied in the direction of manufacturing tools, casting molding equipment, metal processing equipment, etc., can solve the problem of increased viscosity of the release agent, difficulty in bonding the release agent, and easy sedimentation of the components of the release agent, etc. question
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0017] The present invention also provides a preparation method of anti-sedimentation release agent, comprising:
[0018] 1) Soak attapulgite in hydrochloric acid solution after calcining, and then filter to obtain modified attapulgite;
[0019] 2) The mold release agent is prepared by mixing modified attapulgite, sodium alginate, soybean wax, aluminum dihydrogen phosphate, nonylphenol ether polyoxyethylene ether, aluminum oxide and an organic solvent.
[0020] In the above-mentioned preparation method, the specific type of organic solvent can be selected in a wide range, as long as other components can be uniformly dispersed in the organic solvent, but in order to make the prepared mold release agent have more excellent Viscosity and anti-settling properties, preferably, the organic solvent is selected from one or more of ethyl acetate, ethanol and n-hexane.
[0021] In the above-mentioned preparation method, the specific content of each component can be selected in a wide r...
Embodiment 1
[0028] 1) Calcining attapulgite at 600° C. for 12 hours, soaking it in hydrochloric acid solution (the concentration of hydrochloric acid is 25% by weight) at 40° C. for 7 hours, and then filtering to obtain modified attapulgite;
[0029] 2) Mix modified attapulgite, sodium alginate, soybean wax, aluminum dihydrogen phosphate, nonylphenol ether polyoxyethylene ether, aluminum oxide and organic solvent (the weight ratio is 60:25:4:12:5:27 : 100) were mixed at 25°C for 45 minutes to prepare the release agent A1.
Embodiment 2
[0031] 1) After calcining attapulgite at 500° C. for 10 h, soaking it in hydrochloric acid solution (the concentration of hydrochloric acid is 20% by weight) at 35° C. for 6 h, and then filtering to obtain modified attapulgite;
[0032] 2) Mix modified attapulgite, sodium alginate, soybean wax, aluminum dihydrogen phosphate, nonylphenol ether polyoxyethylene ether, aluminum oxide and organic solvent (the weight ratio is 50:10:3:9:2:25 : 100) mixed at 15°C for 30 minutes to prepare release agent A2.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com