High-viscosity waterproof material for architecture and preparation method therefor

A building waterproof and high-viscosity technology, applied in the field of building materials, can solve the problems of not easy oxidation and aging, and achieve the effects of not easy oxidation and aging, improving adhesion and heat resistance

Inactive Publication Date: 2015-11-11
唐秀克
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to solve the problems existing in existing building waterproof materials, and provide a high-viscosity building waterproof material and its preparation method. Long life and other advantages, so as to achieve a good waterproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A high-viscosity building waterproof material, comprising the following components by weight:

[0024] Acrylic resin 20kg, rosin pentaerythritol ester 8kg, vinyl acetate copolymer rubber powder 5kg, talcum powder 15kg, aluminum silicate 10kg and 1070 antioxidant 3kg.

[0025] The specific preparation and production steps are as follows: put the above raw materials into a pulverizer and pulverize them to 100 mesh to obtain raw material powder; then add the above raw material powder into a mixer, stir at a speed of 300r / min for 20min, and pack to obtain a high-viscosity building waterproof material.

Embodiment 2

[0027] A high-viscosity building waterproof material, comprising the following components by weight:

[0028] Acrylic resin 25kg, rosin pentaerythritol ester 10kg, vinyl acetate and ethylene tertiary carbonate copolymer rubber powder 5kg, talcum powder 20kg, sodium silicate 8kg and 1010 antioxidant 4kg.

[0029] The specific preparation and production steps are as follows: put the above raw materials into a pulverizer and pulverize them to 100 mesh to obtain raw material powder; then add the above raw material powder into a mixer, stir at a speed of 500r / min for 20min, and pack to obtain a high-viscosity building waterproof material.

Embodiment 3

[0031] A high-viscosity building waterproof material, comprising the following components by weight:

[0032] Acrylic resin 30kg, rosin glyceride 8kg, vinyl acetate and vinyl acetate homopolymer rubber powder 6kg, talcum powder 18kg, sodium silicate 10kg and 1070 antioxidant 4kg.

[0033] The specific preparation and production steps are as follows: put the above raw materials into a pulverizer and pulverize them to 150 mesh to obtain raw material powder; then add the above raw material powder into a mixer, stir at a speed of 300r / min for 25min, and pack to obtain a high-viscosity building waterproof material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-viscosity waterproof material for architecture and a preparation method therefor. The high-viscosity waterproof material contains the following raw materials in parts by weight: 20-35 parts of acrylic resin, 8-12 parts of rosin resin, 3-7 parts of redispersible latex powder, 15-20 parts of talcum powder, 8-12 parts of silicate and 3-5 parts of antioxidant. The high-viscosity waterproof material has the advantages of low cost, good viscosity, difficulty in oxidating and aging, high tensile strength, long service life, good waterproof effect and the like and can serve as a good waterproof material for interior architecture.

Description

technical field [0001] The invention relates to building materials, in particular to a building waterproof material and a preparation method thereof. Background technique [0002] Waterproof materials are very important building materials, belonging to functional building materials, and their performance determines the quality of building waterproofing to a large extent. Waterproofing of construction projects is related to the use value, use conditions and sanitary conditions of buildings, affects people's production activities, quality of work and life, and plays an important role in ensuring project quality. With the continuous improvement of social living conditions, people pay more and more attention to their own quality of life, and people also put forward higher requirements for the quality and performance of housing construction, and the requirements for waterproof conditions continue to increase. Waterproof material is the material basis of waterproof engineering, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/00C08L93/04C08L31/04C08K3/34C08K5/103
Inventor 唐秀克
Owner 唐秀克
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap