pi‑aln‑ptfe ternary nanocomposite porous membrane material and its preparation method and application

A nano-composite, PTFE-NP technology, applied in the direction of electrical components, electrolytic capacitors, non-aqueous electrolyte batteries, etc., can solve the problems of low battery charge retention, large surface pore size, high porosity, etc., to improve electrical breakdown Effect of Strength, Small Surface Pore Size, Good Pore Structure

Active Publication Date: 2017-04-05
JIANGXI NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since this electrospun nanofiber separator is a non-woven fabric stacked by fibers, it has too high porosity and too large surface pore size, resulting in a low charge retention rate of the battery and frequent micro-short circuits. Especially when the thickness of the battery separator is low, such as below 30 microns, the probability of this situation is quite high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]An organic / inorganic ternary nanocomposite membrane material, which is based on electrospun polyimide (PI) nanofiber nonwoven fabric, and the pores of the substrate are filled with polytetrafluoroethylene nanospheres (PTFE-NP) and aluminum nitride nanoparticles (AlN-NP), the weight ratio of the two is 42 / 38;

[0035] Its preparation method is as follows:

[0036] (1) Water-based mixed suspension of polytetrafluoroethylene nanospheres and aluminum nitride nanoparticles (PTFE-NP / AlN-NP / H 2 O-1) configuration: 70.0 grams of polytetrafluoroethylene nanospheres (mainly distributed in diameter 300nm) emulsion (solid content 60wt%), 38.0 grams of aluminum nitride nanoparticles (mainly distributed in 200nm), ammonium polyacrylate 0.3 grams, 8.7 grams of butyl acrylate-isooctyl acrylate copolymer, 328.0 grams of distilled water, put them in a beaker at one time, emulsify at a speed of 8000 revolutions per minute, and form a polytetrafluoroethylene nanometer with an absolute visc...

Embodiment 2

[0040] An organic / inorganic ternary nanocomposite membrane material, which is based on electrospun polyimide (PI) nanofiber nonwoven fabric, and the pores of the substrate are filled with polytetrafluoroethylene nanospheres (PTFE-NP) and aluminum nitride nanoparticles (AlN-NP), the weight ratio of the two is 30 / 50;

[0041] Its preparation method is as follows:

[0042] (1) Water-based mixed suspension of polytetrafluoroethylene nanospheres and aluminum nitride nanoparticles (PTFE-NP / AlN-NP / H 2 O-2) configuration: 50.0 grams of polytetrafluoroethylene nanospheres (mainly distributed in diameter 300nm) emulsion (solid content 60wt%), 50.0 grams of aluminum nitride nanoparticles (mainly distributed in 100nm), ammonium polyacrylate 0.4 grams, 8.6 grams of butyl acrylate-isooctyl acrylate copolymer, 570.0 grams of distilled water, put them in a beaker at one time, emulsify at a speed of 8000 revolutions per minute, and form a polytetrafluoroethylene nanometer with an absolute vis...

Embodiment 3

[0046] An organic / inorganic ternary nanocomposite membrane material, which is based on electrospun polyimide (PI) nanofiber nonwoven fabric, and the pores of the substrate are filled with polytetrafluoroethylene nanospheres (PTFE-NP) and aluminum nitride nanoparticles (AlN-NP), the weight ratio of the two is 30 / 50;

[0047] Its preparation method is as follows:

[0048] (1) Water-based mixed suspension of polytetrafluoroethylene nanospheres and aluminum nitride nanoparticles (PTFE-NP / AlN-NP / H 2 O-3) configuration: 50.0 grams of polytetrafluoroethylene nanospheres (mainly distributed in diameter 300nm) emulsion (solid content 60wt%), 50.0 grams of aluminum nitride nanoparticles (mainly distributed in 500nm), ammonium polyacrylate 0.5 grams, 8.5 grams of butyl acrylate-isooctyl acrylate copolymer, 415.0 grams of distilled water, put them in a beaker at one time, emulsify at a speed of 8000 revolutions per minute, and form a polytetrafluoroethylene nanometer with an absolute vis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nanocomposite multi-porous membrane material, which uses polyimide (PI) nanofiber non-woven fabric as a base material, and the pores of the base material are filled with composite nanoparticles; it is characterized in that: the composite The nanoparticles are composed of polytetrafluoroethylene nanospheres (PTFE-NP) and aluminum nitride nanoparticles (AlN-NP) mixed in a weight ratio of (7-12) / (8-13). The nanocomposite multi-porous membrane material provided by the invention has high temperature resistance, high hardness, moderate porosity, moderate areal density, good ion transport and excellent mechanical properties. The imide nanofiber diaphragm causes the problem of micro-short circuit of the battery due to high porosity; it can solve the serious problem of thermal runaway caused by mechanical collision of power lithium-ion batteries.

Description

technical field [0001] The invention belongs to the field of battery diaphragms and relates to a multi-porous membrane material, in particular to an organic / inorganic ternary nanocomposite material, a preparation method thereof and an application as a battery diaphragm. Background technique [0002] As the power battery of new energy vehicles, lithium-ion batteries have been developed rapidly and will become an indispensable daily necessities for human beings. However, since the currently used lithium battery separator is a polyolefin porous membrane material with poor temperature resistance, at a higher temperature, or in the case of overcharging, overdischarging and mechanical damage, lithium-ion batteries are prone to smoke, Fire, even explosion and other hidden dangers that endanger the safety of users. Therefore, improving the safety of lithium-ion batteries is the key to promoting the application of lithium-ion batteries in automotive power and other fields. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16H01M10/05H01G9/02H01M50/403H01M50/457H01M50/489H01M50/491
CPCH01M10/05H01G9/02H01M50/446Y02E60/10
Inventor 侯豪情冯艳熊天柔周刚勇朱丽徐海波周松智
Owner JIANGXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com