Method for manufacturing specially-shaped saturated butadiene-acrylonitrile rubber-fiber diaphragm

A technology of nitrile rubber and cloth diaphragm, which is applied in the field of rubber cloth products, can solve the problems of cloth breakage, surface wrinkling and deformation, etc., to ensure uniformity, improve the pass rate, and avoid wrinkles and cloth breakage Effect

Inactive Publication Date: 2015-11-25
南京金三力高分子科技有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the surface wrinkle deformation of the surface of the special-shaped saturated nitrile rubber cloth diaphragm in the prior art, and the problem of cloth fracture, and a kind of manufacturing method of the special-shaped saturated nitrile rubber cloth diaphragm is provided. The technical solution of the invention can solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing specially-shaped saturated butadiene-acrylonitrile rubber-fiber diaphragm
  • Method for manufacturing specially-shaped saturated butadiene-acrylonitrile rubber-fiber diaphragm
  • Method for manufacturing specially-shaped saturated butadiene-acrylonitrile rubber-fiber diaphragm

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In conjunction with accompanying drawing, the vulcanization molding die of a kind of special-shaped saturated acrylonitrile-butadiene rubber cloth diaphragm of the present embodiment comprises mold upper mold 1, mold middle mold 2 and mold lower mold 3 (such as figure 2 shown). The bottom of the mold upper die 1 of the present embodiment is an outwardly protruding rotating body (such as image 3 As shown), the side of the cross-section of the rotating body includes the first arc segment 41 of the upper die, the second arc segment 42 of the upper die, the third arc segment 43 of the upper die, the fourth arc segment 44 of the upper die and the upper die arc segment 44 connected sequentially from top to bottom. As for the fifth arc segment 45, the bottom surface of the above-mentioned rotating body is a planar structure. The first arc section 41 of the patrix in the present embodiment, the second arc section 42 of the patrix, the third arc section 43 of the patrix, the ...

Embodiment 2

[0055] The vulcanization molding die of a kind of special-shaped saturated nitrile rubber cloth cloth diaphragm of the present embodiment, its basic structure is the same as embodiment 1, the difference is: the arc of the bottom arc section 21 of the trapezoidal hole side in the mold 2 The radius is 4mm. A kind of manufacturing method of the special-shaped saturated nitrile rubber cloth diaphragm of the present embodiment, its basic preparation steps are the same as embodiment 1, the difference is: the thickness of the fabric cloth 82 in step 1 is 0.2mm; The body 81 and the material blank of the outer diaphragm body 83 are composed of the following components in parts by weight: saturated nitrile rubber: 100 parts, carbon black: 70 parts, light calcium carbonate: 15 parts, zinc oxide: 8 parts, Liquid nitrile rubber: 10 parts, accelerator CZ: 1.5 parts, accelerator TT: 1.5 parts, sulfur: 0.5 parts, vulcanizing agent double 25: 5 parts, accelerator TAC: 4 parts; vulcanization te...

Embodiment 3

[0057] The vulcanization molding die of a kind of special-shaped saturated nitrile rubber cloth cloth diaphragm of the present embodiment, its basic structure is the same as embodiment 1, the difference is: the arc of the bottom arc section 21 of the trapezoidal hole side in the mold 2 The radius is 5mm. A kind of manufacturing method of the special-shaped saturated nitrile rubber cloth diaphragm of the present embodiment, its basic preparation steps are the same as embodiment 1, the difference is: the thickness of step 1 fabric cloth 82 is 0.4mm; 81 and the blank of the outer diaphragm body 83 are composed of the following components in parts by weight: saturated nitrile rubber: 90 parts, carbon black: 50 parts, light calcium carbonate: 10 parts, zinc oxide: 5 parts, liquid Nitrile rubber: 5 parts, accelerator CZ: 0.5 parts, accelerator TT: 0.5 parts, sulfur: 0.3 parts, vulcanizing agent double 25: 2 parts, accelerator TAC: 1 part; vulcanization temperature control of vulcani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a vulcanization forming mold and manufacturing method of a specially-shaped saturated nitrile rubber laminated cloth diaphragm, and belongs to the technical field of rubber laminated cloth products. The vulcanization forming mold comprises an upper die of the mold, a middle die of the mold and a lower die of the mold, wherein a rotary body protruding outwards is arranged at the lower part of the upper die of the mold; a trapezoidal hole in a vertical direction is formed in the middle die of the mold; an arc section is formed on the bottom of the side surface of the trapezoidal hole; a round table body protruding outwards is arranged at the upper part of the lower die of the mold; the periphery of the round table body of the lower die of the mold is sleeved with the middle die of the mold; the middle die of the mold is in clearance fit with the lower die of the mold; a concave die cavity is formed inside the round table body; the structure of the die cavity is matched with the rotary body of the upper die of the mold. The manufacturing method comprises the following manufacturing steps: preparing sizing materials of fabric cloth and a diaphragm body; pressing the fabric laminated cloth by the middle die of the mold, and tightening the fabric laminated cloth; and vulcanization and forming. By adopting the vulcanization forming mold and the manufacturing method thereof, the problems of wrinkling of the specially-shaped saturated nitrile rubber laminated cloth diaphragm product and fracture of the laminated cloth are solved, and the qualified rate of the specially-shaped saturated nitrile rubber laminated cloth diaphragm is increased.

Description

[0001] The patent application of the present invention is a divisional application with the application number: 201310743444X. The filing date of the original application is: 2013 / 12 / 30. Manufacturing method. technical field [0002] The invention belongs to the technical field of rubber fabric products, and more specifically relates to a method for manufacturing a special-shaped saturated nitrile rubber fabric diaphragm. Background technique [0003] The rubber cloth diaphragm is a rubber seal used in automobile filters. This product must have excellent oil resistance and dynamic rebound performance at low temperature. After the product is assembled and pressed, it must have heat resistance and resistance. Fatigue bending 100,000 times to maintain permanent sealing performance. In the current industry, due to the limitation of domestic production technology, the production efficiency of special-shaped saturated nitrile rubber cloth diaphragm is low, the scrap rate is high,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/34
CPCB29C70/345
Inventor 徐海潮李斌何志刚李香周樱
Owner 南京金三力高分子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com