Inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and preparation method and application thereof

A pink, calendered technology, which is applied in the field of steam vulcanization calendered internal adhesive pink odorless shoe sole rubber and its preparation, can solve the problems of not meeting the needs of users, reducing the service life of rubber shoes, and increasing the smell of rubber, etc., to achieve Good process performance and mechanical properties, improved adhesion performance, low odor effect

Inactive Publication Date: 2015-12-09
JIHUA 3537 SHOE MAKING
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the shoemaking work, especially in the manufacturing process of rubber shoes with calendered soles, in order to realize the calendering and bonding function of rubber, a large amount of rubber softeners such as engine oil must be used in the formula, and softeners such as engine oil and rubber cannot meet the needs of shoe soles. Uniformity of adhesive performance and odor performance
On the one hand, in order to achieve rubber adhesion performance, it is necessary to increase the amount of softener oil, which will lead to an increase in rubber odor. In order to reduce the smell of rubber, it is necessary to reduce the amount of oil, which will cause poor rubber adhesion.
[0003] On the other hand, in order to achieve good adhesive performance and ensure the low-odour of the product, it must be at the expense of the wear resistance and tensile properties of the rubber shoes, which greatly reduces the service life of the rubber shoes and cannot meet the needs of users. need

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and preparation method and application thereof
  • Inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and preparation method and application thereof
  • Inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1 of the present invention: the pink tasteless shoe sole rubber glue of inter-steam vulcanization calendering type internal adhesive method, calculated by weight fraction, comprises 80 parts of standard rubber, 20 parts of butadiene rubber, 2 parts of sulfur, 0.2 part of peptizer DS- T-1, 2.4 parts of vulcanization accelerator, 3 parts of stearic acid, 3 parts of nano zinc oxide, 23 parts of spindle oil, 50 parts of white carbon black, 4.5 parts of polyethylene glycol, 10 parts kaolin , 2.5 parts of anti-aging agent, 4 parts of indene resin, 0.3 part of salicylic acid and 1.8 parts of pink coloring agent; described vulcanization accelerator is that every 2.4 parts of vulcanization accelerator is composed of 0.4 part of accelerator DM, 1.6 parts of accelerator DM and 0.4 parts of accelerator DS; the standard glue is 1# standard glue; the specification of polyethylene glycol is PEG-4000; the pink colorant is, every 1.8 parts of pink colorant is composed of 0.2 ...

Embodiment 2

[0034] Embodiment 2 of the present invention: inter-steam vulcanization calendering type internal adhesive pink odorless shoe sole rubber glue, calculated by weight fraction, including 75 parts of standard glue, 25 parts of butadiene rubber, 1.8 parts of sulfur, 0.15 part of peptizer DS- T-1, 2.6 parts of vulcanization accelerator, 2.5 parts of stearic acid, 3.5 parts of nano zinc oxide, 20 parts of spindle oil, 45 parts of white carbon black, 4.5 parts of polyethylene glycol, 15 parts kaolin , 1 part of anti-aging agent, 3 parts of indene resin, 0.4 part of salicylic acid and 1.5 parts of pink colorant; described vulcanization accelerator is, every 2.4 parts of vulcanization accelerator consists of 0.4 part of accelerator DM, 1.6 parts of accelerator DM and 0.4 parts of accelerator DS; the standard glue is 1# standard glue; the specification of polyethylene glycol is PEG-4000; the pink colorant is, every 1.8 parts of pink colorant is composed of 0.2 parts of red Masterbatch ...

Embodiment 3

[0036] Embodiment 3 of the present invention: inter-steam vulcanization calendering type internal adhesive pink odorless shoe sole rubber glue, calculated by weight fraction, includes 77 parts of standard glue, 23 parts of butadiene rubber, 2.2 parts of sulfur, 0.2 part of peptizer DS- T-1, 2.2 parts of vulcanization accelerator, 3.5 parts of stearic acid, 2.5 parts of nano zinc oxide, 25 parts of spindle oil, 47 parts of white carbon black, 4 parts of polyethylene glycol, 12 parts kaolin , 2 parts of anti-aging agent, 5 parts of indene resin, 0.2 part of salicylic acid and 2.2 parts of pink colorant; described vulcanization accelerator is, every 2.4 parts of vulcanization accelerator is made of 0.4 part of accelerator DM, 1.6 parts of accelerator DM and 0.4 parts of accelerator DS; the standard glue is 1# standard glue; the specification of polyethylene glycol is PEG-4000; the pink colorant is, every 1.8 parts of pink colorant is composed of 0.2 parts of red Masterbatch and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and a preparation method and application thereof. Sizing material formulas are optimized and screened, one formula with specific components and specific dosage is selected, accordingly, products have good process performance and mechanical performance, bonding performance is remarkably improved, and the prepared products are clear in stripe and good in color effect. The inter-steam vulcanization rolling type internal bonding type pink odorless sole rubber and the preparation method and application thereof are simple and feasible, low in cost and good in product use effect.

Description

technical field [0001] The invention relates to the field of rubber processing, in particular to a steam-vulcanized and calendered internal-adhesive pink odorless shoe sole rubber and a preparation method and application thereof. Background technique [0002] In the shoemaking work, especially in the manufacturing process of rubber shoes with calendered soles, in order to realize the calendering and bonding function of rubber, a large amount of rubber softeners such as engine oil must be used in the formula, and softeners such as engine oil and rubber cannot meet the needs of shoe soles. The uniformity of adhesive performance and odor performance. On the one hand, in order to achieve rubber adhesion performance, it is necessary to increase the amount of softener oil, which will lead to an increase in rubber odor. In order to reduce the smell of rubber, it is necessary to reduce the amount of oil, which will cause poor rubber adhesion. [0003] On the other hand, in order to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08L9/00C08L71/08C08L91/00C08K13/02C08K3/06C08K5/09C08K3/22C08K3/36C08K3/34
Inventor 杜江陈松雄周川泉晋齐怀石银平王春桥彭德彪安廷飞
Owner JIHUA 3537 SHOE MAKING