A kind of manufacturing process of sports shoe sole material
A production process and sole material technology, which is applied to soles, footwear, footwear, etc., can solve the problems of being unsuitable for large-scale popularization and use, the hardness is too large, and the sole material is easy to break, etc., and achieves strong supporting force, not easy to break, The effect of convenient production process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] A manufacturing process for a sports shoe sole material, comprising:
[0029] (1) Preparation of auxiliary materials: take fresh aloe vera leaves, cut them finely, crush them, soak in distilled water 15 times the weight of aloe vera for 1 hour, heat at 90°C, stir continuously, filter, and reserve the filtrate for later use, soak the filter residue twice again, and the amount of water used for each time is the amount of filter residue 8 times, heated to 90°C, filtered, combined 3 times and the filtrate was concentrated into a thick paste, after cooling, add 95% ethanol, stirred, and a large amount of flocculent precipitate was precipitated, left to stand for 2 hours, vacuum filtered to dryness, 80°C Blow drying under normal pressure for 4 hours to obtain a gel block, which was pulverized to a particle size of 50 μm with an ultrafine pulverizer to obtain aloe vera gel powder.
[0030] (2) Preparation of the inner plate of the bottom plate: heat the microporous polyurethan...
Embodiment 2
[0034] A manufacturing process for a sports shoe sole material, comprising:
[0035] (1) Preparation of auxiliary materials: Take fresh aloe vera leaves, chop finely, crush them, soak in distilled water 20 times the weight of aloe vera for 2 hours, heat at 95°C, stir continuously, filter, use the filtrate for later use, and soak the filter residue twice again, and the amount of water used for each time is the amount of filter residue 10 times of that, heated at 95°C, filtered, combined 3 times and the filtrate was concentrated into a thick paste, after cooling, add 95% ethanol, stirred, a large amount of flocculent precipitate was precipitated, stood for 3 hours, vacuum filtered to dryness, 90°C Blast drying under normal pressure for 6 hours to obtain a gel block, which was crushed to a particle size of 100 μm with an ultrafine pulverizer to obtain aloe vera gel powder.
[0036] (2) Preparation of the inner plate of the bottom plate: heat the microporous polyurethane elastomer...
Embodiment 3
[0040] A manufacturing process for a sports shoe sole material, comprising:
[0041] (1) Preparation of auxiliary materials: Take fresh aloe vera leaves, cut them finely, crush them, soak in distilled water 17.5 times the weight of aloe vera for 1.5 hours, heat at 92.5°C, stir continuously, filter, reserve the filtrate, and soak the filter residue twice, each time the water consumption is the filter residue 9 times the amount, heated at 92.5°C, filtered, combined for 3 times and the filtrate was concentrated into a thick paste, after cooling, add 95% ethanol, stirred, a large amount of flocculent precipitate was precipitated, stood for 2.5 hours, vacuum filtered to dryness, 85 Under normal pressure at ℃ and air-drying for 5 hours, the rubber block was obtained, which was crushed to a particle size of 75 μm with an ultrafine pulverizer to obtain aloe vera gel powder.
[0042] (2) Preparation of the inner plate of the bottom plate: heat the microporous polyurethane elastomer to ...