Preparation process for double-faced plastic coated waterproof cloth

A preparation process and technology of waterproof cloth, which can be used in textiles and paper making, etc., can solve the problem of low overall effect of waterproof cloth, and achieve the effect of good waterproof performance.

Inactive Publication Date: 2016-01-06
陈跃跃
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that the overall effect of the existing waterproof cloth is low, the present invention provides a preparation process for double-sided plastic-coated waterproof cloth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation process for double-sided plastic-coated waterproof cloth, the preparation process steps are:

[0016] (1) Ingredients: mix 65% PVC paste resin, 10% calcium powder, 6% titanium dioxide, 6% carbon black slurry, and 13% purified water by weight percentage;

[0017] (2) Grinding: put the raw materials prepared in step (1) into the grinder for 10-12 minutes, and ensure the raw material temperature is 40-50°C for the first 10 minutes, and ensure the raw material temperature is 60-70°C for the rest of the time;

[0018] (3) Immersion coating: apply the ground raw materials evenly on the front and back of the linen cloth woven from flax and glass fiber, the density of the front is 13-15g / cm 3 , the density of the opposite side is 5-6g / cm 3 ;

[0019] (4) Drying: Put the linen into the drying oven and dry it at a temperature of 27-35°C;

[0020] (5) High-temperature plasticization: put the linen cloth dried in the above step (4) into an oven and undergo surface ...

Embodiment 2

[0023] A preparation process for double-sided plastic-coated waterproof cloth, the preparation process steps are:

[0024] (1) Ingredients: mix 72% PVC paste resin, 8% calcium powder, 5% titanium dioxide, 5% carbon black slurry, and 10% pure water by weight percentage;

[0025] (2) Grinding: put the raw materials prepared in step (1) into the grinder for 12-14 minutes, and keep the temperature of the raw materials at 30-45°C for the first 10 minutes, and keep the temperature of the raw materials at 50-60°C for the rest of the time;

[0026] (3) Immersion coating: evenly apply the ground raw materials to the front and back of the linen cloth woven from flax and glass fiber, the density of the front is 10-13g / cm 3 , the density of the opposite side is 4-5g / cm 3 ;

[0027] (4) Drying: Put the linen into the drying oven and dry it at a temperature of 24-34°C;

[0028] (5) High-temperature plasticization: put the linen cloth dried in the above step (4) into an oven and undergo s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation process for double-faced plastic coated waterproof cloth. The preparation process comprises the steps of compounding, grinding, dip coating, drying, high-temperature plasticizing and inspecting; a layer of waterproof coating covers base cloth through different recipes to achieve the goal of water resistance; the waterproof cloth produced by the preparation process disclosed by the invention has good waterproofness, and can be suitable for various occasions.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a preparation process of a waterproof cloth. Background technique [0002] Traditional tarpaulins basically use short fibers such as cotton and chemical fibers as raw materials, and produce canvas through spinning and weaving to make tarpaulins. Therefore, the products are bulky and rough with low strength. The waterproof function of canvas is mainly realized by the density of the fabric. Relying on fabric density to improve the waterproof performance of canvas obviously has inherent shortcomings. Even if the fabric density is tighter, water will still infiltrate the fabric over time. When the water content in the fabric fibers reaches saturation, water seepage will appear. With the development of science and technology, silicone coating has appeared in China to improve the waterproof ability of canvas, but silicone coating also has defects: first, its stability is poor, it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/06D06N3/00
Inventor 陈跃跃
Owner 陈跃跃
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com