Continuous pickling method for hot-rolled dual-phase steel
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A hot-rolled dual-phase steel and pickling technology, which is applied in the field of metallurgy, can solve the problems of complex production control, numerous procedures, and high costs, and achieve the effects of simple and easy process steps, high pickling efficiency, and improved yield strength
Active Publication Date: 2018-01-26
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF7 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The pickling methods described in the above patents are all mixed acid pickling, which has the disadvantages of high cost, heavy pollution, numerous procedures, and complicated production control.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] Continuous pickling of embodiment 1C-Si-Mn-Cr series hot-rolled dual-phase steel DP600 strip
[0031] The 1650 turbulent flow continuous pickling unit is used for continuous pickling of C-Si-Mn-Cr hot-rolled dual-phase steel DP600 strip. The nominal thickness of the strip raw material is 4.0mm, the nominal width is 1290mm, and the length is 630m.
[0032] The production process is: uncoiling of hot-rolled raw materials→laser welding→phosphorus breaking by tension leveling unit→turbulent pickling→rinsing→on-line leveling→edge trimming→on-line oiling→bundling→packing and storage.
[0033] After the head and tail of the front and rear coils are welded by a plasma welding machine (can be welded between different steel bells), the phosphorus is broken by the breaking and leveling unit, and the elongation of the tension and leveling is 1.5%, and then pickled in an acid tank. 1 # ,2 # 、3 # The temperature of the acid solution in the acid tank is 60°C, 55°C, 55°C, 1 # Acid ...
Embodiment 2
[0035] Continuous pickling of embodiment 2C-Si-Mn-Cr series hot-rolled dual-phase steel DP600 strip
[0036] The 1650 turbulent flow continuous pickling unit is used for continuous pickling of C-Si-Mn-Cr hot-rolled dual-phase steel DP600 strip. The nominal thickness of the strip raw material is 4.0mm, the nominal width is 1290mm, and the length is 650m.
[0037] The production process is: uncoiling of hot-rolled raw materials→laser welding→phosphorus breaking by tension leveling unit→turbulent pickling→rinsing→on-line leveling→edge trimming→on-line oiling→bundling→packing and storage.
[0038] After the head and tail of the front and rear coils are welded by a plasma welding machine (can be welded between different steel bells), the phosphorus is broken by the breaking and leveling unit, and the elongation of the tension and leveling is 1.5%, and then pickled in an acid tank. 1 # ,2 # 、3 # The temperature of the acid solution in the acid tank is 85°C, 85°C, 75°C, 1 # Acid ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a pickling method for hot-rolled dual-phase steel and belongs to the field of metallurgy. The invention provides a continuous pickling method for hot-rolled dual-phase steel. The steps include: uncoiling of hot-rolled raw materials, laser welding, phosphorus breaking in a tension and straightening unit, turbulent flow pickling, rinsing and online leveling, wherein turbulent flow pickling Single-acid environment pickling is used in the process. The pickling temperature is 55-85°C. Pickling is carried out in at least three stages, and the pickling conditions of each stage are controlled as follows: During the first pickling process, the Fe2+ concentration in the pickling tank is ≤ 150g / l, the concentration of the single acid is 50~120g / l; during the second pickling process, the Fe2+ concentration in the pickling tank is ≤120g / l, and the concentration of the single acid is 60~160g / l; third During the pickling process, the Fe2+ concentration in the pickling tank is ≤80g / l, and the concentration of the single acid is 80-200g / l. The process steps are simple and easy to implement, the acid liquid can be recycled and regenerated, and has certain environmental protection. It also has the characteristics of continuous large-scale production, high pickling efficiency, and low pickling cost.
Description
technical field [0001] The invention relates to a pickling method for hot-rolled dual-phase steel, belonging to the field of metallurgy. Background technique [0002] The hot-rolled pickled sheet is made of high-quality hot-rolled sheet as raw material. The oxide layer is removed, trimmed and finished by the pickling unit. treatment) → turbulent pickling → rinsing → online leveling → trimming → online oiling → bundling → packaging and storage, the surface quality and use requirements are between hot-rolled sheets and cold-rolled sheets, which are partially hot-rolled sheets An ideal substitute for steel plates and cold-rolled plates. [0003] The dual phase steel (Dual Phase Steel, referred to as DP steel) structure is composed of ferrite (F) + martensite (M) or bainite. At present, the common hot-rolled dual phase steel strip C-Si-Mn- Cr system, C-Si-Mn-Cr-Mo system, C-Si-Mn-Mo system, C-Mn-Cr system, C-Mn-Si system and C-Si-Mn system, etc., which have excellent mechanica...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more