Superfine fiber glasses pocket

A technology of ultra-fine fiber and glasses bag, applied in fiber processing, textiles and papermaking, etc., can solve the problems of antibacterial performance and washability to be improved, and achieve the effect of excellent antifouling performance and strong washability

Inactive Publication Date: 2016-02-03
JIANGSU TAILIN TEXTILE CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The antifouling performance, antibacterial performance and washability of existing fabrics need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of microfiber glasses bag, it is processed through finishing process, and this finishing process comprises the following steps:

[0021] 1) Put 1-2 parts by mass of modified triazine-5, 1.2 parts by mass of borneol, and 0.6 parts by mass of polyoxyethylene sorbitan fatty acid ester into 12.3 parts by mass of deionized water, and stir evenly;

[0022] 2) Then add 1.2 parts by mass of alkanolamide polyoxyethylene ether and 1.1 parts by mass of dibutyl tetramethylammonium bromide in sequence, and continue to stir until fully mixed to obtain a finishing solution;

[0023] 3) Pad the cloth in the finishing solution and dry it at constant temperature.

Embodiment 2

[0025] The microfiber glasses bag is processed through a finishing process, and the finishing process includes the following steps:

[0026] 1) Put 1 part by mass of modified triazine-5, 1.2 parts by mass of borneol, and 0.6 part by mass of polyoxyethylene sorbitan fatty acid ester into 12.3 parts by mass of deionized water, and stir evenly;

[0027] 2) Then add 1.2 parts by mass of alkanolamide polyoxyethylene ether and 1.1 parts by mass of dibutyl tetramethylammonium bromide in sequence, and continue to stir until fully mixed to obtain a finishing solution;

[0028] 3) Pad the cloth in the finishing solution and dry it at constant temperature.

Embodiment 3

[0030] The microfiber glasses bag is processed through a finishing process, and the finishing process includes the following steps:

[0031] 1) Put 2 parts by mass of modified triazine-5, 1.2 parts by mass of borneol, and 0.6 parts by mass of polyoxyethylene sorbitan fatty acid ester into 12.3 parts by mass of deionized water, and stir evenly;

[0032] 2) Then add 1.2 parts by mass of alkanolamide polyoxyethylene ether and 1.1 parts by mass of dibutyl tetramethylammonium bromide in sequence, and continue to stir until fully mixed to obtain a finishing solution;

[0033] 3) Pad the cloth in the finishing solution and dry it at constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a superfine fiber glasses pocket treated by a finishing process. The finishing process comprises the following steps: 1) putting 1 to 2 parts by mass of modified triazine-5, 1.2 parts by mass of borneol, 0.6 parts by mass of polyoxyethylene sorbitan aliphatic ester into 12.3 parts by mass of deionized water, and stirring evenly; 2) adding 1.2 parts by mass of alkylolamide poly(oxy ethane ether) and 1.1 parts by mass of dibutyl ester tetramethyl ammonium bromide in sequence, and continuously stirring, until a mixture is mixed thoroughly to be even, thus preparing finishing liquid; 3) padding cloth in the finishing liquid, and drying at constant temperature. The superfine fiber glasses pocket has excellent antifouling property, antibacterial property and strong washability.

Description

technical field [0001] The invention relates to a superfine fiber eyeglass bag. Background technique [0002] The antifouling performance, antibacterial performance and washability of existing fabrics all need to be improved. Contents of the invention [0003] The object of the present invention is to provide a microfiber eyeglass bag, which has excellent antifouling performance, antibacterial performance, and strong washability. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of microfiber glasses bag, which is processed through a finishing process, and the finishing process includes the following steps: [0005] 1) Put 1-2 parts by mass of modified triazine-5, 1.2 parts by mass of borneol, and 0.6 parts by mass of polyoxyethylene sorbitan fatty acid ester into 12.3 parts by mass of deionized water, and stir evenly; [0006] 2) Then add 1.2 parts by mass of alkanolamide polyoxyethylene ether and 1.1 part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/144D06M15/53D06M13/358D06M13/463
Inventor 龚雪芳
Owner JIANGSU TAILIN TEXTILE CO LTD