Elastic TPU (Thermoplastic Polyurethane) polishing composite membrane

A composite film and elastic technology, applied in the direction of adhesive types, polyurea/polyurethane adhesives, coatings, etc., can solve problems such as difficult to apply irregular shapes or curved products, and achieve good anti-clogging and lubrication functions, Wide application range and good cold resistance

Inactive Publication Date: 2016-02-10
DONGGUAN GOLDEN SUN ABRASIVES
View PDF10 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For some products that require high surface precision, they must undergo corresponding polishing and grinding processes; however, in the actual polishing and grinding process, the existing traditional coated abrasives are difficult to apply to irregular or curved surfaces Products (such as electronic products in the 3C industry)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Elastic TPU (Thermoplastic Polyurethane) polishing composite membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention will be described below in conjunction with specific embodiments.

[0018] Such as figure 1 As shown, a kind of elastic TPU polishing composite film comprises a TPU film layer 1 and an abrasive layer 2 arranged in layers, the lower surface of the abrasive layer 2 is adhered to the upper surface of the TPU film layer 1 by a modified adhesive, and the abrasive layer The upper surface of 2 is evenly coated with a lubricating antistatic coating 3 .

[0019] Further, the modified adhesive is composed of polyurethane resin, curing agent and leveling agent, wherein the weight ratio of polyurethane resin, curing agent and leveling agent is 100:10-20:0.5-1.5.

[0020] Furthermore, the lubricating antistatic coating 3 is composed of three materials: paraffin lubricating solution, film forming agent and antistatic agent, wherein the weight ratio of paraffin lubricating solution, film forming agent and antistatic agent is 100:8 -12:5-8.

[0021] Preferably,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an elastic TPU (Thermoplastic Polyurethane) polishing composite membrane. The elastic TPU polishing composite membrane comprises a TPU adhesive membrane layer and a grinding material layer, wherein the lower surface of the grinding material layer is stuck on the upper surface of the TPU adhesive membrane layer through a modified adhesive; a lubricating antistatic coating is uniformly coated on the upper surface of the grinding material layer; the modified adhesive is prepared from three materials including polyurethane resin, a curing agent and a flatting agent at the weight ratio of 100 : (10 to 20) : (0.5 to 1.5); the lubricating antistatic coating is prepared from three materials including a lubricating solution paraffin, a film forming agent and an antistatic agent at the weight ratio of 100 : (8 to 12) : (5 to 8). The grinding material layer composed of a polishing and grinding material is compounded on the TPU adhesive membrane layer so that the properties of the grinding material layer and the TPU adhesive membrane layer are effectively combined; the lubricating antistatic coating has good anti-blocking and lubricating functions so that the service life can be prolonged, the surface quality of polishing is improved and scratches are reduced. Therefore, the elastic TPU polishing composite membrane has the advantages of novel design, stable and reliable structure and wide applicable range.

Description

technical field [0001] The invention relates to the technical field of polishing and grinding, in particular to an elastic TPU polishing composite film. Background technique [0002] For some products that require high surface precision, they must undergo corresponding polishing and grinding processes; however, in the actual polishing and grinding process, the existing traditional coated abrasives are difficult to apply to irregular or curved surfaces Products (such as electronic products in the 3C industry). Contents of the invention [0003] The object of the present invention is to provide an elastic TPU polishing composite film for the deficiencies of the prior art, which has novel design, stable and reliable structure and wide application range. [0004] In order to achieve the above object, the present invention is achieved through the following technical solutions. [0005] An elastic TPU polishing composite film, including a layered TPU film layer and an abrasive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24D11/00C09J175/04C09D7/12
Inventor 方红农忠超
Owner DONGGUAN GOLDEN SUN ABRASIVES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap