Water-based super-fogging super-blackening treating agent for synthetic leather and preparation method thereof

A technology of special fog, special black and synthetic leather, which is applied in fiber treatment, textiles and papermaking, etc., to achieve the effects of good compatibility, wide application range and excellent mechanical properties

Inactive Publication Date: 2016-02-10
JIANGSU BAOZE POLYMER MATERIAL
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing surface treatment agents can no longer meet the increasing requirements of consumers for the brightness and handle of synthetic leather. Therefore, there is an urgent need for a synthetic leather that can not only improve the touch of synthetic leather, but also improve the comprehensive effects of synthetic leather such as handle, brightness, and gloss. treatment agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based super-fogging super-blackening treating agent for synthetic leather and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The water-based special fog special black treatment agent for synthetic leather is composed of the following components: 26 parts by weight of water-based resin, 0.2 parts by weight of water-based dispersant, 0.2 parts by weight of defoamer, 4 parts by weight of silica matting powder, wetting 0.2 parts by weight of agent, 1 part by weight of Deqian thickener, and 55 parts by weight of water.

[0026] The preparation method of the above-mentioned water-based special black treatment agent for synthetic leather is: under normal temperature and pressure, 26 parts by weight of water-based resin, 0.2 parts by weight of water-based dispersant, 0.2 parts by weight of defoamer, 4 parts by weight of Silica matting powder, 0.2 parts by weight of wetting agent, 1 part by weight of Deqian thickener, and 55 parts by weight of water are mixed, stirred for at least 30 minutes until the mixture is evenly mixed, and the synthetic leather water-based Special fog special black treatment ag...

Embodiment 2

[0029] The water-based special fog special black treatment agent for synthetic leather is composed of the following components: 27 parts by weight of water-based resin, 0.4 parts by weight of water-based dispersant, 0.3 parts by weight of defoamer, 5 parts by weight of silica matting powder, wetting 0.4 parts by weight of agent, 1.5 parts by weight of Deqian thickener, and 56 parts by weight of water.

[0030] The preparation method of the above-mentioned water-based special black treatment agent for synthetic leather is: under normal temperature and pressure, 27 parts by weight of water-based resin, 0.4 parts by weight of water-based dispersant, 0.3 parts by weight of defoamer, 5 parts by weight of Silica matting powder, 0.4 parts by weight of wetting agent, 1.5 parts by weight of Deqian thickener, and 56 parts by weight of water are mixed, stirred for at least 30 minutes until the mixture is evenly mixed, and the synthetic leather is obtained. Special fog special black treat...

Embodiment 3

[0033] The water-based special fog special black treatment agent for synthetic leather is composed of the following components: 28 parts by weight of water-based resin, 0.5 parts by weight of water-based dispersant, 0.5 parts by weight of defoamer, 6 parts by weight of silica matting powder, wetting 0.5 parts by weight of agent, 1 part by weight of Deqian thickener, and 57 parts by weight of water.

[0034] The preparation method of the above-mentioned water-based special black treatment agent for synthetic leather is: under normal temperature and pressure, 28 parts by weight of water-based resin, 0.5 parts by weight of water-based dispersant, 0.5 parts by weight of defoamer, 6 parts by weight of Silica matting powder, 0.5 parts by weight of wetting agent, 1 part by weight of Deqian thickener, and 57 parts by weight of water are mixed, stirred for at least 30 minutes until the mixture is evenly mixed, and the synthetic leather is obtained. Special fog special black treatment a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water-based super-fogging super-blackening treating agent for synthetic leather, and the water-based super-fogging super-blackening treating agent is applied to a later period technology of the synthetic leather. The water-based super-fogging super-blackening treating agent is prepared from water-based resin, a water-based dispersing agent, a defoaming agent, silicon dioxide matting powder, a wetting agent, a Deuchem thickening agent and water. The invention further relates to a preparation method of the water-based super-fogging super-blackening treating agent for the synthetic leather. According to the water-based super-fogging super-blackening treating agent, all the components cooperate with one another and interact with one another, the synthetic leather is unique in handfeel after being treated, and the synthetic leather treated by the treating agent is natural in gloss, clear in color and luster, better in color developing and excellent in comprehensive effect, meanwhile, a prepared spraying dilute solution has the very good storage stability, and pigments are not prone to sedimentation. The water-based super-fogging super-blackening treating agent for the synthetic leather is a novel material in later period treatment and can be applied to an existing synthetic leather production line, the technology is simple, production equipment does not need to be changed, and the production cost cannot be increased.

Description

technical field [0001] The invention relates to the field of surface treatment agents for synthetic leather, in particular to a water-based special fog and special black treatment agent for synthetic leather used in the back-stage process of synthetic leather, and the invention also relates to the water-based special fog and special black treatment of the synthetic leather The preparation method of the agent. Background technique [0002] The synthetic leather surface treatment agent can be used for surface finishing according to the product category, which can improve the brightness, color and feel of synthetic leather. However, as consumers have higher and higher requirements for the color and feel of the leather surface, it is necessary not only to increase the touch of synthetic leather, but also to ensure the brightness and color of the surface of synthetic leather. However, the existing surface treatment agents can no longer meet the increasing requirements of consume...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M11/79
CPCD06M11/79D06M15/564
Inventor 陈勇刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap