High-weatherability aqueous wall coating and preparation method thereof

A water-based, weather-resistant technology, applied in the direction of reflection/signal coatings, coatings, etc., can solve problems such as poor weather resistance, and achieve the effect of improving ozone aging resistance and good ozone aging resistance

Active Publication Date: 2016-03-16
广东顺德石头彩涂料有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating mainly uses ultraviolet absorbers to improve the weather resistance of the coating. However, the weather resistance of architectural coatings depends on many factors, and UV aging resistance is only one of them. The resulting aging effect cannot be ignored either. The surface of the coating is not ideal in terms of ozone aging resistance and infrared reflection, so the overall weather resistance effect is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-weatherability aqueous wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] High weather-resistant water-based wall paint, in parts by weight, is made of the following components: 32 parts of pure acrylic emulsion, 20 parts of PEVE emulsion, 8 parts of CPVC, 6 parts of nano-titanium dioxide, 12 parts of mica powder, and 17 parts of deionized water , 0.2 part of non-ionic alkyl vinyl ether, 0.4 part of sodium tripolyphosphate, 2 parts of dodecyl alcohol ester, 0.2 part of alginate, 0.3 part of isothiazolinone derivative, 0.5 part of ethylene glycol, aluminum-doped oxidation 9 parts of zinc.

[0028] The steps of its preparation method are as follows:

[0029] (1) Put aluminum-doped zinc oxide in an oven, dry at 110°C for 2 hours, dissolve sodium polyacrylate in water, heat to 90°C and stir evenly to obtain a modified solution, add the dried aluminum-doped zinc oxide In the modified solution, adjust the pH value to 4.5 with acetic acid, react at a constant temperature of 90°C for 2 hours, filter the product with suction and wash it repeatedly wi...

Embodiment 2

[0033] High weather-resistant water-based wall paint, in parts by weight, is made of the following components: 30 parts of pure acrylic emulsion, 24 parts of PEVE emulsion, 9.5 parts of CPVC, 4.5 parts of nano-titanium dioxide, 14 parts of silicon micropowder, deionized water 20 parts, 0.3 parts of non-ionic alkyl vinyl ether, 0.3 parts of sodium tripolyphosphate, 2.2 parts of dodecyl alcohol ester, 0.4 parts of alginate, 0.2 parts of isothiazolinone derivatives, 0.6 parts of ethylene glycol, mixed Aluminum zinc oxide 11 parts.

[0034] The steps of its preparation method are as follows:

[0035] (1) Put aluminum-doped zinc oxide in an oven, dry at 110°C for 2 hours, dissolve sodium polyacrylate in water, heat to 90°C and stir evenly to obtain a modified solution, add the dried aluminum-doped zinc oxide In the modified solution, use acetic acid to adjust the pH value to 4.5, react at a constant temperature of 90°C for 2 hours, filter the product with suction and wash it repea...

Embodiment 3

[0039] High weather-resistant water-based wall paint, in parts by weight, is made of the following components: 35 parts of pure acrylic emulsion, 22 parts of PEVE emulsion, 10 parts of CPVC, 4 parts of nano-titanium dioxide, 11 parts of silicon micropowder, and 16 parts of deionized water , 0.4 part of non-ionic alkyl vinyl ether, 0.5 part of sodium tripolyphosphate, 2.4 parts of dodecyl alcohol ester, 0.6 part of alginate, 0.1 part of isothiazolinone derivative, 0.5 part of ethylene glycol, aluminum-doped oxidation Zinc 13 parts.

[0040] The steps of its preparation method are as follows:

[0041] (1) Put aluminum-doped zinc oxide in an oven, dry at 110°C for 2 hours, dissolve sodium polyacrylate in water, heat to 90°C and stir evenly to obtain a modified solution, add the dried aluminum-doped zinc oxide In the modified solution, adjust the pH value to 4.5 with acetic acid, react at a constant temperature of 90°C for 2 hours, filter the product with suction and wash it repe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-weatherability aqueous wall coating. The high-weatherability aqueous wall coating is prepared from, by weight, 30-38 parts of a pure acrylic emulsion, 18-24 parts of a PEVE emulsion, 8-10 parts of CPVC, 4-6 parts of a pigment, 10-16 parts of a filler, 15-21 parts of water, 0.2-0.4 parts of a wetting agent, 0.2-0.5 parts of a dispersant, 2-2.5 parts of a film forming assistant, 0.1-0.6 parts of a thickener, 0.1-0.3 parts of a mildew inhibitor, 0.5-0.6 parts of glycol and 9-14 parts of aluminum doped zinc oxide. The invention also provides a preparation method of the high-weatherability aqueous wall coating. The high-weatherability aqueous wall coating has the advantages of very good ozone ageing resistance, very good infrared reflection performance, and very good weatherability.

Description

Technical field: [0001] The invention relates to a wall paint, in particular to a high weather resistance water-based wall paint and a preparation method thereof. Background technique: [0002] Wall coating refers to the coating used for decoration and protection of building walls, making the building walls beautiful and tidy, and at the same time protecting the building walls and prolonging their service life. According to the classification of building walls, wall coatings include interior wall coatings and exterior wall coatings. Interior wall paint focuses on decoration and environmental protection, while exterior wall paint focuses on protection and durability. In addition to its own decorative and protective functions, wall paint is also developing towards a colorful, fashionable, healthy and environmentally friendly trend. People hope that the decorative effect will be radiant, beautiful, noble, elegant, romantic, and warm; they also hope that the material itself is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D127/12C09D127/24C09D5/33C09D7/12
CPCC08K2201/011C08L2205/02C08L2205/035C09D5/004C09D7/61C09D7/63C09D7/65C09D133/04C08L27/12C08L27/24C08L5/04C08K13/06C08K9/08C08K2003/2296C08K2003/2241C08K5/053
Inventor 谢永忠
Owner 广东顺德石头彩涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap