Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polymer emulsion architectural waterproof coating modified by emulsified asphalt and preparation method of coating

A technology of polymer emulsion and emulsified asphalt, used in asphalt coatings, coatings, etc., can solve the problems of poor high and low temperature resistance, weak acid and alkali corrosion resistance, and insufficient mechanical properties, and achieve acid and alkali corrosion resistance. Strong, high and low temperature resistance, good mechanical properties

Inactive Publication Date: 2016-03-23
WEIFANG HONGYUAN WATERPROOF MATERIAL
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing polymer emulsion waterproof coatings have the following defects: (1) The mechanical properties are not good enough; (2) The high and low temperature resistance is poor; (3) The waterproof effect is not good enough; (4) The acid and alkali corrosion resistance is not strong; (5) ) does not have self-healing properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer emulsion architectural waterproof coating modified by emulsified asphalt and preparation method of coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1 A kind of polymer emulsion architectural waterproof coating modified with emulsified asphalt and preparation method thereof

[0041] The raw material formula of emulsified asphalt modified polymer emulsion building waterproof coating is shown in Table 1;

[0042] Table 1 Raw material formula table

[0043] raw material

VAE emulsion

fungicide

Emulsifier

Dispersant

Defoamer

emulsified asphalt

Powder filler

water

thickener

parts by weight

25

0.3

0.4

0.3

0.4

25

45

10

0.8

[0044] The VAE emulsion described in table 1 is Celanese 1475 emulsion, and the solid content is 55.6%;

[0045] The bactericide described in table 1 is Dow BIT20;

[0046] The emulsifying agent described in table 1 is Dow's NP-10;

[0047] The dispersant described in table 1 is Dow 731A;

[0048] The defoamer described in Table 1 is polyether defoamer Dow Chemical UCONLB-1715;

[0049] The emul...

Embodiment 2

[0061] Embodiment 2 A kind of polymer emulsion architectural waterproof coating modified with emulsified asphalt and preparation method thereof

[0062]The raw material formula of emulsified asphalt modified polymer emulsion building waterproof coating is shown in Table 2;

[0063] Table 2 Raw material formula table

[0064] raw material

VAE emulsion

fungicide

Emulsifier

Dispersant

Defoamer

emulsified asphalt

Powder filler

water

parts by weight

35

0.3

0.4

0.3

0.4

25

50

8

[0065] The VAE emulsion described in table 2 is Celanese 1318 emulsion, and solid content is 55.8%;

[0066] The bactericide described in table 2 is Dow BIT20;

[0067] The emulsifying agent described in table 2 is Dow's NP-10;

[0068] The emulsifier described in table 2 is Dow 731A;

[0069] The defoamer described in Table 2 is polyether defoamer Dow Chemical UCONLB-1715;

[0070] The emulsified asphalt described in ...

Embodiment 3

[0080] Embodiment 3 A kind of polymer emulsion architectural waterproof coating modified with emulsified asphalt and preparation method thereof

[0081] The raw material formula of emulsified asphalt modified polymer emulsion building waterproof coating is shown in Table 3;

[0082] Table 3 raw material formula table

[0083] raw material

Styrene acrylic emulsion

fungicide

Emulsifier

Dispersant

Defoamer

emulsified asphalt

Powder filler

water

thickener

parts by weight

25

0.3

0.4

0.3

0.4

25

50

12

0.8

[0084] The styrene-acrylic emulsion described in table 3 is BASF GS409 emulsion, and solid content is 50%;

[0085] The bactericide described in table 3 is Dow BIT20;

[0086] The emulsifying agent described in table 3 is Dow's NP-10;

[0087] The emulsifier described in table 3 is Dow 731A;

[0088] The antifoaming agent described in table 3 is BASF antifoaming agent NXZ and A10 by 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides polymer emulsion architectural waterproof coating modified by emulsified asphalt. The polymer emulsion architectural waterproof coating is characterized by being prepared from the following raw materials in parts by weight: 20 to 45 parts of polymer emulsion, 0.2 to 0.5 part of dispersing agent, 0.2 to 0.5 part of emulsifying agent, 0.3 to 0.6 part of defoaming agent, 0.2 to 0.4 part of sterilizing agent, 10 to 35 parts of the emulsified asphalt, 30 to 52 parts of powdery fillers and 7 to 15 parts of water. The polymer emulsion architectural waterproof coating disclosed by the invention has the advantages of good mechanical performance, good weather resistance, strong waterproof ability and acid-base corrosion resistance.

Description

technical field [0001] The invention relates to a building waterproof coating, in particular to a polymer emulsion building waterproof coating modified with emulsified asphalt and a preparation method thereof, belonging to the field of building waterproof coatings. Background technique [0002] There are two types of waterproof materials on the market: one is polyurethane waterproof coatings. Such materials are generally made of polyurethane and coal tar as raw materials. The tar gas it volatilizes is highly toxic and not easy to remove, so it was banned in China in 2000. The polyurethane waterproof coating that is still on sale uses asphalt instead of coal tar as a raw material. However, when using this kind of paint, it is generally diluted with organic solvents such as toluene and xylene, so it also contains toxicity. [0003] Another type is polymer cement-based waterproof coating. It is composed of a variety of water-based polymer emulsions and high-quality cement m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D131/04C09D195/00C09D125/14C09D7/12
CPCC09D131/04C08L2201/08C08L2205/03C08L2205/035C09D7/61C09D125/14C09D195/00C08L95/00C08L1/02C08L71/00C08K2003/265C08L31/04C08L33/00C08L25/14
Inventor 张冬冬胡希宝刘晓东李超侯江超
Owner WEIFANG HONGYUAN WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More