Paste mixing and curing technology for paste-squeezing production of tubular positive plate

A curing process and positive plate technology, used in electrode manufacturing, lead-acid battery electrodes, etc., can solve the problems of workers’ working environment and labor intensity, low battery life, environmental pollution, etc. Eliminate the effect of high pollution

Active Publication Date: 2016-03-23
东阳市琰安建筑工程有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the lead paste on the positive plate in the existing battery production is easy to crack, the scrap rate is high, and the life of the battery is l...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paste mixing and curing technology for paste-squeezing production of tubular positive plate
  • Paste mixing and curing technology for paste-squeezing production of tubular positive plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] A paste-squeezing production tube-type positive electrode plate and paste and curing process. This process is suitable for all tube-type positive electrode plate extrusion-type production, and is characterized by:

[0015] 5) Additives: graphite 0.2-0.5%, 0.8-1.2mm long and short fibers 0.6-0.8%, silica sol 1-5%, calcium sulfate 0.25-0.5%, nano-level tetrabasic lead sulfate 0.2-0.4%.

[0016] 6) Lead powder adopts oxidation degree 72~80% and apparent specific gravity 1.2~1.3g / cm 3 Lead powder, sulfuric acid adopts a dilute sulfuric acid solution with a content of 20-25%,

[0017] 7) Ingredients pre-mixing: Pre-mix the formula amount of graphite, long and short fibers, calcium sulfate, nano-level tetrabasic lead sulfate, and 3 to 5% lead powder for 30 minutes;

[0018] 8) Preparation method: First, add the premixed additives in the paste machine, and then add the remaining lead powder. During the process of adding the lead powder, add the lead powder, add water, and stir. The amo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a paste mixing and curing technology for paste-squeezing production of a tubular positive plate. The technology is applicable to paste-squeezing production of all tube positive plates. The paste mixing and curing technology is characterized by comprising the following steps: with an additive, lead powder of which the oxidizability is 72%-80% and the apparent specific gravity is 1.2g/cm<3> to 1.3g/cm<3>, and a dilute sulfuric acid solution with the sulfuric acid content of 20%-25% as ingredients, premixing the ingredients; and stirring graphite, long and short fibers, calcium sulfate, nanoscale tetrabasic lead sulfate and 3%-5% of lead powder at a formula ratio for 30 minutes, and premixing, mixing and curing the mixture. The paste mixing and curing technology has the advantages that the problem of cracking of lead plaster in a production process is avoided; the lifetime of a storage battery is prolonged; a reliable guarantee is provided; compared with other technologies, the technonoly makes the capacity improved by over 15%; the lifetime is prolonged by 20%; dust in the conventional paste mixing technology is completely eradicated; and the paste mixing and curing technology is a novel environment-friendly production technology.

Description

Technical field [0001] The invention belongs to the technical field of accumulators, and specifically is a process for producing tubular positive plates and pastes in paste extrusion and curing. Background technique [0002] At present, the lead paste on the positive plate in the current battery production is easy to crack, the rejection rate is high, and the battery life is relatively low; the dust in the past and the paste process is very large, the environmental pollution is serious, and the working environment and labor intensity of the workers are high. . Summary of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the prior art, and provide a paste extrusion type production tubular positive plate and paste with simple process, high production efficiency, long service life, high yield, and pollution-free production environment. Curing process. [0004] In order to achieve the above-mentioned purpose of the invention, the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/20H01M4/04
CPCH01M4/04H01M4/20Y02E60/10
Inventor 程艳青
Owner 东阳市琰安建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap