Preparation method of carbon fiber composite material plate and its self-piercing riveting mold and method with aluminum alloy plate

A technology for composite material plates and aluminum alloy plates, which is applied in the field of self-piercing riveting molds and the preparation of carbon fiber composite material plates, can solve problems such as the inability to form riveted joints, reduce the quality of riveted joints, and brittle damage to material plates, so as to avoid matrix cracking and fiber breakage, superior shear resistance, and the effect of avoiding brittle failure

Inactive Publication Date: 2017-09-26
JILIN UNIV
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention designs and develops the preparation method of the carbon fiber composite material plate, the purpose is to solve the problem in the prior art that the material plate is prone to brittle failure when the carbon fiber composite material plate is punched again
[0007] The present invention also designs and develops a self-piercing riveting die and method for a carbon fiber composite material plate and an aluminum alloy plate. Joint quality, even the inability to form effective riveted joints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbon fiber composite material plate and its self-piercing riveting mold and method with aluminum alloy plate
  • Preparation method of carbon fiber composite material plate and its self-piercing riveting mold and method with aluminum alloy plate
  • Preparation method of carbon fiber composite material plate and its self-piercing riveting mold and method with aluminum alloy plate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0069] Fabrication process of carbon fiber composite panels with through holes:

[0070] 1. After the carbon fiber cloth prepreg process is completed, the carbon fiber composite material prepreg cloth is cut, and the prepreg cloth is placed into the groove in the lower die 120. During the laying process, the woven carbon fiber composite material prepreg cloth is The weaving pores of the lower die 120 pass through the beam of light, and ensure that the carbon fiber composite material prepreg is completely paved in the groove, and there is no gap between the bottom surface of the groove and the carbon fiber composite material prepreg;

[0071] 2. Assemble the upper punch 110 and the lower die 120 together, and heat the combined mold consisting of the upper punch 110 and the lower punch 120 together to perform prepreg gelation. Taking novolac epoxy vinyl resin as an example, raise the mold clamping temperature to 100°C-110°C to complete the gelation process of the resin;

[0072...

Embodiment

[0138] Apply the method for preparing a carbon fiber composite material plate with a through hole according to the present invention to prepare a central through hole with a diameter of 8mm, and the overall size of the carbon fiber composite material plate is 200mm×80mm×2mm. The base material of the prepared carbon fiber composite board is phenolic epoxy vinyl resin, and the reinforcement material is 3k carbon fiber filament.

[0139] The steps of the self-piercing riveting method between the aluminum alloy plate and the carbon fiber composite plate comprising the preparation process of the carbon fiber composite material plate with through holes described in the present invention are as follows:

[0140] 1. Take an aluminum alloy plate 160 with a thickness of 2mm;

[0141] 2. Prepare a carbon fiber composite material plate 150 with a through hole with a diameter of 8 mm. Cut the prepreg cloth into 8 cuboids with a size of 200 mm × 80 mm, and spread the cut carbon fiber prepr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a self-piercing riveting die for a carbon fiber composite material plate and an aluminum alloy plate, comprising: a rivet, which is used for riveting a carbon fiber composite material plate and an aluminum alloy plate; Reciprocating motion; the main body of the concave mold, the concave mold cavity in the center is set concentrically with the punch, the side wall of the concave mold cavity is a light hole cylindrical side wall, and the center is a conical boss, and the light hole and the cone boss are matched with riveting , the punch and the main body of the die are connected with sensors, and the height adjustment coefficient, speed adjustment coefficient and timing adjustment coefficient of the punch are obtained through data collection. The invention also discloses a preparation method of the carbon fiber composite material plate and a self-piercing riveting method of the carbon fiber composite material plate and the aluminum alloy plate. The invention has the characteristics of being able to withstand relatively large impact force, simple process steps, low cost, and superior tensile, shearing and fatigue resistance performances of riveted joints.

Description

technical field [0001] The invention relates to the field of riveting of a carbon fiber composite material plate and an aluminum alloy plate, in particular to a preparation method of a carbon fiber composite material plate and a self-piercing riveting mold and method for the carbon fiber composite material plate and an aluminum alloy plate. Background technique [0002] With the rapid development of science and technology, carbon fiber composite materials have high mechanical properties, so that carbon fiber composite materials have been widely used in aviation, ships, automobiles and other fields. In the automotive industry, the application proportion of carbon fiber composite materials is also increasing year by year. As a high-performance composite material, it is being widely recognized, and its transformation from high-end models to mid-range models is being realized rapidly. Carbon fiber composite materials have good impact resistance and energy absorption, good fatigu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/34B29C70/54B21J15/02B21J15/10B21J15/28
CPCB21J15/025B21J15/147
Inventor 庄蔚敏敖文宏刘西洋徐纪栓杨冠男解东旋李冰娇胡哲张凯希郭帅闫雪燕李晓鹏
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products