A kind of preparation method of antibacterial and deodorizing polypropylene fiber

A polyethylene wax and polymer technology, applied in the direction of single-component polyolefin artificial filament, etc., can solve the problems of chemical reaction, complicated operation, high cost, etc., and achieve the effect of simple reaction operation, low product cost and low toxicity

Inactive Publication Date: 2017-10-24
DONGHUA UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN 102675625 introduces a method for preparing an environmentally friendly water-soluble phthalocyanine containing PEG side chains, but this method still requires chemical reactions and multiple purifications
The above methods still belong to the category of chemical modification. Although they help to improve the dispersion of phthalocyanine in the polymer matrix, there are still problems such as complicated operation and high cost.
[0004] At present, there are no reports or patents that can uniformly disperse phthalocyanine in the polypropylene matrix by physical modification.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of antibacterial and deodorizing polypropylene fiber
  • A kind of preparation method of antibacterial and deodorizing polypropylene fiber
  • A kind of preparation method of antibacterial and deodorizing polypropylene fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Dissolve 0.10g of iron octacarboxyphthalocyanine in a small amount of water, add 10g of PEG 400, stir evenly, place in a blast oven at 70°C for 12 hours, dry the solvent, take 1g of the mixture and add it to 100g of polypropylene slices and mix evenly. The melting point of the slices is 160°C, and the modified polypropylene slices are added to the double-cone micro-kneader, the melt-blending temperature is 200°C, the screw diameter is (Φ4-Φ12mm), the twin-screw speed is 80r / min, and the extruded wire Finally, the winding speed was 50 m / min to prepare polypropylene fibers.

Embodiment 2

[0024] Dissolve 1g copper octacarboxyphthalocyanine in a small amount of water, add 9g PEG 2000, stir evenly, place in a blast oven at 70°C for 12 hours, dry the solvent, take 1g and add it to 9g polypropylene and mix evenly, add it to the double cone micro mixer In the refiner, the melt blending temperature is 200°C, the screw diameter is (Φ4-Φ12mm), the twin-screw speed is 80r / min, and after extrusion, the winding speed is 50m / min to prepare polypropylene fibers.

Embodiment 3

[0026] Dissolve 1g of zinc octacarboxyphthalocyanine in a small amount of ethanol, add 4g of PPG 4000 and stir evenly, place it in a blast oven at 70°C for 12 hours, dry the solvent, take 1g and add it to 4g of polypropylene and mix evenly, add it to the double cone micro mixer In the refiner, the melt blending temperature is 200°C, the screw diameter is (Φ4-Φ12mm), the twin-screw rotation speed is 80r / min, and the winding speed is 50m / min to prepare polypropylene fibers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of antibiosis and deodorization polypropylene fibers. The method comprises the following steps: dissolving metal octocarboxyphthalocyanine in a small amount of a solvent, adding the obtained solution to a polymer matrix, stirring the obtained solution until uniformity, removing the solvent, and fully drying the obtained material to obtain a metal octocarboxyphthalocyanine uniformly-dispersed polymer matrix mixture represented by general formula 1; and adding the mixture to polypropylene slices according to a certain ratio to prepare the polypropylene fibers with different proportions of the mixture. The problem of unable application of phthalocyanine in the fiber and fabric modification field due to agglomeration blocking after solvent volatilization is solved in the invention. Compared with phthalocyanine chemical modification methods, the method disclosed in the invention has the advantages of simple operation, short time, no need of a catalyst, environmental protection, safety and energy saving. The polypropylene fibers prepared in the invention have the advantages of stable phthalocyanine adhesion, good fatigue resistance, and substantial antibiosis and deodorization effects.

Description

technical field [0001] The invention belongs to the field of preparation of antibacterial and deodorant fibers and fabrics, in particular to a preparation method of antibacterial and deodorant polypropylene fibers. Background technique [0002] With the improvement of people's living standards and the continuous improvement of the quality of life, people's requirements for environmental quality are also getting higher and higher. In recent years, environmental pollution has become more and more serious, and air purification devices have become more and more important to people's lives, and polypropylene non-woven fabrics, fibers and fabrics are the best choices for air purification materials and filter materials. At present, the purification material is mainly attached to activated carbon to absorb odor by physical methods, which cannot fundamentally eliminate odor. Therefore, chemical methods to eliminate odor are becoming more and more important. [0003] Phthalocyanine i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L71/02C08L23/06C08K5/3467D01F6/46D01F1/10
CPCC08K5/3467D01F1/10D01F6/46C08L71/02C08L23/06
Inventor 陈大俊题杨吕莹陈思喻
Owner DONGHUA UNIV