Method for processing fluoride-free hydrostatic-pressure-resisting durable aterproof pure cotton canvas

A technology of hydrostatic pressure resistance and processing method, which is applied in the field of textile industry, can solve the problems of unclear migration process, and achieve the effect of eliminating the baking process, durable waterproof effect, and high hydrostatic pressure resistance

Active Publication Date: 2016-04-20
HEBEI NINGFANG GRP
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PFOS exists in groundwater, surface water and seawater surveyed all over the world (including the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for processing fluoride-free hydrostatic-pressure-resisting durable aterproof pure cotton canvas
  • Method for processing fluoride-free hydrostatic-pressure-resisting durable aterproof pure cotton canvas
  • Method for processing fluoride-free hydrostatic-pressure-resisting durable aterproof pure cotton canvas

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: Preparation of 21 / 2×21 / 272×4557 / 58 pure cotton canvas

[0045] (1) First, the gray cloth is subjected to blank inspection, seam turning, and singeing;

[0046] (2), cold pile - short steam washing:

[0047] The cold stack formula is: refining agent FORYLMAG10g / L, 27.5% industrial grade hydrogen peroxide 20g / L, 100% industrial grade caustic soda 30g / L, the stacking temperature is 35°C, and the stacking time is 4 hours;

[0048] The short steam washing process is as follows: vehicle speed 35m / min, excess rolling rate 70%, steaming temperature 90°C, washing tank temperature 80°C, and the rolling tank material formula is refining agent FORYLMAG 3g / L, 100% industrial grade caustic soda 20g / L ;

[0049] (3), mercerizing treatment: arrange the blank after cold stacking-short steaming and washing in a mercerizing machine equipped with a flat washing tank, control the speed of the vehicle at 45m / min, the concentration of caustic soda 250g / L, and the chelating dis...

Embodiment 2

[0056] Embodiment 2: prepare 21 / 2 * 1072 * 4557 / 58 pure cotton canvas

[0057] (1) First, the gray cloth is subjected to blank inspection, seam turning, and singeing;

[0058] (2), cold pile - short steam washing:

[0059] The cold stack formula is: refining agent FORYLMAG20g / L, 27.5% industrial grade hydrogen peroxide 30g / L, 100% industrial grade caustic soda 50g / L, the stacking temperature is 45°C, and the stacking time is 10 hours;

[0060] The short steam washing process is as follows: vehicle speed 60m / min, rolling rate 90%, steaming temperature 101°C, washing tank temperature 90°C, the rolling tank material formula is refining agent FORYLMAG 5g / L, 100% industrial grade caustic soda 35g / L ;

[0061] (3), mercerizing treatment: arrange the base after cold stacking-short steaming and washing in a mercerizing machine equipped with a flat washing tank, control the speed of the vehicle at 60m / min, the concentration of caustic soda 260g / L, and the chelating dispersant of 0.5g...

Embodiment 3

[0069] (1) First, the gray cloth is subjected to blank inspection, seam turning, and singeing;

[0070] (2), cold pile - short steam washing:

[0071] The cold stack formula is: refining agent FORYLMAG15g / L, 27.5% industrial grade hydrogen peroxide 25g / L, 100% industrial grade caustic soda 35g / L, the stacking temperature is 38°C, and the stacking time is 6 hours;

[0072] The short steam washing process is as follows: speed of 45m / min, excess rolling rate of 88%, steaming temperature of 100°C, washing tank temperature of 86°C, and the rolling tank material formula is refining agent FORYLMAG 5g / L, 100% industrial grade caustic soda 28g / L ;

[0073] (3), mercerizing treatment: arrange the base after cold stacking-short steam washing in a mercerizing machine equipped with a flat washing tank, control the speed of the vehicle at 55m / min, the concentration of caustic soda 260g / L, and the chelating dispersant of 0.7g / L , Soda soaking time is 42s, recovered alkalinity is 49g / L, fla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a method for processing fluoride-free hydrostatic-pressure-resisting durable waterproof pure cotton canvas. According to the method, pure cotton gray fabric is adopted, and the fluoride-free hydrostatic-pressure-resisting durable waterproof pure cotton canvas is obtained after fabric detection, seam turning, singeing, cold batching-short steaming washing, dyeing, full-width washing, tentering, fluoride-free waterproof treatment and preshrinking. According to operation of fluoride-free waterproof finishing, fluoride-free waterproof finishing liquid is prepared firstly, and is formed by blending 180 g/L to 240 g/L of a fluoride-free water-proofing agent RSH-NF, 18 g/L to 24 g/L of synergist and 0.3 g/L to 1.0 g/L of acetic acid; then, the gray fabric is soaked and rolled with the fluoride-free waterproof finishing liquid, and the rolling-over rate ranges from 60% to 70%; then, baking is carried out at the temperature of 110 DEG C to 130 DEG C. The processed fabric has the high hydrostatic-pressure-resisting effect and the lasting waterproof effect.

Description

technical field [0001] The invention belongs to the technical field of the textile industry and relates to a processing method for cotton and polyester-cotton fabrics, in particular to a processing method for a fluorine-free hydrostatic pressure-resistant and durable waterproof pure cotton canvas. Background technique [0002] The water resistance of tight fabrics (such as canvas, tent cloth, rainproof clothing, oilcloth, coated cloth, etc.) is an extremely important characteristic index of rainproof fabrics. To meet resistance, ISO811-1981 or GB / T4744-1997 Textile Water Resistance Determination - Hydrostatic Pressure Test Method is widely used in international trade, as well as American AATCC21-2001, German DIN53886 and other test methods. [0003] At present, the production methods of hydrostatic pressure-resistant fabrics in the market are mostly coating method and organic fluorine finishing, or the composite finishing method of coating + organic fluorine. The above prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/37D06M13/188D06M11/38D06M11/50D06P5/02D06M101/04
CPCD06M11/38D06M11/50D06M13/188D06M15/37D06M2101/04D06P5/02
Inventor 刘瑞宁赵冰唐立尚维欣杨现华王友明侯立山
Owner HEBEI NINGFANG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap