Novel early-strength and quick-drying tile adhesive concentrate

A tile adhesive and concentrated material technology, which is applied in the field of new early-strength and quick-drying tile adhesive concentrated material, can solve the problems of high transportation and storage costs, and achieve the effects of shortening construction time, saving construction period, and facilitating transportation

Inactive Publication Date: 2016-07-13
西卡德高(上海)建材有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tile glue solves the phenomenon of tile hollowing and brick falling well, but its transportation and storage costs are very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel early-strength and quick-drying tile adhesive concentrate
  • Novel early-strength and quick-drying tile adhesive concentrate
  • Novel early-strength and quick-drying tile adhesive concentrate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A new type of early-strength and quick-drying tile adhesive concentrate, said tile adhesive concentrate at least includes the following components, each component and the specific gravity ranges of the components are respectively:

[0036]

[0037] According to the proportion of 1 part of concentrated material, 1 part of 52.5 Portland cement, and 1 part of 60~120 mesh quartz sand, put the concentrated material, Portland cement and quartz sand into JC / T681-2005 planetary cement mortar mixer at low speed Stir for 10-20 minutes until the mixture is even, and you can get the adhesive for pasting tiles.

[0038] The ceramic tile adhesive prepared in embodiment 1 is tested for performance index, as shown in the following table:

[0039]

Embodiment 2

[0041] A new type of early-strength and quick-drying tile adhesive concentrate, said tile adhesive concentrate at least includes the following components, each component and the specific gravity ranges of the components are respectively:

[0042]

[0043] According to the proportion of 1 part of concentrated material, 1 part of 52.5 Portland cement, and 1 part of 60~120 mesh quartz sand, put the concentrated material, Portland cement and quartz sand into JC / T681-2005 planetary cement mortar mixer at low speed Stir for 10-20 minutes until the mixture is even, and you can get the adhesive for pasting tiles.

Embodiment 3

[0045] A new type of early-strength and quick-drying tile adhesive concentrate, said tile adhesive concentrate at least includes the following components, each component and the specific gravity ranges of the components are respectively:

[0046]

[0047] According to the proportion of 1 part of concentrated material, 1 part of 52.5 Portland cement, and 1 part of 60~120 mesh quartz sand, put the concentrated material, Portland cement and quartz sand into JC / T681-2005 planetary cement mortar mixer at low speed Stir for 10-20 minutes until the mixture is even, and you can get the adhesive for pasting tiles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to novel early-strength and quick-drying tile adhesive concentrate.The tile adhesive concentrate at least comprises, by weight, 500-800 parts of sulphoaluminate cement clinker, 200-500 parts of high-strength gypsum, 1-100 parts of early strength agent, 40-120 parts of dispersible latex powder, 1-10 parts of retarder, 1-40 parts of water reducer and 5-20 parts of cellulose ether.The novel early-strength and quick-drying tile adhesive concentrate has the advantages that the sulphoaluminate cement clinker and Portland cement are used as the composite cement base materials, the composite cement base materials are coordinated with the additives such as the early strength agent and retarder, tile glue coagulation time is regulated, sufficient operation time is guaranteed, early strength and quick drying are achieved, the next joint filling can be performed immediately after tile adhering, construction time can be shortened, and the construction period can be shortened.

Description

technical field [0001] The invention relates to a tile adhesive concentrate, in particular to a novel early-strength and quick-drying tile adhesive concentrate. Background technique [0002] Ceramic tiles are one of the important decorative building materials. The traditional method of pasting tiles is to soak the tiles in water for a period of time, mix gray cement and sand in a certain proportion to form a paste, apply it to the back of the tiles, and then paste it on the base. As people's requirements for tiles are getting higher and higher, the water absorption of tiles is getting lower and lower. Traditional pasting methods are likely to cause hollowing and falling off of tiles. In order to prevent hollowing and falling bricks, tile glue is widely used for pasting tiles. The tile glue is a mixture of gray cement and quartz sand as the main components, and redispersible rubber powder and other additives. Tile glue solves the phenomenon of tile hollowing and brick fall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B24/24C04B24/38
Inventor 宋丹曾翠云孙园园李文杰董峰亮万德刚张永进何曙光周碧平薛静丁天华王鸿博刘莹琨严昌俊郑徳煜
Owner 西卡德高(上海)建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com