A method for measuring sulfur content in slag melting flux

A technology of sulfur content and flux, applied in measuring devices, color/spectral characteristic measurement, instruments, etc., can solve the problem of no national standard samples for slag melting flux, etc., and achieve the solution of measurement problems, good accuracy, and easy operation Effect

Active Publication Date: 2018-10-02
WUKUN STEEL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The slag melting flux is in a powder state, so how to choose a suitable fluxing material to ensure the complete release of sulfur is particularly important. How to determine the working conditions of the high-frequency infrared carbon and sulfur analyzer is still inconclusive; there is no national standard sample for the slag melting flux. How to find a substitute standard sample is a difficult point

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. The spare parts used in the determination process are as follows: the first standard substance: converter slag GBW01707, the sulfur content is: 0.459%; the second standard substance: converter slag GBW01705, the sulfur content is: 0.126%; the third standard substance: high Slag BH0124-3, sulfur content: 0.76%; porcelain crucible: PT type ￠25mm×25mm; high-purity tungsten flux: C: <0.0008%, S: <0.0005%; pure iron flux: C: <0.0005 %, S: <0.0005%;

[0031] The instrument used in the determination process is CS-3000 (Beijing Nanke) high-frequency infrared carbon and sulfur analyzer. The working conditions of the instrument are: measuring flow rate 3.5L / min, oxygen pressure 0.30MPa, power gas pressure 0.38MPa, analysis time 50s. Environmental conditions: indoor relative humidity 45%.

[0032] 2. Determine the blank value of sulfur content: use a high-frequency infrared carbon-sulfur analyzer to measure the blank value of pure iron flux: S: 0.00005%, and the blank value o...

Embodiment 2

[0040] 1. The spare parts used in the determination process are as follows: the first standard substance: converter slag GBW01707, the sulfur content is: 0.459%; the second standard substance: converter slag GBW01705, the sulfur content is: 0.126%; the third standard substance: high Slag BH0124-3, sulfur content: 0.76%; porcelain crucible: PT type ￠25mm×25mm; high-purity tungsten flux: C: <0.0008%, S: <0.0005%; pure iron flux: C: <0.0005 %, S: <0.0005%;

[0041] The instrument used in the determination process is CS-3000 (Beijing Nanke) high-frequency infrared carbon and sulfur analyzer. The working conditions of the instrument are: measuring flow rate 3.0L / min, oxygen pressure 0.28MPa, power gas pressure 0.28MPa, analysis time 50s. Environmental conditions: indoor relative humidity 60%.

[0042] 2. Determine the blank value of sulfur content: use a high-frequency infrared carbon-sulfur analyzer to measure the blank value of pure iron flux: S: 0.00005%, and the blank value o...

Embodiment 3

[0050] 1. The spare parts used in the determination process are as follows: the first standard substance: converter slag GBW01707, the sulfur content is: 0.459%; the second standard substance: converter slag GBW01705, the sulfur content is: 0.126%; the third standard substance: high Slag BH0124-3, sulfur content: 0.76%; porcelain crucible: PT type ￠25mm×25mm; high-purity tungsten flux: C: <0.0008%, S: <0.0005%; pure iron flux: C: <0.0005 %, S: <0.0005%; the instrument used in the determination process is CS-3000 (Beijing Nanke) high-frequency infrared carbon and sulfur analyzer. The working conditions of the instrument are: measuring flow rate 2.5L / min, oxygen pressure 0.20MPa, power gas pressure 0.20MPa, analysis time 55s. Environmental conditions: indoor relative humidity 50%.

[0051] 2. Determine the blank value of sulfur content: use a high-frequency infrared carbon-sulfur analyzer to measure the blank value of pure iron flux: S: 0.00005%, and the blank value of sulfur c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for measuring the sulfur content of a slag melting flux. According to the method, a high frequency infrared carbon-sulfur analyzer is adopted, and a high frequency induced combustion-infrared ray absorption method is used to measure the sulfur content. The method comprises the following steps: preparing a spare for the test, measuring the blank value of sulfur content, calibrating a high frequency infrared carbon-sulfur analyzer, sampling, preparing a sample, preparing a specimen, and measuring the sulfur content of a sample of slag melting flux powder. The provided method solve the problem that there is no a standard sample of slag melting flux. The repeatability and accuracy of measurement results are good. The problem that sulfur content of slag melting flux is difficult to measure is solved. A reliable technical support is provided for controlling the quality of steel smelting.

Description

technical field [0001] The invention belongs to the technical field of element quantitative analysis, and in particular relates to a method for measuring the sulfur element content in a slag melting flux. Background technique [0002] In converter steelmaking, the speed of slagging and the effect of slagging directly affect the metallurgical effect of the smelting process. In order to improve the slag removal effect, the commonly used fluxes are iron oxide-containing materials such as fluorspar, iron ore, and sludge balls. Fluorite slag is conducive to rapid slagging, does not reduce the slag alkalinity, has the advantages of small impact on thermal balance, but has the disadvantages of accelerating lining erosion, easily causing splashing and polluting the environment; materials containing iron oxide have little environmental pollution, but the cost is high , Slow slag melting, great influence on heat balance. In order to better improve the stability of smelting process c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/3563
CPCG01N21/35
Inventor 李文生王磊阚绍宽许涯平欧阳光
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com