Method for achieving germanium precipitation through metallic oxide

An oxide and germanium precipitation technology, applied in the direction of improving process efficiency, can solve the problems of low germanium grade, high raw material requirements, harsh operating conditions, etc. Effect

Active Publication Date: 2016-08-31
ZHEJIANG HUAYOU COBALT +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tannin precipitation method is easy to operate and has a high precipitation rate, but tannin is expensive and used in a large amount, generally 25 to 30 times the content of germanium, which is a one-time consumable, and the tannin organic matter contained in tannin will affect the subsequent The extraction process of cobalt and copper has a certain impact, and the price of tannin is relatively expensive, and the supply of tannin is limited
h 2 Although the S precipitation method has the advantages of fast germanium enrichment and good selectivity, the operating conditions are harsh, which is not conducive to production, and the H 2 S is toxic, the operating environment is poor, there are safety hazards in actua

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for achieving germanium precipitation through metallic oxide
  • Method for achieving germanium precipitation through metallic oxide
  • Method for achieving germanium precipitation through metallic oxide

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] Take 50L of sulfuric acid leaching solution from cobalt copper smelting as the preliquid for germanium precipitation, in which the concentration of Cu is 0.73g / L, the concentration of Fe is 22.97g / L, the concentration of Ge is 1.09g / L, and the other impurity concentrations are shown in Table 1, and heated to 72℃ , Add metal oxides and water to the germanium precipitation pre-liquid, adjust the pH value to 5.0, carry out an alkaline one-step germanium precipitation reaction for 1h, then filter, one-step filter residue is washed and then dried for testing; one-step filtrate is heated to 70℃ and then metal oxide is added With water, adjust the pH value to 6.0, carry out the second-stage germanium precipitation reaction for 1 hour and then filter, the second-stage filter residue is washed and then dried for testing, and the second-stage filtrate is tested. The test results are shown in Table 1.

[0019] Table 1 Test results of Example 1

[0020] ingredien...

Example Embodiment

[0022] Example 2

[0023] Take 50L of sulfuric acid leaching solution from cobalt copper smelting as the preliquid for germanium precipitation, in which the concentration of Cu is 0.55g / L, the concentration of Fe is 24.04g / L, the concentration of Ge is 1.28g / L, and the other impurity concentrations are shown in Table 2, and heated to 75℃ , Add metal oxides and water to the germanium precipitation pre-liquid, adjust the pH value to 4.5, carry out an alkaline one-step germanium precipitation reaction for 1.5h, then filter, one-step filter residue is washed and then dried for testing; one-step filtrate is heated to 72℃, and metal oxidation is added And water, adjust the pH value to 5, carry out the second-stage germanium precipitation reaction for 2 hours and then filter, the second-stage filter residue is washed and then dried for testing, and the second-stage filtrate is tested. The test results are shown in Table 2.

[0024] Table 2 Test results of Example 2

[0025]

[0026]

[00...

Example Embodiment

[0028] Example 3

[0029] Take 50L of sulfuric acid leaching solution from cobalt copper smelting as the preliquid for germanium precipitation, in which the concentration of Cu is 0.46g / L, the concentration of Fe is 3.68g / L, the concentration of Ge is 0.79g / L, and the concentration of other impurities is shown in Table 3, heated to 70℃ , Add metal oxide and water to the germanium precipitation pre-liquid, adjust the pH value to 6, carry out an alkaline one-step germanium precipitation reaction for 1h, then filter, one-step filter residue is washed and then dried for testing, one-step filtrate is heated to 75℃ and then metal oxide is added With water, adjust the pH value to 7, carry out the second-stage germanium precipitation reaction for 1 hour and then filter, the second-stage filter residue is washed and then dried for testing, and the second-stage filtrate is tested. The test results are shown in Table 3.

[0030] Table 3 Test results of Example 3

[0031]

[0032]

[0033] It ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a treatment method for comprehensive resource recycling of dissipated metal germanium, in particular to a treatment method for carrying out precipitation recycling on germanium through metallic oxide. According to the treatment method, the metallic oxide is adopted as a neutral precipitation agent, a two-section neutralizing hydrolysis method is adopted, and the germanium is subjected to precipitation recycling from germanium containing material liquid. Compared with an existing germanium precipitation recycling process, the advantages of the method are remarkable, the metallic oxide is adopted as the neutral precipitation agent, and the two-section neutralizing hydrolysis method is adopted for treating germanium pre-precipitation liquid; operation is easy, the residue filtering performance is good, and the quantity of added auxiliary materials is small; and the total germanium precipitation rate can reach 98% or above, the grade of obtained germanium concentrates is about 6%-8%, and extraction and comprehensive recycling of the valuable metal germanium in the germanium containing material liquid can be achieved.

Description

technical field [0001] The invention relates to a treatment method for the comprehensive resource recovery of scattered germanium metal, in particular to a treatment method for recovering germanium by metal oxide precipitation. technical background [0002] At present, the main process methods for precipitation and recovery of germanium from cobalt-copper smelting leachate and other germanium-containing liquids include: tannin precipitation method, H 2 S precipitation method and Fe-Ge co-precipitation method. The tannin precipitation method is easy to operate and has a high precipitation rate, but tannin is expensive and used in a large amount, generally 25 to 30 times the content of germanium, which is a one-time consumable, and the tannin organic matter contained in tannin will affect the subsequent The extraction process of cobalt and copper has a certain impact, and the price of tannin is relatively expensive, and the supply of tannin is limited. h 2 Although the S pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B41/00C22B3/44
CPCC22B3/44C22B41/00Y02P10/20
Inventor 沈建中韩笑孙灿
Owner ZHEJIANG HUAYOU COBALT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap