Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method of outdoor sportswear fabric

A technology for sportswear and fabrics, applied in the field of textile fabrics, can solve the problems of difficult maintenance, difficult to wash, poor wear resistance, etc., and achieve the effects of enhancing antibacterial performance, moisture absorption and breathability, increasing drape and good breathability.

Active Publication Date: 2016-09-21
东阳新东煌服饰有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Real silk fabrics have problems such as high price, low strength, poor wear resistance, not easy to wash, and difficult maintenance. For this reason, many imitation silk fabrics have entered the market. The advanced manufacturing process is used to make imitation silk fabrics, so as to overcome many shortcomings of real silk fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of outdoor sportswear fabric
  • Preparation method of outdoor sportswear fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method for outdoor sportswear fabric, comprising the following steps:

[0031] A. Weaving: use superfine polyester fiber, Coolmax fiber and modified cattail fiber as raw materials, and use water jet loom to make gray cloth;

[0032] B, sizing and oiling: the gray cloth prepared in step A is subjected to sizing and oiling;

[0033] C. Desizing and refining: use a low bath ratio high pressure jet overflow machine for desizing and refining treatment, the process prescription and conditions are as follows: desizing bath PH value 8, refining agent: 3g / L, NaOH: 1.5g / L, liquor ratio : 1:12, temperature: 78°C, time: 38min;

[0034] D. Alkali weight reduction: After the desizing and refining is completed, then carry out alkali weight reduction treatment. The treatment conditions are 35% NaOH 120g / L, temperature: 105°C, time: 8min;

[0035] E. Post-setting drying: first soak in 3% sodium dodecylsulfonate solution for 8 minutes, then perform 100°C water padding, an...

Embodiment 2

[0048] A preparation method of outdoor sportswear fabric, comprising the following steps:

[0049] A. Weaving: use superfine polyester fiber, Coolmax fiber and modified cattail fiber as raw materials, and use water jet loom to make gray cloth;

[0050] B, sizing and oiling: the gray cloth prepared in step A is subjected to sizing and oiling;

[0051] C. Desizing and refining: use a low bath ratio high-pressure jet overflow machine for desizing and refining treatment. The process prescription and conditions are as follows: desizing bath PH value 7.5-8.5, refining agent: 2g / L, NaOH: 1g / L, bath Ratio: 1:15, temperature: 80°C, time: 35min;

[0052]D. Alkali weight reduction: After desizing and refining, carry out alkali weight reduction treatment. The treatment conditions are 35% NaOH 140g / L, temperature: 110°C, time: 10min;

[0053] E. Post-setting drying: first soak in 5% sodium dodecylsulfonate solution for 10 minutes, then perform 100°C water padding, and then dry and shape ...

Embodiment 3

[0066] A preparation method for outdoor sportswear fabric, comprising the following steps:

[0067] A. Weaving: use superfine polyester fiber, Coolmax fiber and modified cattail fiber as raw materials, and use water jet loom to make gray cloth;

[0068] B, sizing and oiling: the gray cloth prepared in step A is subjected to sizing and oiling;

[0069] C. Desizing and refining: use a low bath ratio high-pressure jet overflow machine for desizing and refining treatment. The process prescription and conditions are as follows: desizing bath PH value 7.5-8.5, refining agent: 2g / L, NaOH: 2g / L, bath Ratio: 1:10, temperature: 75-80°C, time: 35-40min;

[0070] D. Alkali reduction: After desizing and refining, carry out alkali reduction treatment. The treatment conditions are 35% NaOH 100g / L, temperature: 100°C, time: 5min;

[0071] E. Post-setting drying: first soak in 5% sodium dodecylsulfonate solution for 5 minutes, then perform padding in 100°C water, and then dry and shape at 19...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of outdoor sportswear fabric. The fabric adopting ultrafine polyester fibers has better moisture absorption, more excellent moisture absorption and sweat releasing properties and better breathability and drapability than conventional silk-like fabric. Through appropriate twisting, the polyester fibers have a diffuse reflection phenomenon on light and have the luster of almost real silk, and the drapability of the fabric can be increased; Coolmax fibers and cottongrass fibers are added for blending, and the antibacterial performance and the moisture absorption and sweat releasing properties of the fabric are enhanced; through pretreatment of the cottongrass fibers, the effective antibacterial ingredients of the cottongrass fibers are prevented from being damaged as far as possible.

Description

technical field [0001] The invention relates to a method for manufacturing a fabric, which belongs to the field of textile fabrics, in particular to a method for preparing an outdoor sportswear fabric. Background technique [0002] Real silk fabrics have problems such as high price, low strength, poor wear resistance, not easy to wash, and difficult maintenance. For this reason, many imitation silk fabrics have entered the market. The advanced manufacturing process is used to make imitation silk fabrics, so as to overcome many shortcomings of real silk fabrics. [0003] Public documents, such as the Chinese patent whose patent number is CN1096333A, disclose a kind of using three different polyester co-spun fine denier filaments as warp yarns, fine denier polyester low elastic yarns as weft yarns, and the fabric structure adopts variable plain weave; the publication number is CN1021270522A The Chinese patent disclosed a wrinkle-resistant imitation silk fabric, the fabric ado...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/38D06M13/256D06M16/00D06M101/32D06M101/06
CPCD06M11/38D06M13/256D06M16/003D06M2101/06D06M2101/32
Inventor 朱卫强
Owner 东阳新东煌服饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More