Silk softener

A softener and silk technology, which is applied in the field of softener preparation, can solve the problems of easy entanglement, adhesion, elasticity and heat retention of silk fibers, and achieves excellent bactericidal performance, low preparation cost and good rewetting performance.

Inactive Publication Date: 2016-09-21
广西南宁马山东龙蚕业有限责任公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a silk softener to solve the problems that silk fibers are easy to tangle and stick together, and the elasticity and warmth retention will decrease accordingly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silk softener
  • Silk softener
  • Silk softener

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The preparation method of described silk softening agent, comprises the following steps:

[0043] S1: Add the surfactant into the water, raise the temperature to 44-46°C and stir to dissolve to prepare the mixed solution I;

[0044] S2: Add penetrant, emulsifier, dispersant, cross-linking agent, thickener to the mixed solution I prepared in step S1, heat to 58-62°C, and stir at a speed of 200-300r / min under the action of ultrasonic waves Treat for 25-30 minutes to obtain the mixed solution II;

[0045] S3: Stop the heating and ultrasonic action, add defoamer and foam stabilizer to the mixed solution II prepared in step S2, and stir for 5-10 minutes at a rotating speed of 100-300r / min to prepare mixed solution III;

[0046] S4: Add preservatives and fragrances to the mixed solution III prepared in step S3, and stir for 3-5 minutes at a rotation speed of 100-200 r / min to prepare mixed solution IV;

[0047] S5: Adding a regulator to the mixed solution IV prepared in step...

Embodiment 1

[0050] A silk softening agent, in parts by weight, comprising the following raw materials: 90 parts of surfactants, 8 parts of defoamers, 4 parts of foam stabilizers, 3 parts of penetrants, 2 parts of emulsifiers, 2 parts of dispersants, 3 parts of joint agent, 3 parts of regulator, 2 parts of thickener, 2 parts of preservative, 1 part of flavoring agent, 850 parts of water.

[0051] The surfactant is polyacrylamide.

[0052] The defoamer is silane-modified propionate.

[0053] The foam stabilizer is polyvinyl alcohol.

[0054] The penetrant potassium alkylbenzene sulfonate.

[0055] Described emulsifier is glyceryl monostearate.

[0056] The dispersant is potassium lauryl sulfate.

[0057] The cross-linking agent is diethyl phosphate.

[0058] The regulator is acetic acid.

[0059] The thickener is carrageenan.

[0060] Described preservative is quinoxyfin.

[0061] The flavoring agent is lavender essential oil.

[0062] The preparation method of described silk softe...

Embodiment 2

[0069] A silk softening agent, in parts by weight, comprising the following raw materials: 80 parts of surfactants, 6 parts of defoamers, 3 parts of foam stabilizers, 2 parts of penetrants, 2 parts of emulsifiers, 1 part of dispersants, 2 parts of joint agent, 2 parts of regulator, 2 parts of thickener, 1 part of preservative, 0.8 part of flavoring agent, 700 parts of water.

[0070] The surfactant is polyacrylamide.

[0071] The defoamer is silane-modified propionate.

[0072] The foam stabilizer is polyvinyl alcohol.

[0073] The penetrant potassium alkylbenzene sulfonate.

[0074] Described emulsifier is glyceryl monostearate.

[0075] The dispersant is potassium lauryl sulfate.

[0076] The cross-linking agent is diethyl phosphate.

[0077] The regulator is acetic acid.

[0078] The thickener is carrageenan.

[0079] Described preservative is quinoxyfin.

[0080] The flavoring agent is lavender essential oil.

[0081] The preparation method of described silk softeni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a silk softener which comprises the following raw materials in parts by weight: 80 to 100 parts of surfactant, 6 to 10 parts of antifoaming agent, 3 to 5 parts of foam stabilizer, 2 to 4 parts of penetrant, 2 to 3 parts of emulsifier, 1 to 2 parts of dispersing agent, 2 to 4 parts of cross-linking agent, 2 to 3 parts of modifier, 2 to 3 parts of thickener, 1 to 2 parts of preservative, 0.8 to 1.2 parts of flavouring agent and 700 to 1,000 parts of water. The silk softener disclosed by the invention is excellent in sterilization performance, and has a sterilizing rate of over 96% on staphylococcus aureus, escherichia coli and candida albicans; a preparation method of the silk softener is simple, convenient and feasible; the silk softener is low in preparation cost and is beneficial to popularization and application.

Description

【Technical field】 [0001] The invention belongs to the technical field of softener preparation, and in particular relates to a silk softener. 【Background technique】 [0002] The process of processing silk quilts in the traditional way is simple, and the variety is extremely single. After the silk quilts processed by the traditional process are used, the silk fibers are easy to tangle and stick, and the elasticity and warmth will be reduced accordingly, requiring frequent dismantling and tearing Loose, in order to maintain the original excellent clothing performance of silk quilt. [0003] In order to endow silk with excellent properties such as bulkiness, softness, and high elasticity, it is necessary to refine the silk to expand the voids of the silk fibers, and the resulting silk cotton has the characteristics of bulkiness, high elasticity, and no knots between fibers. Through the puffing treatment of silk, the bulkiness, high elasticity and softness of silk fibers can be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/285D06M15/333D06M13/224D06M13/292D06M13/256D06M13/262D06M15/03D06M13/00D06M101/10
CPCD06M15/285D06M13/00D06M13/2243D06M13/256D06M13/262D06M13/292D06M15/03D06M15/333D06M16/00D06M2101/10D06M2200/50
Inventor 蓝莉芬蓝芬唐站蓝惠芬黄正然
Owner 广西南宁马山东龙蚕业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com