A kind of high flux thick polytetrafluoroethylene membrane and preparation method thereof

A polytetrafluoroethylene film and a polytetrafluoroethylene technology are applied in the field of high-flux thick polytetrafluoroethylene film and its preparation, which can solve the problems of inability to meet the thickness, porosity and air permeability at the same time, and achieve the service life Long, good porosity, high working efficiency

Active Publication Date: 2018-05-15
上海灵氟隆新材料科技有限公司 +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention is to overcome the defect that the single-layer / multi-layer polytetrafluoroethylene membrane in the prior art cannot simultaneously meet the thickness, porosity and air permeability required by the high-temperature filter material for the polytetrafluoroethylene membrane, Provided is a high-throughput thick polytetrafluoroethylene membrane and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of high flux thick polytetrafluoroethylene membrane, it comprises the steps:

[0039] (1) 2 single-layer polytetrafluoroethylene films are aligned and stacked to form a laminated double-layer film; wherein, the porosity of the single-layer polytetrafluoroethylene film is 80%, and the thickness of the single-layer polytetrafluoroethylene film 0.006mm and a width of 2000mm;

[0040] (2) Feed the laminated double-layer film into the hot-air bonding device through a steel feed roller, and perform a hot-air bonding process on the laminated double-layer film with a hot air flow, so that the laminated double-layer film The upper surface of the film absorbs heat and softens and bonds with the polytetrafluoroethylene film of the lower floor; wherein, the number of nozzles of the first hot air flow is 2, and the pressure of the first hot air flow out of the nozzle is 1.5MPa, and the temperature of the first hot air flow The temperature is 270°C, the moving s...

Embodiment 2

[0047] A preparation method of high flux thick polytetrafluoroethylene membrane, it comprises the steps:

[0048] (1) 3 single-layer polytetrafluoroethylene films are aligned and stacked to form a stacked three-layer film; wherein, the porosity of the single-layer polytetrafluoroethylene film is 80%, and the thickness of the single-layer polytetrafluoroethylene film 0.006mm and a width of 2000mm;

[0049] (2) Feed the laminated three-layer film into the hot-air bonding device through a steel feed roller, and perform one hot-air bonding process on the laminated three-layer film with the first hot air flow, so that the laminated three-layer The upper surface of the film absorbs heat and softens and bonds with the polytetrafluoroethylene film of the lower floor; wherein, the number of nozzles of the first hot air flow is 2, and the pressure of the first hot air flow out of the nozzle is 2MPa, and the temperature of the first hot air flow is 330°C, the moving speed of the laminat...

Embodiment 3

[0056] A preparation method of high flux thick polytetrafluoroethylene membrane, it comprises the steps:

[0057] (1) 4 single-layer polytetrafluoroethylene films are aligned and stacked to form a stacked four-layer film; wherein, the porosity of the single-layer polytetrafluoroethylene film is 80%, and the thickness of the single-layer polytetrafluoroethylene film 0.006mm and a width of 2000mm;

[0058] (2) Feed the laminated four-layer film into the hot-air bonding device through a steel feed roller, and perform one hot-air bonding process on the laminated four-layer film with the first hot air flow, so that the laminated four-layer film The upper surface of the film absorbs heat and softens and bonds with the polytetrafluoroethylene film of the lower floor; wherein, the number of nozzles of the first hot air flow is 2, and the pressure of the first hot air flow out of the nozzle is 2.5MPa, and the temperature of the first hot air flow 350°C, the moving speed of the laminat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-throughput thick polytetrafluoroethylene membrane and a preparation method thereof. The method is as follows: (1) aligning and stacking several single-layer polytetrafluoroethylene membranes to form a stacked multilayer membrane; (2) Feed the laminated multilayer film into the hot air bonding device through the feed roller, then carry out one hot air bonding process with one hot air flow, so that the upper surface of the laminated multilayer film absorbs heat and softens and Bonding with the lower polytetrafluoroethylene film; (3) Perform tension adjustment treatment; (4) Use II hot air flow to carry out II hot air bonding treatment, so that the lower surface of the multilayer composite film absorbs heat and softens Adjacent PTFE films bonded; (5) tension adjustment processing; (6) winding output. The high-flux thick polytetrafluoroethylene membrane of the present invention has high porosity and good air permeability, and it is covered with non-woven filter mat to make high-temperature filter material, which has high filtration efficiency for fine particles in high-temperature flue gas, and can prolong The service life of high temperature filter material.

Description

technical field [0001] The invention relates to a high-flux thick polytetrafluoroethylene membrane and a preparation method thereof. Background technique [0002] PTFE has excellent thermal stability, its melting point is 327°C, its decomposition temperature exceeds 400°C, and it can work for a long time in the range of -196°C to 260°C; it has a relatively high viscosity coefficient of about 10 10 ~10 12 Pa·S, no viscous flow even above the melting point; outstanding chemical corrosion resistance, insoluble in any solvent except its own fluoride and molten alkali metal; at the same time, low surface free energy and low friction coefficient (0.04 ), has excellent self-cleaning properties, and is an ideal material for preparing high-temperature flue gas filter materials. At present, the high-temperature flue gas filter material is a composite material composed of non-woven filter felt and polytetrafluoroethylene membrane. During the filtration process, the high-temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/36B01D69/02B01D67/00
Inventor 薛刚张建军郑淑琴陈迎妹
Owner 上海灵氟隆新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com