Cement-stabilizing layer material of regenerated fiber-reinforced building solid waste recycled fine aggregate and preparation method of cement-stabilizing layer material

A technology of solid waste and recycled fine aggregate, which is applied in the direction of solid waste management, sustainable waste treatment, and climate sustainability, and can solve problems such as environmental pollution, waste of construction solid waste regeneration resources, and high processing costs. Achieve high compressive strength and enhance the effect of use value

Inactive Publication Date: 2016-10-12
HUNAN YUNZHONG REGENERATION TECH CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the current grading ratio of construction solid waste recycled road water stabilization layer, the amount of fine aggregate below 9.5mm is less than 50%, and more than 20% of the fine aggregate cannot be fully utilized
Therefore, if these fine materials cannot be fully and rationally utilized, it will result in a waste of construction solid waste renewable resources, and at the same time bring new environmental pollution problems, and the treatment cost will remain high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement-stabilizing layer material of regenerated fiber-reinforced building solid waste recycled fine aggregate and preparation method of cement-stabilizing layer material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This embodiment relates to a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, which is composed of 94.5% mass fraction of construction solid waste regenerated fine aggregate (wherein the mass of 1# material and 2# material ratio of 3.26:6.74) and 5.5% of P.O 42.5 cement, mixed with 3‰ of recycled woven bag fiber and 9.6% of water relative to the sum of the above two raw materials, wherein the length of the recycled woven bag fiber is 15~ 20mm, equivalent diameter 35-50μm, tensile strength ≥ 826MPa.

[0045]This embodiment also relates to a method for preparing a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, the method comprising the following steps:

[0046] Add 94.5% mass fraction of construction solid waste regenerated fine aggregate (the mass ratio of 1# material to 2# material is 3.26:6.74) and 5.5% mass fraction of P.O 42.5 cement into the forced mix...

Embodiment 2

[0048] This embodiment relates to a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, which is composed of 95.5% mass fraction of construction solid waste regenerated fine aggregate (wherein the mass of 1# material and 2# material The ratio is 4.35:5.65) and 4.5% of P.O 32.5 cement, and externally mixed with 1‰ of recycled glass fiber and 10.4% of water relative to the sum of the above two raw materials, wherein the length of recycled glass fiber is 6-15mm, The equivalent diameter is 15-35μm, and the tensile strength is ≥950MPa.

[0049] This embodiment also relates to a method for preparing a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, the method comprising the following steps:

[0050] Add 95.5% mass fraction of construction solid waste regenerated fine aggregate (the mass ratio of 1# material to 2# material is 4.35:5.65) and 4.5% mass fraction of P.O 32.5 ce...

Embodiment 3

[0052] This embodiment relates to a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, the material is composed of 97% mass fraction of construction solid waste regenerated fine aggregate (wherein the quality of 1# material and 2# material The ratio is 6.86:3.14) and 3% of P.O 42.5 cement with a mass fraction of 2‰ of recycled woven bag fiber and 12.5% ​​of water relative to the sum of the above two raw materials, wherein the length of the recycled woven bag fiber is 15 ~20mm, equivalent diameter 35~50μm, tensile strength ≥826MPa.

[0053] This embodiment also relates to a method for preparing a water-stabilizing layer material of fiber-reinforced construction solid waste regenerated fine aggregate, the method comprising the following steps:

[0054] Add 97% mass fraction of construction solid waste regenerated fine aggregate (the mass ratio of 1# material to 2# material is 6.86:3.14) and 3% mass fraction of P.O 42.5 cemen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a cement-stabilizing layer material of regenerated fiber-reinforced building solid waste recycled fine aggregate and a preparation method of the cement-stabilizing layer material. Building solid waste recycled fine aggregate and Portland cement serve as main materials and are doped with regenerated fibers and water, stirring and blending are carried out, and the cement-stabilizing layer material is obtained. The added fiber material and the cement material act synergistically, and thus the building solid waste recycled fine aggregate can be stably aggregated to form an integral structure. The added fiber material has high tensile strength and forms a network skeleton structure in the mixture, the toughness and impact resistance of the cement-stabilizing layer material can be obviously improved, generation and development of cracks can be effectively prevented, and the anti-scouring property, the freezing resistance and other endurance properties of the cement-stabilizing layer can be improved.

Description

technical field [0001] The invention belongs to the technical field of preparation of water-stabilizing layer materials for road bases, and in particular relates to a water-stabilizing layer material for regenerated fiber-reinforced construction solid waste recycled fine aggregate and a preparation method thereof. Background technique [0002] In the past ten years, with the acceleration of urbanization and industrialization in my country, urban construction has progressed from extensive development and large-scale old city renovation, to large-scale construction of residential quarters and reconstruction and expansion of roads, resulting in the rapid generation of a large amount of construction waste. At present, domestic construction waste treatment basically remains in the backward and simple landfill treatment. Due to the non-degradability of construction waste, landfill treatment will bring disastrous consequences to the society. The simple processing method consumes a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/16C04B20/02C04B14/42C04B18/20
CPCC04B20/0048C04B20/0076C04B20/026C04B28/04C04B2111/343C04B2201/50C04B18/16C04B22/002C04B18/20C04B14/42Y02W30/91
Inventor 杨科吴超凡肖红波李行欧阳添资
Owner HUNAN YUNZHONG REGENERATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com