Preparation method of refractory ceramic tile

A refractory and ceramic tile technology, applied in the ceramic tile field, can solve the problem of waste glass polluting the environment, and achieve the effects of reducing the amount of raw materials, fully mixing powder materials, and improving strength

Inactive Publication Date: 2016-10-12
岑溪市新建球陶瓷有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a preparation method of refractory tiles, which can solve the problem of environmental pollution caused by waste glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing refractory tiles, comprising a brick body, the brick body is made of the following raw materials in parts by weight: 40 parts of kaolin, 21 parts of crushed stone, 15 parts of waste glass, 10 parts of magnesia, and 9 parts of high alumina bauxite , 8 parts of refractory binder;

[0018] A. Take the kaolin, crushed stone, waste glass, magnesia, and high alumina bauxite of the above ingredients and grind them into powder with a ball mill, and pass the powder through a 300-mesh sieve; B. Mix the sieved powder with a refractory binder , use a sprayer to spray powder; C. send the powder into a ceramic press for compression molding to make adobe, the pressure setting value of the ceramic press is greater than 40Mpa; the pressing times of the adobe is 2 times; D. After the bricks enter the roller kiln for firing, the firing time is 7 hours, the firing temperature in the pre-tropical zone is 800°C; the firing temperature in the firing zone is 1600°C; Dro...

Embodiment 2

[0020] A method for preparing refractory tiles, comprising a brick body, the brick body is made of the following raw materials in parts by weight: 50 parts of kaolin, 31 parts of crushed stone, 20 parts of waste glass, 16 parts of magnesia, and 13 parts of high alumina bauxite , 16 parts of refractory binder;

[0021] A. Take the kaolin, crushed stone, waste glass, magnesia, and high alumina bauxite of the above ingredients and grind them into powder with a ball mill, and pass the powder through a 600-mesh sieve; B. Mix the sieved powder with a refractory binder , use a sprayer to spray powder; C. send the powder into a ceramic press for compression molding to make adobe, the pressure setting value of the ceramic press is greater than 40Mpa; the pressing times of the adobe is 5 times; D. After the bricks enter the roller kiln for firing, the firing time is 12 hours, the firing temperature of the pre-tropical zone is 1000°C; the firing temperature of the firing zone is 2000°C; ...

Embodiment 3

[0023] A method for preparing refractory tiles, comprising a brick body, the brick body is made of the following raw materials in parts by weight: 45 parts of kaolin, 16 parts of gravel, 17 parts of waste glass, 13 parts of magnesia, and 11 parts of high alumina bauxite , 12 parts of refractory binder.

[0024] A. Take the kaolin, crushed stone, waste glass, magnesia, and high alumina bauxite of the above ingredients and grind them into powder with a ball mill, and pass the powder through a 450-mesh sieve; B. Mix the sieved powder with a refractory binder , use a sprayer to spray powder; C. send the powder into a ceramic press for compression molding to make adobe, the pressure setting value of the ceramic press is greater than 40Mpa; the pressing times of the adobe is 3 times; D. After the bricks enter the roller kiln for firing, the firing time is 9 hours, the firing temperature in the pre-tropical zone is 900°C; the firing temperature in the firing zone is 1800°C; Drop to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a refractory ceramic tile and relates to the technical field of ceramic tiles. The refractory ceramic tile comprises a tile body, wherein the tile body is prepared from raw materials in parts by weight as follows: kaolin, broken stone, waste glass, magnesite, high-aluminum bauxite and a refractory binder. The preparation method comprises following steps: A, the kaolin, the broken stone, the waste glass, the magnesite and the high-aluminum bauxite are taken and ground into powder by a ball grinding mill, and the powder is screened by a sieve of 300-600 meshes; B, the screened powder is mixed with the refractory binder, and spray powder preparation is performed by a spraying machine; C, the powder is fed into a ceramic press for press forming, and a green tile is prepared; D, the green tile enters a roller kiln for firing; E, edge grinding is performed finally, and a finished product can be obtained. Compared with the prior art, the waste glass can be utilized as aggregate for the preparation method of the refractory ceramic tile, so that the strength of the refractory ceramic tile is improved and the environment pollution is reduced.

Description

technical field [0001] The invention relates to the technical field of tiles, in particular to a method for preparing refractory tiles using waste glass as one of the aggregates. Background technique [0002] Waste glass is one of the more difficult components of municipal waste. Waste glass can neither be incinerated nor degraded in landfill. Waste glass contains a large amount of silica and silicate, and some of them contain heavy metals such as zinc and copper. Once discarded at will, it may also cause soil and groundwater pollution. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing refractory ceramic tiles, which can solve the problem of environmental pollution caused by waste glass. [0004] In order to solve the above problems, the technical solution adopted in the present invention is: the preparation method of the refractory ceramic tile, including the brick body, the brick body is m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66C04B33/13C04B33/132C04B35/63
CPCC04B33/13C04B35/63C04B35/66C04B2235/3206C04B2235/3217Y02P40/60
Inventor 文亮
Owner 岑溪市新建球陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap