PE (Poly Ethylene) heat shrink film and preparation method thereof

A heat-shrinkable film and polyethylene technology, applied in the field of packaging materials, can solve the problems of poor transparency and surface gloss, single performance, environmental pollution, etc., and achieve the effects of good anti-aging, simple preparation method and easy operation.

Inactive Publication Date: 2016-10-12
桐城市华猫软膜有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a PE heat-shrinkable film and its preparation method to solve the single performance in the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A PE heat-shrinkable film, which is prepared from the following raw materials in parts by weight: 40 parts of ethylene-vinyl acetate copolymer, 60 parts of poly-3-hydroxybutyrate, 60 parts of high-density polyethylene, 40 parts of linear low-density polyethylene 1 part, 2 parts of PS-802 antioxidant, 1 part of heat stabilizer, 1 part of brominated epoxy resin, 3 parts of mixture of fluoropolymer processing aid and polyethylene, mixture of silica and polyethylene 3 parts, the plasticizer is 2 parts of adipate, wherein the melt flow rate of linear low density polyethylene is 0.2g / 10min, and the density is 0.850g / cm 3 .

[0023] A preparation method of PE heat shrinkable film, comprising the following steps:

[0024] (1) Take raw materials according to the above-mentioned parts by weight;

[0025] (2) Add ethylene-vinyl acetate copolymer, poly-3 hydroxybutyrate, high-density polyethylene, linear low-density polyethylene, antioxidant, heat stabilizer, flame retardant, lub...

Embodiment 2

[0029] A PE heat-shrinkable film, which is prepared from the following raw materials in parts by weight: 60 parts of ethylene-vinyl acetate copolymer, 50 parts of poly-3-hydroxybutyrate, 70 parts of high-density polyethylene, and 50 parts of linear low-density polyethylene 1 part, 1 part of PS-802 antioxidant, 3 parts of heat stabilizer, 5 parts of brominated epoxy resin, 1 part of mixture of fluoropolymer processing aid and polyethylene, mixture of silica and polyethylene 1 part, the plasticizer is 4 parts of adipate, wherein the melt flow rate of linear low density polyethylene is 1.2g / 10min, and the density is 0.900g / cm 3 .

[0030] A preparation method of PE heat shrinkable film, comprising the following steps:

[0031] (1) Take raw materials according to the above-mentioned parts by weight;

[0032] (2) Add ethylene-vinyl acetate copolymer, poly-3 hydroxybutyrate, high-density polyethylene, linear low-density polyethylene, antioxidant, heat stabilizer, flame retardant, ...

Embodiment 3

[0036] A PE heat-shrinkable film, which is prepared from the following raw materials in parts by weight: 50 parts of ethylene-vinyl acetate copolymer, 55 parts of poly-3-hydroxybutyrate, 65 parts of high-density polyethylene, 45 parts of linear low-density polyethylene 1.5 parts of PS-802 antioxidant, 2 parts of heat stabilizer, 3 parts of brominated epoxy resin, 2 parts of mixture of fluoropolymer processing aid and polyethylene, mixture of silica and polyethylene 2 parts, 3 parts of adipate, the melt flow rate of linear low density polyethylene is 0.7g / 10min, and the density is 0.875g / cm 3 .

[0037] A preparation method of PE heat shrinkable film, comprising the following steps:

[0038] (1) Take raw materials according to the above-mentioned parts by weight;

[0039] (2) Add ethylene-vinyl acetate copolymer, poly-3-hydroxybutyrate, high-density polyethylene, linear low-density polyethylene, antioxidant, heat stabilizer, flame retardant, lubricant to the reactor at 80°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The melt flow rateaaaaaaaaaa
The melt flow rateaaaaaaaaaa
The melt flow rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PE (Poly Ethylene) heat shrink film and a preparation method thereof, and relates to the field of packing materials. The PE heat shrink film is prepared from the following raw materials in parts by weight: 40-60 parts of ethylene-ethylene vinyl acetate copolymer, 50-60 parts of poly-3-hydroxybutyrate, 60-70 parts of high density polyethylene, 40-50 parts of linear low density polyethylene, 1-2 parts of antioxygen, 1-3 parts of heat stabilizer, 1-5 parts of fire retardant, 1-3 parts of lubricating agent, 1-3 parts of antiblocking agent and 2-4 parts of plasticizer. Since the raw materials mutually cooperate and act, the prepared PE heat shrink film has various excellent properties, high impact resistance and tear resistance and good transparency and surface glossiness, is easy to degrade and does not pollute environment. The preparation method is simple and easy in operation, and can realize large-scale production.

Description

technical field [0001] The invention relates to the field of packaging materials, in particular to a PE heat shrinkable film and a preparation method thereof. Background technique [0002] With the continuous development of my country's economy, the demand for heat-shrinkable films in the packaging industry is increasing, and the scope of application is also expanding. Because heat-shrinkable films not only have good comprehensive performance in terms of mechanical properties, packaging, storage, transportation, moisture-proof and appearance, etc. High performance, easy recycling and recycling of raw materials, meet the requirements of environmental protection, and improve the packaging efficiency on the automatic packaging line, reduce the overall packaging cost, and are gradually replacing traditional packaging as the first choice for bulk packaging. [0003] However, the heat-shrinkable film in the prior art has single performance, low strength, easy cracking, poor transpa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L67/04C08L23/08C08L63/00C08L27/12C08K3/36C08K5/11B29D7/01B29K23/00
CPCC08L23/06B29D7/01B29K2023/06C08J5/18C08J2323/06C08J2367/04C08J2423/06C08J2467/04C08L67/04C08L2201/06C08L2201/08C08L2201/10C08L2203/16C08L2205/025C08L2205/035C08L2207/062C08L23/0853C08L23/0815C08L63/00C08L27/12C08K3/36C08K5/11
Inventor 方小梅吴金明张启红
Owner 桐城市华猫软膜有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap