Resin material and preparation method thereof

A technology of resin material and matrix resin, applied in the field of resin material and its preparation, can solve the problems of complex production process, high comprehensive cost and high energy consumption, and achieve the effects of improving compatibility, improving production efficiency and improving impact resistance.

Active Publication Date: 2016-10-12
深圳市前海同益科技研发有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has defects such as complex production process, high ene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin material and preparation method thereof
  • Resin material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0063] The present invention also provides a method for preparing the aforementioned resin material, which includes the following steps:

[0064] The base resin, toughening agent, compatibilizer, and coloring masterbatch are placed at 80°C to 120°C and dried for 4 to 6 hours.

[0065] Each raw material is added to a high-speed mixer, and mixed for 1 min to 5 min to obtain a mixture.

[0066] The mixture is melted and pelletized by a twin-screw extrusion pelletizing unit; wherein the heating temperature is 180°C to 250°C, the die temperature is 195°C to 210°C, and the screw speed of the main engine is 400r / min to 550r / min, the feeding speed is 40r / min~60r / min.

[0067] The drying process of the matrix resin, toughening agent, compatibilizer, and coloring masterbatch can make the matrix resin, toughening agent, compatibilizing agent, and coloring masterbatch obtain excellent performance that is more suitable for mixing, and ensure the subsequent mixing process. The uniformity and qual...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a resin material and a preparation method thereof. The resin material is prepared from, by weight, 45-85 parts of matrix resin, 2-8 parts of color master-batches, 5-15 parts of flexibilizer, 1-5 parts of compatilizer and 0.05-0.4 part of antioxidant. The color master-batches comprise imitation metal master batches or imitation pearl master batches. According to the technical scheme, the situation that a product with a metal or pearl quality appearance effect can be obtained through direct injection moulding by means of the resin material can be achieved, the production efficiency of imitation metal plastic products and imitation pearl plastic products is improved, energy consumption and the comprehensive cost are reduced, and the resin material is environmentally friendly.

Description

Technical field [0001] The invention relates to a resin material and a preparation method thereof. Background technique [0002] In recent years, with the continuous development of product production technology and the gradual improvement of design requirements, products such as consumer electronics, household appliances, cosmetics, and automobile-related appliances have begun to be personalized, experiential, and customized. Transformation, the application of imitation metal effect or imitation pearl effect began to appear in these products. Initially, technicians in the industry generally used ordinary materials after injection molding to achieve the imitation metal effect or imitation pearlescent effect of the product. However, this method has disadvantages such as complex production processes, high energy consumption, high overall cost, and easy environmental pollution. Nowadays, with the rapid development of material technology, product structure designers have higher and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L51/04C08L25/12C08L25/10C08L33/20C08L33/12C08L69/00B29C47/92B29C48/92
Inventor 谢文涛姜旭潘丽梅
Owner 深圳市前海同益科技研发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap