A colored glass and melting technology, applied in glass manufacturing equipment, manufacturing tools, glass furnace equipment, etc., can solve the problems of difficult to meet market requirements, products have no golden yellow feeling, low color purity, etc., and achieve melting process parameters. Easy to control, reduces UV radiation, overcomes discoloration and darkening effects

Pending Publication Date: 2016-11-02
西安亚岱新能源科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In terms of glass melting process, the energy consumption of the traditional glass melting process realized by fuel accounts for the total energy consumption of the entire industry. The method of using industrial microwave energy for thermal energy conversion, through the design of raw materials and auxiliary heat materials, can realize overall heating, separation Stage melting, clarification, stirring, removing bubbles and other functions, the use of base-colored golden yellow glass plated mirror, not only bright color, elegant, luxurious, strong mirror effect, the whole glass is golden yellow, but they can only be produced on a small scale, and Its products have no golden yellow feeling, its color is only general yellow, and the color purity is also low, so it is difficult to meet market requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The glass in this embodiment consists of the following raw material components: SiO 2 50%, B 2 o 3 35%, BaO10%, MgO8%, Na 2 O5%, Al 2 o 3 3% and containing Fe 2 o 3 0.5%, Cr 2 o 3 1.0%, Nd 2 o 3 1.5%, Eu1% and Mn1% colorant 5%.

[0016] The melting steps of above-mentioned glass are as follows:

[0017] 1), select raw materials, carry out raw material mixing according to weight percentage;

[0018] 2) The mixed raw materials are melted in a high-temperature industrial microwave oven with a frequency of 2.45 Hz, and the glass melt melted by microwaves at high temperature is poured into a preheated mold for molding, and then placed in a heating furnace for annealing to obtain luminescence Glass.

Embodiment 2

[0020] The glass in this embodiment consists of the following raw material components: SiO 2 40%, B 2 o 3 30%, BaO5%, MgO7%, Na 2 O3%, Al 2 o 3 1% and containing Fe 2 o 3 0.1%, Cr 2 o 3 0.5%, Nd 2 o 3 0.8%, Eu0.1% and Mn0.3% colorant 2%.

[0021] The melting steps of above-mentioned glass are as follows:

[0022] 1), select raw materials, carry out raw material mixing according to weight percentage;

[0023] 2) Melting the mixed raw materials in a high-temperature industrial microwave oven with a frequency of 5.25 Hz, pouring the microwave-melted glass melt at high temperature into a preheated mold for molding, and annealing in a heating furnace to obtain luminescence Glass.

[0024] It can be seen from the above examples that the product produced by the present invention not only has all the advantages and characteristics of glass, but also has a golden color, elegant and luxurious, and also overcomes the disadvantages of ordinary glass discoloration and darkenin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses lead-free colored glass and its melting process. The glass is composed of the following raw material components: SiO2, B2O3, BaO, MgO, Na2O, Al2O3 and colorant; the melting steps of the glass are as follows: 1), select raw materials, mix raw materials according to the weight percentage, 2), microwave the mixed raw materials, and after heat treatment, obtain luminous glass; Disadvantages of discoloration and darkening under high-energy radiation, reducing ultraviolet radiation, no crystallization during glass production, stable luminous performance, energy saving in microwave melting process, and easy control of melting process parameters.

Description

technical field [0001] The invention relates to glass, in particular to lead-free colored glass and its melting process. Background technique [0002] With the continuous improvement of people's living standards, people's pursuit of various decorative effects is getting higher and higher and more abundant. Glass has been widely used because of its high visible light transmittance. In terms of glass melting process, the energy consumption of the traditional glass melting process realized by fuel accounts for the total energy consumption of the entire industry. The method of using industrial microwave energy for thermal energy conversion, through the design of raw materials and auxiliary heat materials, can realize overall heating, separation Stage melting, clarification, stirring, removing bubbles and other functions, the use of base-colored golden yellow glass plated mirror, not only bright color, elegant, luxurious, strong mirror effect, the whole glass is golden yellow, bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/091C03C4/12C03B5/16
Inventor 杨留胜
Owner 西安亚岱新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap