High-refractive-index watch glass for watch outer cover and production process of high-refractive-index watch glass

A technology with high refractive index and production technology, which is applied in the field of high refractive index watch glass for watch covers and its production technology, which can solve the problem of reducing the refractive index and dispersion of watch glass, glass cannot absorb short-wavelength rays, and reduce the stability of watch glass and other problems, to achieve the effect of being beneficial to processing and production, improving the refractive index and dispersion, and facilitating processing

Inactive Publication Date: 2021-01-22
DONGGUAN JINGSHI OPTICAL CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Watch glass is the transparent lens on the surface of the watch, which is used to protect the dial of the watch surface; the watch mirror can be divided into three types according to the material: plastic mirror, quartz glass mirror, and synthetic sapphire glass mirror; plastic mirror is relatively not afraid of falling; traditional watch glass uses long Stone is used as a raw material, which is melted and processed into shape. The glass crystallization phenomenon is serious during processing, which reduces the stability of watch glass, resulting in a decrease in strength, and the processed glass cannot absorb short-wavelength rays, which reduces the refractive index and dispersion of watch glass. At the same time, traditional watch glass The cost of raw materials is expensive, the processing is troublesome, and the production cost is increased, which is not conducive to processing and production; in view of these defects, it is necessary to design a watch glass with high refractive index for watch cover and its production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-refractive-index watch glass for watch outer cover and production process of high-refractive-index watch glass
  • High-refractive-index watch glass for watch outer cover and production process of high-refractive-index watch glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A high-refractive-index watch glass for a watch cover. The formula includes: silicon dioxide, aluminum oxide, borax, calcium carbonate, zinc oxide, dolomite, soda ash, clarifying agent and initiator, and the mass percentage of each component The contents are: 30% silicon dioxide, 16% aluminum oxide, 15% borax, 10% calcium carbonate, 4% zinc oxide, 10% dolomite, 2% soda ash, 8% Clarifying agent, 5% initiator.

[0033] A production process of high-refractive-index watch glass for a watch cover, comprising the following steps: Step 1, raw material selection; Step 2, melting and processing; Step 3, pressing and forming; Step 4, annealing treatment; Step 5, packaging and storage;

[0034] Wherein in above-mentioned step 1, according to the mass percentage content of each component is respectively: 30% silicon dioxide, 16% aluminum oxide, 15% borax, 10% calcium carbonate, 4% zinc oxide, 10% of dolomite, 2% of soda ash, 8% of clarifying agent, and 5% of initiator are selected...

Embodiment 2

[0049]A high-refractive-index watch glass for a watch cover. The formula includes: silicon dioxide, aluminum oxide, borax, calcium carbonate, zinc oxide, dolomite, soda ash, clarifying agent and initiator, and the mass percentage of each component The contents are: 25% silicon dioxide, 16% aluminum oxide, 20% borax, 10% calcium carbonate, 4% zinc oxide, 10% dolomite, 2% soda ash, 8% Clarifying agent, 5% initiator.

[0050] A production process of high-refractive-index watch glass for a watch cover, comprising the following steps: Step 1, raw material selection; Step 2, melting and processing; Step 3, pressing and forming; Step 4, annealing treatment; Step 5, packaging and storage;

[0051] Wherein in above-mentioned step 1, according to the mass percentage content of each component is respectively: 25% silicon dioxide, 16% aluminum oxide, 20% borax, 10% calcium carbonate, 4% zinc oxide, 10% of dolomite, 2% of soda ash, 8% of clarifying agent, and 5% of initiator are selected ...

Embodiment 3

[0066] A high-refractive-index watch glass for a watch cover. The formula includes: silicon dioxide, aluminum oxide, borax, calcium carbonate, zinc oxide, dolomite, soda ash, clarifying agent and initiator, and the mass percentage of each component The contents are: 20% silicon dioxide, 16% aluminum oxide, 25% borax, 10% calcium carbonate, 4% zinc oxide, 10% dolomite, 2% soda ash, 8% Clarifying agent, 5% initiator.

[0067] A production process of high-refractive-index watch glass for a watch cover, comprising the following steps: Step 1, raw material selection; Step 2, melting and processing; Step 3, pressing and forming; Step 4, annealing treatment; Step 5, packaging and storage;

[0068] Wherein in the above-mentioned step 1, according to the mass percentage of each component, it is respectively: 20% silicon dioxide, 16% aluminum oxide, 25% borax, 10% calcium carbonate, 4% zinc oxide, 10% of dolomite, 2% of soda ash, 8% of clarifying agent, and 5% of initiator are selected...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-refractive-index watch glass for a watch outer cover and a production process of the high-refractive-index watch glass. The high-refractive-index watch glass is prepared from silicon dioxide, aluminum oxide, borax, calcium carbonate, zinc oxide, dolomite, sodium carbonate, a clarifying agent and an initiator. The mass percentage of each component is as follows: 20-30%of silicon dioxide, 15-25% of aluminum oxide, 15-25% of borax, 10-20% of calcium carbonate, 2-4% of zinc oxide, 10-20% of dolomite, 1-3% of sodium carbonate, 5-10% of a clarifying agent and 2-5% of aninitiator. The glass is safe and reliable, silicon dioxide, aluminum oxide, borax, calcium carbonate, zinc oxide and dolomite are adopted as raw materials and subjected to dissolving processing and then compression molding, the glass crystallization phenomenon is reduced, the stability and strength of the watch glass are improved, the glass absorbs short-wavelength rays, the refractive index anddispersion of the watch glass are improved, the process is simple and rigorous, the raw materials are cheap, and the cost is low; machining is convenient, the production cost is greatly saved, and machining and production are facilitated.

Description

technical field [0001] The invention relates to the technical field of watch glass, in particular to a high-refractive-index watch glass for a watch cover and a production process thereof. Background technique [0002] Watch glass is the transparent lens on the surface of the watch, which is used to protect the dial of the watch surface; the watch mirror can be divided into three types according to the material: plastic mirror, quartz glass mirror, and synthetic sapphire glass mirror; plastic mirror is relatively not afraid of falling; traditional watch glass uses long Stone is used as a raw material, which is melted and processed into shape. The glass crystallization phenomenon is serious during processing, which reduces the stability of watch glass, resulting in a decrease in strength, and the processed glass cannot absorb short-wavelength rays, which reduces the refractive index and dispersion of watch glass. At the same time, traditional watch glass The cost of raw mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/066C03C1/00C03B11/00C03B25/00
CPCC03C3/066C03C1/004C03B11/00C03B25/00
Inventor 艾春前
Owner DONGGUAN JINGSHI OPTICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products