Device and method for double-strand continuous casting clad metal sheet

A technology of sheet metal and metal raw materials, which is applied in the field of manufacturing clad sheet metal, can solve the problems of long production cycle and low material utilization rate, and achieve the effects of shortened production cycle, high material utilization rate, and reduced operating intensity

Active Publication Date: 2018-11-27
ZHEJIANG FUDA ALLOY MATERIALS TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a device and method for double-strand continuous casting of clad metal sheets in order to solve the shortcomings of low material utilization and long production cycle in the hot-rolled silver cladding process of internal oxidation sheet contact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Device and method for double-strand continuous casting clad metal sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] a) The first drainage rod 5 width * thickness = 40mm * 2mm, the first drainage rod 5 passes through the traction mechanism 7, the second crystallizer 4 and the first crystallizer 3, and pure silver is melted in the first smelting furnace 10, The melting temperature is 1400°C. After melting, it is poured from the first smelting furnace 10 into the first holding furnace 1, and flows into the heat preservation section of the first crystallizer 3. The heat preservation temperature of the first holding furnace 1 is 1150°C. Adjust the first water cooling jacket 801 The water flow rate is 0.5m 3 / second, water pressure 0.1MPa, adjust the temperature of the first crystallizer 3 to 800°C, set the pulling speed to 10mm / min, pull the pure silver plate out of the first crystallizer 3, enter the cooling section of the second crystallizer 4, and stop traction.

[0027] b) Melting silver and cadmium in the second smelting furnace 11 to form a homogenized alloy with a melting tempera...

Embodiment 2

[0030] a) first drainage rod 5 width×thickness=100mm×5mm, first drainage rod 5 passes through traction mechanism 7, second crystallizer 4 and first crystallizer 3, and pure silver is melted in first melting furnace 10, The melting temperature is 1300°C. After melting, it is poured from the first smelting furnace 10 into the first holding furnace 1, and flows into the heat preservation section of the first crystallizer 3. The heat preservation temperature of the first holding furnace 1 is 1100°C. Adjust the first water cooling jacket 801 The water flow is 1m 3 / second, water pressure 1MPa, adjust the temperature of the first crystallizer 3 to 500°C, set the traction speed to 100mm / min, pull the pure silver plate out of the first crystallizer 3, enter the cooling section of the second crystallizer 4, and stop the traction .

[0031]b) Melting silver, tin, and indium in the second smelting furnace 11 to form a homogenized alloy with a melting temperature of 1250° C.; adjusting ...

Embodiment 3

[0034] a) Width of the first drainage rod 5 × thickness = 60mm × 2.5mm, the first drainage rod 5 passes through the traction mechanism 7, the second crystallizer 4 and the first crystallizer 3, and the pure silver is melted in the first melting furnace 10 , the melting temperature is 1200°C. After melting, it is poured from the first melting furnace 10 into the first holding furnace 1, and flows into the holding section of the first crystallizer 3. The holding temperature of the first holding furnace 1 is 1050°C. In the first water cooling jacket 801 The water flow is 1.5m 3 / second, water pressure 5MPa, the temperature of the first crystallizer 3 is adjusted to 650°C, the pure silver plate is drawn out of the first crystallizer 3, enters the cooling section of the second crystallizer 4, and stops pulling.

[0035] b) Melting silver and copper in the second smelting furnace 11 to form a homogenized alloy with a melting temperature of 1400°C; adjusting the traction mechanism 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention specifically relates to a device and method for double-strand continuous casting of clad metal sheets. The device is equipped with a first holding furnace, a second holding furnace, a first crystallizer, a second crystallizer, a first drainage rod, and a second drainage rod , the bottom end of the first holding furnace is connected to the first crystallizer, the bottom end of the second holding furnace is connected to the second crystallizer, the first crystallizer is connected to the second crystallizer, and the width of the first draining rod and the second draining rod are equal , the first drainage rod is located below the second drainage rod and fits closely, the first drainage rod and the second drainage rod pass through the bottom end of the second crystallizer together, the first drainage rod penetrates into the bottom end of the first crystallizer, and the The first drainage rod and the second drainage rod are connected to the traction mechanism. The invention can significantly reduce the production process of the composite board, shorten the production cycle, improve the material utilization rate, produce the composite board with lower manufacturing cost, effectively improve the bonding strength of the composite surface and the like, and improve the reliability of the finished product.

Description

technical field [0001] The invention relates to a manufacturing technology of a clad metal sheet, in particular to a device and method for double-strand continuous casting of a clad metal sheet. Background technique [0002] In the field of electrical contacts, the internal oxidation process is a common process for manufacturing silver metal oxide contacts. Among them, the sheet contacts used in electrical appliances such as AC contactors need to be assembled with copper contact bridges after welding, while silver metal oxides The wettability between the material and the solder and the copper contact bridge is not good, and it is not easy to weld, so a pure silver layer should be added on the welding surface of the silver metal oxide sheet contact to facilitate welding, and the thickness distribution of the silver layer is required As uniform as possible, there is a relatively clear boundary between the silver metal oxide layer and the silver layer. Internal Oxidation Silve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/00B22D11/14
CPCB22D11/007B22D11/143
Inventor 万岱缪仁梁周克武姚培建张秀芳柏小平林万焕
Owner ZHEJIANG FUDA ALLOY MATERIALS TECH CO LTD