Novel cement foam material

A new type of cement foaming technology, used in applications, household appliances, ceramic products, etc., can solve the problems of poor impact resistance and poor durability, and achieve good wind pressure resistance, excellent thermal insulation, and high compressive strength. Effect

Inactive Publication Date: 2016-11-09
张莘蔓
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a new type of cement foam material to solve the problems of poor impact resistance and relatively poor durability in existing foam materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel cement foam material
  • Novel cement foam material
  • Novel cement foam material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of the novel concrete environmental protection brick includes the following steps:

[0031] S1: Preparation of hollow brick

[0032] Mix cement, shale ore, fly ash, tailings sand, and slag and mix them evenly at a speed of 200-400r / min to make hollow bricks;

[0033] S2: Preparation of cement foam material

[0034] S21: Stir the cement, glyoxal and water at a speed of 100-300r / min to make slurry;

[0035] S22: Combine calcium carbonate, calcium silicate, limestone, magnesium borate, wheat straw powder, AR glass fiber, carboxymethyl cellulose, water reducing agent, foaming agent, foaming regulator, catalyst, crosslinking agent and foam stabilizer The agent is stirred at a speed of 60-100r / min for 2-3h to obtain a foam liquid;

[0036] S23: adding the foam liquid prepared in step S22 to the slurry prepared in step S21, and stirring uniformly at a rotation speed of 150-200 r / min to prepare a new cement foam material;

[0037] S3: Preparation of insulation brick...

Embodiment 1

[0041] A new type of environmentally friendly concrete brick includes a hollow brick as the outer shell of the brick body and a cement foam material filled in the cavity of the brick body. The hollow brick is in parts by weight and includes the following raw materials: 52 parts of cement and 38 parts of shale ore , 27 parts of fly ash, 10 parts of tailing sand, 8 parts of slag; the cement foaming material is based on parts by weight, including the following raw materials: 32 parts of cement, 2 parts of calcium carbonate, 2 parts of calcium silicate, 2 parts of limestone , 2 parts of magnesium borate, 2 parts of wheat straw powder, 0.8 parts of AR glass fiber, 0.6 parts of carboxymethyl cellulose, 2 parts of water reducing agent, 0.6 parts of foaming agent, 0.4 parts of foaming regulator, 0.2 parts of catalyst, Coupling agent 0.5 parts, foam stabilizer 0.3 parts, glyoxal 25 parts, water 280 parts.

[0042] The grain size of the wheat straw powder is less than or equal to 300 μm, a...

Embodiment 2

[0061] A new type of environmentally friendly concrete brick includes a hollow brick as the outer shell of the brick body and a cement foam material filled in the cavity of the brick body. The hollow brick is in parts by weight and includes the following raw materials: 45 parts of cement and 35 parts of shale ore , 25 parts of fly ash, 8 parts of tailings sand, 6 parts of slag; the cement foaming material is in parts by weight, including the following raw materials: cement 23 parts, calcium carbonate 2 parts, calcium silicate 2 parts, limestone 2 parts , 1 part of magnesium borate, 1 part of wheat straw powder, 0.6 part of AR glass fiber, 0.4 part of carboxymethyl cellulose, 1.5 part of water reducing agent, 0.2 part of foaming agent, 0.2 part of foaming regulator, 0.1 part of catalyst, Coupling agent 0.3 parts, foam stabilizer 0.1 parts, glyoxal 20 parts, water 240 parts.

[0062] The grain size of the wheat straw powder is less than or equal to 300 μm, and the moisture content ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel cement foam material. The novel cement foam material is prepared from, by weight, 23-42 parts of cement, 2-3 parts of calcium carbonate, 2-3 parts of calcium silicate, 2-3 parts of limestone, 1-2 parts of magnesium borate, 1-2 parts of wheat straw powder, 0.6-1 part of AR glass fibers, 0.4-0.8 part of carboxymethylcellulose, 1.5-2.5 parts of a water reducing agent, 0.2-0.8 part of a foaming agent, 0.2-0.6 part of a foaming regulator, 0.1-0.3 part of a catalyst, 0.3-0.6 part of a crosslinking agent, 0.1-0.5 part of a foam stabilizer, 20-30 parts of glyoxal and 240-300 parts of water. An environment-friendly concrete brick made of the novel cement foam material has the advantages of being good in heat preservation and heat insulation performance and sound insulation effect, light, resistant to pressure and the like.

Description

Technical field [0001] The invention belongs to the technical field of building material preparation, and specifically relates to a new type of cement foam material. Background technique [0002] With the promotion of building energy saving and people's increasing demand for the comfort of living environment, thermal insulation materials have received more and more attention from people. The existing thermal insulation composite bricks or blocks mainly have various forms such as inlaid thermal insulation materials, thermal insulation interlayers or thermal insulation holes and trenches. As one of the house thermal insulation materials, the room temperature non-fired foam bricks are more and more popular because of their thermal insulation, sound insulation, fire resistance, and strength superior to traditional thermal insulation materials. However, the existing foam materials on the market have disadvantages such as poor impact resistance and relatively poor durability. Summary...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/02
CPCC04B28/00C04B2201/20C04B2201/32C04B2201/50C04B14/108C04B18/08C04B18/12C04B18/06C04B14/28C04B22/08C04B22/0013C04B18/24C04B14/42C04B24/383C04B2103/302C04B24/045C04B24/40C04B24/00C04B24/42C04B24/008C04B24/129C04B38/02C04B24/128
Inventor 张莘蔓
Owner 张莘蔓
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap