A waterproof coating and two-component technology, applied in the field of waterproof coatings, can solve the problems of high water absorption rate and poor water resistance, and achieve the effects of low water absorption rate, lower water absorption rate, and improved bonding performance.
Inactive Publication Date: 2016-11-09
ANHUI KUAILAI WATERPROOFING & ANTI CORROSION
View PDF2 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, at present, this kind of products still has the disadvantages of high water absorption and poor water resistance.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0021] A high water-resistant two-component silicone-acrylic polymer cement-based waterproof coating, which is composed of liquid material A and powder material B in a mass ratio of 1:1.8,
[0022] Described liquid material A is made up of the raw material of following weight (kg): solid content is 45% silicon acrylic emulsion 70, polyethylene glycol 5, trifluoroethyl methacrylate 4, octyldodecyl beescemic acid Ester 1.5, acrylic ribose polysaccharide 4, sodium methylene dinaphthalene sulfonate 2.5, liquid paraffin 5, white petrolatum 3, hydroxyethyl cellulose 3, Span-20 1.5, water 60;
[0023] The powder B is made of the following raw materials by weight (kg): 38 magnesia slag Portland cement, 25 river sand, 14 silicon phosphate, 26 dickite, 7 hexahydrate magnesium hexafluorosilicate, 7 vanadium extraction tails Slag 16, halloysite slag 15, hydrophobic fumed silica 8, dolomite 17, converter steel slag 19, clastic rock 18, calcium rosinate 6.
[0024] A preparation method of ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-water-resistance two-component siloxane-acrylate copolymer cement-based waterproof coating and a preparation method thereof. The coating is prepared from a liquid material A and a powdery material B in a mass ratio of 1: (1.5-2). The liquid material A is prepared from raw materials consisting of silicone acrylic emulsion, polyethylene glycol, trifluoroethyl methacrylate, octyldodecyl beeswax, polyribosome acrylate, disodium methylene dinaphthalene sulfonate, liquid paraffin, albolene, hydroxyethyl cellulose, Span-20, water and the like. The powdery material B is prepared from raw materials consisting of magnesium-slag Portland cement, river sand, silicon phosphorate, dickite, magnesium hexafluorosilicate hexahydrate, vanadium extraction tailings, halloysite slag, hydrophobic fumed silica, dolomite, converter slag, clastic rock, calcium rosinate, etc. The two-component siloxane-acrylate copolymer cement-based waterproof coating prepared in the invention is low in water absorption capacity and good in water resistance, does not swell in case of soaking in water and has excellent caking properties, corrosion resistance, temperature tolerance and ageing resistance.
Description
technical field [0001] The invention relates to a high water resistance two-component silicone-acrylic polymer cement-based waterproof coating and a preparation method thereof, belonging to the field of waterproof coatings. Background technique [0002] Two-component polymer cement-based waterproof coating is a two-component waterproof coating based on water-based polymer dispersion and cement. The two components are stirred on site to form a uniform and fine slurry, which is brushed or sprayed on the surface of the substrate. After curing Form a flexible, high-strength waterproof coating film. This kind of coating not only has the advantages of high strength of cement-based cementitious materials, is easy to bond with wet substrates, but also has the advantages of high elasticity and good water resistance of the polymer coating film. The disadvantage of waterproof coatings polluting the environment is a new type of green and environmentally friendly waterproof coating that...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.