Mobile phone faceplate multi-layer coating film layer and preparation method thereof

A coating layer and panel technology, which is applied in the field of multilayer coating layer and its preparation of mobile phone panels, can solve the problems of lack of crystalline alumina and high film forming temperature, so as to improve wear resistance, reduce film forming temperature, and increase transmittance rate effect

Active Publication Date: 2016-11-09
SUN YAT SEN UNIV +1
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since glass is an amorphous substrate, the lack of nucleation cores of crystalline alumina leads to high film formation temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mobile phone faceplate multi-layer coating film layer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The accompanying drawings are for illustrative purposes only, and should not be construed as limitations on this patent; in order to better illustrate this embodiment, certain components in the accompanying drawings will be omitted, enlarged or reduced, and do not represent the size of the actual product; for those skilled in the art It is understandable that some well-known structures and descriptions thereof may be omitted in the drawings. The positional relationship described in the drawings is for illustrative purposes only, and should not be construed as a limitation on this patent.

[0023] Such as figure 1 as shown,

[0024] The purpose of this specific embodiment is to provide a low-temperature, low-cost anti-scratch, wear-resistant and high-transparency coating technology on glass surfaces.

[0025] The preliminary thinking of the present invention is: Utilize the existing industrial mass-production type MOCVD (Metal-organic Chemical Vapor Deposition, metal-o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of multi-layer coating films of glass substrates, in particular to a mobile phone faceplate multi-layer coating film layer and a preparation method thereof. According to the technology for preparing the high-transmittance and abrasion-resistant multi-layer film on a glass substrate, the glass substrate, a magnesium oxide polycrystal seed layer, a high-hardness abrasion-resistant aluminum oxide coating film layer and a titanium oxide / aluminum oxide laminated transmittance enhanced layer are specifically included. According to the mobile phone faceplate multi-layer coating film layer and the preparation method thereof, (1) the metal organic chemical vapor deposition (MOCVD) technology is adopted so that large-area uniform film forming can be achieved; (2) through the design of a polycrystal buffer layer, the high-hardness aluminum oxide coating film of a microcrystal-amorphous mixed structure is grown in an extending mode at a low film forming temperature; and (3) the transmittance is improved through the aluminum oxide / titanium oxide / aluminum oxide laminated layer.

Description

technical field [0001] The invention relates to the technical field of multilayer coating of glass substrates, and more specifically, relates to a multilayer coating layer of a mobile phone panel and a preparation method thereof. Background technique [0002] With the development of display and mobile terminals, it is urgent to seek glass coating technology with low cost, high wear resistance and scratch resistance, and high transmission characteristics to meet the needs of mobile terminal products such as smart phone panels. Under the above background, coating glass panels with high hardness and high transmittance will be an effective way to realize high scratch resistance, high transmittance, and low-cost smartphone panels. At present, the diamond-like carbon film (DLC: Diamond Like Carbon) is widely researched and applied as a high-hardness coating technology, which has the advantages of diamond carbon sp3 hybrid orbital, high hardness, chemical inertness, and low frictio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C16/40C23C14/30C23C14/08C23C28/04
CPCC23C14/083C23C14/30C23C16/403C23C28/042
Inventor 裴艳丽林家勇刘佳慧吴土祥
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com